Lanthanum telluride (La3−xTe4) has been synthesized via mechanical alloying and characterized for thermoelectric performance. This work confirms prior reports of lanthanum telluride as a good high-temperature thermoelectric material, with zT~1.1 obtained at 1275 K. The thermoelectric performance is found to be better than that of SiGe, the current state-of-the-art high-temperature n-type thermoelectric material. Inherent self-doping of the system allows control over carrier concentration via sample stoichiometry. Prior high-temperature syntheses were prone to solute rejection in liquid and vapor phases, which resulted in inhomogeneous chemical composition and carrier concentration. The low-temperature synthesis provides homogeneous samples with acceptable control of the stoichiometry, and thus allows a thorough examination of the transition from a heavily doped degenerate semiconductor to a nondegenerate semiconductor. The effect of carrier concentration on the Hall mobility, Seebeck coefficient, thermal and electrical conductivity, lattice thermal conductivity, and thermoelectric compatibility are examined for 0.03<=x<=0.33.
[1]
D. Rowe.
Thermoelectrics Handbook
,
2005
.
[2]
Mohamed S. El-Genk,et al.
Space Technology and Applications International Forum
,
1996
.
[3]
C. B. Vining,et al.
Modern perspectives on thermoelectrics and related materials
,
1991
.
[4]
R. Pierret,et al.
Advanced semiconductor fundamentals
,
1987
.
[5]
L. Alexander,et al.
X-Ray diffraction procedures for polycrystalline and amorphous materials
,
1974
.
[6]
V. Fistul.
Statistical Physics of Carriers in Heavily Doped Semiconductors
,
1969
.
[7]
I. B. Cadoff,et al.
Thermoelectric materials and devices
,
1960
.