Thickness dependent fatigue life at microcrack nucleation for metal thin films on flexible substrates

For polymer-supported metal thin films used in flexible electronics, the definition of the fatigue lifetime at microcrack nucleation (FLMN) should be more physically meaningful than all the previous definitions at structural instability. In this paper, the FLMN of Cu films (with thickness from 100 nm to 3.75 µm) as well as Al thin films (from 80 to 800 nm) was experimentally characterized at different strain ranges and different thicknesses by using a simple electrical resistance measurement (ERM). A significant thickness dependence was revealed for the FLMN and a similar Coffin–Manson fatigue relationship observed commonly in bulk materials was found to be still operative in both the films. Microstructural analyses were carried out to verify the feasibility of ERM correspondingly.

[1]  G. Crawford,et al.  Strain-dependent electrical resistance of tin-doped indium oxide on polymer substrates , 2000 .

[2]  O. Kraft,et al.  Fatigue in thin films: lifetime and damage formation , 2001 .

[3]  Z. Suo,et al.  Metal films on polymer substrates stretched beyond 50 , 2007 .

[4]  Oliver Kraft,et al.  Cyclic deformation of polycrystalline Cu films , 2003 .

[5]  Stephen R. Forrest,et al.  The path to ubiquitous and low-cost organic electronic appliances on plastic , 2004, Nature.

[6]  E. Arzt,et al.  Damage behavior of 200-nm thin copper films under cyclic loading , 2005 .

[7]  W. Brückner,et al.  Tensile testing of AlCu thin films on polyimide foils , 1999 .

[8]  Z. Suo,et al.  Stretchability of thin metal films on elastomer substrates , 2004 .

[9]  Zhigang Suo,et al.  High ductility of a metal film adherent on a polymer substrate , 2005 .

[10]  Z. Suo,et al.  Stretchable gold conductors on elastomeric substrates , 2003 .

[11]  E. Arzt,et al.  Length-scale-controlled fatigue mechanisms in thin copper films , 2006 .

[12]  Z. Suo,et al.  Mechanics of thin-film transistors and solar cells on flexible substrates , 2006 .

[13]  A. Zaslavsky,et al.  Electrical resistance of island-containing thin metal interconnects on polymer substrates under high strain , 2005 .

[14]  A NEW METHOD TO STUDY CYCLIC DEFORMATION OF THIN FILMS IN TENSION AND COMPRESSION , 1999 .

[15]  Zujian Wang,et al.  Tensile and fatigue strength of ultrathin copper films , 2008 .

[16]  E. Arzt,et al.  Fatigue behavior of polycrystalline thin copper films , 2002 .

[17]  Xiangdong Ding,et al.  Thickness dependent critical strain in submicron Cu films adherent to polymer substrate , 2007 .

[18]  Z. Suo,et al.  Delocalizing strain in a thin metal film on a polymer substrate , 2005 .