Behavior of stainless steels in pressurized water reactor primary circuits

Abstract Stainless steels are widely used in primary circuits of pressurized water reactors (PWRs). Operating experience with the various grades of stainless steels over several decades of years has generally been excellent. Nevertheless, stress corrosion failures have been reported in few cases. Two main factors contributing to SCC susceptibility enhancement are investigated in this study: cold work and irradiation. Irradiation is involved in the stress corrosion cracking and corrosion of in-core reactor components in PWR environment. Irradiated assisted stress corrosion cracking (IASCC) is a complex and multi-physics phenomenon for which a predictive modeling able to describe initiation and/or propagation is not yet achieved. Experimentally, development of initiation smart tests and of in situ instrumentation, also in nuclear reactors, is an important axis in order to gain a better understanding of IASCC kinetics. A strong susceptibility for SCC of heavily cold worked austenitic stainless steels is evidenced in hydrogenated primary water typical of PWRs. It is shown that for a given cold-working procedure, SCC susceptibility of austenitic stainless steels materials increases with increasing cold-work. Results have shown also strong influences of the cold work on the oxide layer composition and of the maximum stress on the time to fracture.

[1]  In-pile electrochemical measurements on AISI 304 and AISI 306 in PWR conditions - : Experimental results , 2007 .

[2]  P. Evrard,et al.  Modelling of the effect of dislocation channel on intergranular microcrack nucleation in pre-irradiated austenitic stainless steels during low strain rate tensile loading , 2010 .

[3]  B. Tanguy,et al.  Initiation Stress Threshold Irradiation Assisted Stress Corrosion Cracking Criterion Assessment for Core Internals in PWR Environment , 2011 .

[4]  Gary S. Was,et al.  Fundamentals of Radiation Materials Science: Metals and Alloys , 2007 .

[5]  K. Fujii,et al.  IASCC Initiation in Highly Irradiated Stainless Steels under Uniaxial Constant Load Conditions , 2008 .

[6]  D. Féron,et al.  Electrochemical behaviour of stainless steel in PWR primary coolant conditions: Effects of radiolysis , 2011 .

[7]  Z. Xia,et al.  Comparative Studies of SCC in Two Austenitic Stainless Steels and Alloy 600 on Exposure to Lithiated Water at 350°C ✫ , 1992 .

[8]  E. Andrieu,et al.  Effect of surface preparation on the corrosion of austenitic stainless steel 304L in high temperature steam and simulated PWR primary water , 2012 .

[9]  D. Delafosse,et al.  Influence of localized deformation on A-286 austenitic stainless steel stress corrosion cracking in PWR primary water , 2007 .

[10]  P. Dubuisson,et al.  Irradiation damage in 304 and 316 stainless steels: experimental investigation and modeling. Part II: Irradiation induced hardening , 2004 .

[11]  Z. Xia,et al.  Stress corrosion cracking of AISI 304 and 316 stainless steels in lithiated water at 350°C , 1992 .

[12]  J. Malaplate,et al.  TEM and EFTEM characterization of solution annealed 304L stainless steel irradiated in PHENIX, up to 36 dpa and at 390 °C , 2012 .

[13]  O. Raquet,et al.  6 – Effect of cold work hardening on stress corrosion cracking of stainless steels in primary water of pressurized water reactors , 2007 .

[14]  P. Combrade,et al.  Effect of chlorides and sulfates on the EAC of austenitic stainless steel in PWR environment , 2007 .

[15]  Z. Jiao,et al.  Impact of localized deformation on IASCC in austenitic stainless steels , 2011 .