论文信息 - Preparation of anatase powders from fluorine-complexed titanium(iv) aqueous solution using microwave irradiation

Preparation of anatase powders from fluorine-complexed titanium(iv) aqueous solution using microwave irradiation

The microwave radiation activated precipitation of titanium dioxide from homogeneous aqueous solutions of titanium–fluoro complexes and boric acid has been carried out in batch reactors. Crystalline anatase powders with narrow monodisperse size distribution have been obtained in a short time, at low temperature and atmospheric pressure. Microwave power, irradiation time and precursor concentration determine the properties of the obtained materials, i.e. crystal size, powder aggregate morphology and BET surface area. The obtained materials do not show photocatalytic activity, probably due to a considerable fluoride content that is in the range of 2–5%.

[1] B. Vaidhyanathan,et al. Synthesis of inorganic solids using microwaves , 1999 .

[2] Xavier Domènech,et al. TiO2 thin film deposition from solution using microwave heating , 2000 .

[3] N. Serpone,et al. Application of concept of relative photonic efficiencies and surface characterization of a new titania photocatalyst designed for environmental remediation , 1996 .

[4] IzumiFujio. The Polymorphic Crystallization of Titanium(IV) Oxide under Hydro-thermal Conditions. II. The Roles of Inorganic Anions in the Nucleation of Rutile and Anatase from Acid Solutions , 1978 .

[5] C. Wamser. Equilibria in the System Boron Trifluoride—Water at 25° , 1951 .

[6] A. Liberti,et al. Complexity of titanium(IV) fluoride solutions , 1960 .

[7] A. Cassano,et al. ABSORPTION AND SCATTERING COEFFICIENTS OF TITANIUM DIOXIDE PARTICULATE SUSPENSIONS IN WATER , 1996 .

[8] Q. H. Li,et al. Microwave-hydrothermal synthesis of ceramic powders , 1992 .

[9] S. N. Subbarao,et al. Electrical and optical properties of the system TiO2-xFx , 1979 .

[10] J. Caro,et al. Large AlPO4-5 crystals by microwave heating , 1995 .

[11] E. L. Grove,et al. The Equivalent Conductance of the Hexafluorocomplexes of Group IV (Si, Ge, Sn, Ti, Zr, Hf)1 , 1960 .

[12] X. Doménech,et al. TiO2 thin films grown using microwave-activated solutions , 1999 .

[13] S. Deki,et al. Synthesis of metal oxide thin films by liquid-phase deposition method , 1998 .