Effect of Ni-P Plating Temperature on Growth of Interfacial Intermetallic Compound in Electroless Nickel Immersion Gold/Sn-Ag-Cu Solder Joints

The growth of interfacial intermetallic compound and the brittle fracture behavior of Sn-3.0Ag-0.5-Cu solder (SAC305) joints on electroless nickel immersion gold (ENIG) surface finish have been investigated using Ni-P plating solution at temperatures from 75°C to 85°C and fixed pH of 4.5. SAC305 solder balls with diameter of 450 μm were mounted on the prepared ENIG-finished Cu pads and reflowed with peak temperature of 250°C. The interfacial intermetallic compound (IMC) thickness after reflow decreased with increasing Ni-P plating temperature. After 800 h of thermal aging, the IMC thickness of the sample prepared at 85°C was higher than for that prepared at 75°C. Scanning electron microscopy of the Ni-P surface after removal of the Au layer revealed a nodular structure on the Ni-P surface. The nodule size of the Ni-P decreased with increasing Ni-P plating temperature. The Cu content near the IMC layer increased to 0.6 wt.%, higher than the original Cu content of 0.5 wt.%, indicating that Cu diffused from the Cu pad to the solder ball through the Ni-P layer at a rate depending on the nodule size. The sample prepared at 75°C with thicker interfacial IMC showed greater high-speed shear strength than the sample prepared at 85°C. Brittle fracture increased with decreasing Ni-P plating temperature.

[1]  W. Cai,et al.  Effects of ligands on electroless Ni–P alloy plating from alkaline citrate–ammonia solution , 2003 .

[2]  S. Jung,et al.  MORPHOLOGY, THERMAL STABILITY, AND SOLDERABILITY OF ELECTROLESS NICKEL–PHOSPHORUS PLATING LAYER , 2007 .

[3]  Glenn O. Mallory,et al.  Electroless plating : fundamentals and applications , 1990 .

[4]  W. M. Lau,et al.  Surface properties and solderability behaviour of nickel–phosphorus and nickel–boron deposited by electroless plating , 2001 .

[5]  Chuang‐Chuang Tsai,et al.  Dependence of hydrogen diffusion on growth conditions in hydrogenated amorphous silicon , 1988 .

[6]  C. Chao,et al.  The growth morphology and crystallinity of electroless NiP deposition on silicon , 2004 .

[7]  N. Dimitrov,et al.  Toward a Better Understanding of the Effect of Cu Electroplating Process Parameters on Cu3Sn Voiding , 2012, Journal of Electronic Materials.

[8]  T.S.N. Sankara Narayanan,et al.  Effect of accelerators and stabilizers on the formation and characteristics of electroless Ni–P deposits , 2006 .

[9]  D. A. Smith,et al.  Study of grain growth in electrodeposited nanocrystalline nickel-1.2 wt.% phosphorus alloy , 1995 .

[10]  Y. Chan,et al.  Effect of reaction time and P content on mechanical strength of the interface formed between eutectic Sn–Ag solder and Au/electroless Ni(P)/Cu bond pad , 2003 .

[11]  Andreas Ostmann,et al.  Electroless nickel/copper plating as a new bump metallization , 1995 .

[12]  S. Jung,et al.  Characteristic evaluation of electroless nickel-phosphorus deposits with different phosphorus contents , 2007 .

[13]  Vesa Vuorinen,et al.  Interfacial reactions between lead-free SnAgCu solder and Ni(P) surface finish on printed circuit boards , 2002 .

[14]  Jin Yu,et al.  Correlation between chemical reaction and brittle fracture found in electroless Ni(P)/immersion gold–solder interconnection , 2005 .

[15]  Y. L. Lin,et al.  Effect of Cu concentration on the reactions between Sn-Ag-Cu solders and Ni , 2002 .

[16]  Jin Yu,et al.  Effects of residual S on Kirkendall void formation at Cu/Sn–3.5Ag solder joints , 2008 .

[17]  Yi Ping Wu,et al.  Study of Intermetallic Growth and Kinetics in Fine-Pitch Lead-Free Solder Bumps for Next-Generation Flip-Chip Assemblies , 2013, Journal of Electronic Materials.

[18]  Jin Yu,et al.  Heat-treatment to suppress the formation of Kirkendall voids in Sn-3.5Ag/Cu solder joints , 2013 .

[19]  K. Tu,et al.  Six cases of reliability study of Pb-free solder joints in electronic packaging technology , 2002 .

[20]  Y. C. Chan,et al.  Effect of 0.5 wt % Cu in Sn-3.5%ag solder on the interfacial reaction with Au/Ni metallization , 2003 .

[21]  Jin Yu,et al.  Secondary IMC formation induced by Kirkendall voiding in Cu/Sn-3.5Ag solder joints , 2010 .

[22]  Y. L. Lin,et al.  Strong effect of Cu concentration on the reaction between lead-free microelectronic solders and Ni , 2002 .

[23]  D. Isheim,et al.  Nanocrystalline Ni-3.6 at.% P and its transformation sequence studied by atom-probe field-ion microscopy , 2000 .

[24]  Tomi Laurila,et al.  Interfacial reactions between lead-free solders and common base materials , 2005 .

[25]  J. Duh,et al.  Detailed Phase Evolution of a Phosphorous-Rich Layer and Formation of the Ni-Sn-P Compound in Sn-Ag-Cu/Electroplated Ni-P Solder Joints , 2010 .

[26]  Peter Borgesen,et al.  Influence of plating parameters and solution chemistry on the voiding propensity at electroplated copper–solder interface , 2008 .