论文信息 - Spectral Property and Stability of Color Centers in Alkali Halide Crystals Induced by He+ Ion Implantation at Room Temperature

Spectral Property and Stability of Color Centers in Alkali Halide Crystals Induced by He+ Ion Implantation at Room Temperature

Thin colored layers with high density defect centers could be produced on alkali halide crystals implanted by 300-400 keV He+ ions at room temperature. Besides well known absorption bands, several new absorption bands and colloid absorption band are observed in the crystals, such as 520 and 842 nm absorption bands in the implanted LiF crystals, 840 nm absorption band in the implanted NaF:OH- crystals, and 875 nm absorption band in the implanted NaCl:OH- crystals.

Zhifang Chen | Zhifan Chen | Zhijuan Li | H. Gu

[1] Q. Lan,et al. Reproduction of high density F2+ centers in undoped and doped sodium fluoride crystals , 1990 .

[2] L. Qi,et al. Nonlinear optical phase conjugation using F+3 centers in LiF crystals , 1989 .

[3] Lan Qi,et al. The two-step creation and tunable laser operation of F+3 centers in LiF crystals , 1989 .

[4] L. Qi,et al. Broadly tunable yellow‐green laser using color centers in a LiF crystal at room temperature , 1988 .

[5] P. Townsend,et al. F and F2 centres in LiF induced by ion implantation , 1986 .

[6] R. Shelby,et al. Thin-film aggregate color centers as media for frequency domain optical storage , 1981 .

[7] W. Gellermann,et al. F2+ center stabilization and tuneable laser operation in OH− doped alkali halides , 1980 .

[8] S. Jain,et al. Metal colloids in ionic crystals , 1979 .

[9] K. Ozawa,et al. Induced F aggregate centres in NaF crystals irradiated with charged particles at low temperature , 1973 .

[10] D. Pooley. The saturation of F-centre production in alkali halides under proton irradiation , 1966 .

[11] W. D. Compton,et al. Luminescence and Symmetry Properties of Color Centers , 1957 .