Transition from Self-Organized Criticality into Self-Organization during Sliding Si3N4 Balls against Nanocrystalline Diamond Films

The paper investigates the variation of friction force (Fx) during reciprocating sliding tests on nanocrystalline diamond (NCD) films. The analysis of the friction behavior during the run-in period is the focus of the study. The NCD films were grown using microwave plasma-enhanced chemical vapor deposition (MW-PECVD) on single-crystalline diamond SCD(110) substrates. Reciprocating sliding tests were conducted under 500 and 2000 g of normal load using Si3N4 balls as a counter body. The friction force permanently varies during the test, namely Fx value can locally increase or decrease in each cycle of sliding. The distribution of friction force drops (dFx) was extracted from the experimental data using a specially developed program. The analysis revealed a power-law distribution f−µ of dFx for the early stage of the run-in with the exponent value (µ) in the range from 0.6 to 2.9. In addition, the frequency power spectrum of Fx time series follows power-law distribution f−α with α value in the range of 1.0–2.0, with the highest values (1.6–2.0) for the initial stage of the run-in. No power-law distribution of dFx was found for the later stage of the run-in and the steady-state periods of sliding with the exception for periods where a relatively extended decrease of coefficient of friction (COF) was observed. The asperity interlocking leads to the stick-slip like sliding at the early stage of the run-in. This tribological behavior can be related to the self-organized criticality (SOC). The emergence of dissipative structures at the later stages of the run-in, namely the formation of ripples, carbonaceous tribolayer, etc., can be associated with the self-organization (SO).

[1]  Iosif S. Gershman,et al.  Relation between Self-Organization and Wear Mechanisms of Diamond Films , 2018, Entropy.

[2]  George R. Fenske,et al.  Friction and Wear Mechanisms of Smooth Diamond Films During Sliding in Air and Dry Nitrogen , 1997 .

[3]  Ajay P. Malshe,et al.  Tribological properties of polished diamond films , 1993 .

[4]  Sergey V Buldyrev,et al.  Dry friction avalanches: experiment and theory. , 2006, Physical review. E, Statistical, nonlinear, and soft matter physics.

[5]  J. Field,et al.  Diamond polishing , 2004, Proceedings of the Royal Society of London. Series A: Mathematical, Physical and Engineering Sciences.

[6]  R. Traksmaa,et al.  Changes in Surface Morphology, Deflection and Wear of Microcrystalline Diamond Film Observed during Sliding Tests against Si3N4 Balls , 2016 .

[7]  Bharat Bhushan,et al.  Thermodynamics of surface degradation, self-organization and self-healing for biomimetic surfaces , 2009, Philosophical Transactions of the Royal Society A: Mathematical, Physical and Engineering Sciences.

[8]  Shu-Kun Lin,et al.  Modern Thermodynamics: From Heat Engines to Dissipative Structures , 1999, Entropy.

[9]  Tang,et al.  Self-Organized Criticality: An Explanation of 1/f Noise , 2011 .

[10]  Anssi Laukkanen,et al.  Friction and wear of coated surfaces — scales, modelling and simulation of tribomechanisms , 2007 .

[11]  Robert W. Carpick,et al.  Influence of surface passivation on the friction and wear behavior of ultrananocrystalline diamond and tetrahedral amorphous carbon thin films , 2012 .

[12]  K. Holmberg,et al.  Load-carrying capacity evaluation of coating/substrate systems for hydrogen-free and hydrogenated diamond-like carbon films , 1999 .

[13]  J. Lüning,et al.  Run-In Behavior of Nanocrystalline Diamond Coatings Studied By in Situ Tribometry , 2008 .

[14]  George E. Totten,et al.  Self-Organization During Friction : Advanced Surface-Engineered Materials and Systems Design , 2006 .

[15]  Maksim Antonov,et al.  Rippling on Wear Scar Surfaces of Nanocrystalline Diamond Films After Reciprocating Sliding Against Ceramic Balls , 2014, Tribology Letters.

[16]  W. V. Enckevort,et al.  A simple model to describe the anisotropy of diamond polishing , 1999 .

[17]  P. Koidl,et al.  Crystallographic anisotropy of wear on a polycrystalline diamond surface , 2005 .

[18]  Rui F. Silva,et al.  Friction and wear performance of HFCVD nanocrystalline diamond coated silicon nitride ceramics , 2006 .

[19]  J. E. Field,et al.  Electron microscopy analysis of debris produced during diamond polishing , 2003 .

[20]  Bharat Bhushan,et al.  Multiscale friction mechanisms and hierarchical surfaces in nano- and bio-tribology , 2007 .

[21]  Peter Gumbsch,et al.  Anisotropic mechanical amorphization drives wear in diamond. , 2011, Nature materials.

[22]  M. Gardos,et al.  The effect of environment on the tribological properties of polycrystalline diamond films , 1990 .

[23]  T. Raadik,et al.  Investigation of Morphology Changes on Nanocrystalline Diamond Film Surfaces during Reciprocating Sliding against Si3N4 Balls , 2014 .

[24]  J. Gershman,et al.  Thin films and self-organization during friction under the current collection conditions , 2004 .

[25]  Phillip B. Abel,et al.  LETTER TO THE EDITOR: Evidence of self-organized criticality in dry sliding friction , 2003 .

[26]  V. Podgursky,et al.  Effect of Nanocrystalline Diamond Films Deflection on Wear Observed in Reciprocating Sliding Tests , 2016 .

[27]  T. Raadik,et al.  A comparative study of the growth dynamics and tribological properties of nanocrystalline diamond films deposited on the (110) single crystal diamond and Si(100) substrates , 2019, Diamond and Related Materials.