Poly(α-hydroxyacids) for application in the spinal cord: Resorbability and biocompatibility with adult rat schwann cells and spinal cord

Future surgical strategies to restore neurological function in the damaged human spinal cord may involve replacement of nerve tissue with cultured Schwann cells using biodegradable guiding implants. We have studied the in vitro and in vivo degradability of various aliphatic polyesters as well as their effects on rat Schwann cells in vitro and on spinal cord tissue in vivo. In vitro, cylinders made of poly(D,L-lactic-co-glycolic acid) 50:50 (PLA25GA50) started to degrade at 7 days, compared with 28 days for cylinders made of poly(D,L-lactic acid) (PLA50). This faster degradation of PLA25GA50 was reflected by a much higher absorption of water. In vivo, after implantation of PLA25GA50 or PLA50 cylinders between the stumps of a completely transected adult rat spinal cord, the decrease in molecular weight of both polymers was similar to that found in vitro. In vitro degradation of poly(L-lactic acid) (PLA100) mixed with increasing amounts of PLA100 oligomers also was determined. The degradation rate of PLA100 mixed with 30% oligomers was found to be similar to that of PLA50. In vitro, PLA25GA50 and the breakdown products had no adverse effect on the morphology, survival, and proliferation of cultured rat Schwann cells. In vivo, PLA25GA50 cylinders were integrated into the spinal tissue 2 weeks after implantation, unlike PLA50 cylinders. At all time points after surgery, the glial and inflammatory response near the lesion site was largely similar in both experimental and control animals. At time points later than 1 week, neurofilament-positive fibers were found within PLA25GA50 cylinders or the remains thereof. Growth-associated protein 43, which is indicative of regenerating axons, was observed in fibers in the vicinity of the injury site and in the remains of PLA25GA50 cylinders. The results suggest that poly(alpha-hydroxyacids) are likely candidates for application in spinal cord regeneration paradigms involving Schwann cells.

[1]  M. Scandola,et al.  Thermal properties and physical ageing of poly (l-lactic acid) , 1992 .

[2]  A. Mikos,et al.  Retinal pigment epithelium cells cultured on synthetic biodegradable polymers. , 1997, Journal of biomedical materials research.

[3]  Aqing Chen,et al.  Methylprednisolone Administration Improves Axonal Regeneration into Schwann Cell Grafts in Transected Adult Rat Thoracic Spinal Cord , 1996, Experimental Neurology.

[4]  Philippe Menei,et al.  Drug targeting into the central nervous system by stereotactic implantation of biodegradable microspheres. , 1994 .

[5]  Suming Li,et al.  Hydrolytic degradation of devices based on poly(DL-lactic acid) size-dependence. , 1995, Biomaterials.

[6]  Susan E. Mackinnon,et al.  Clinical Nerve Reconstruction with a Bioabsorbable Polyglycolic Acid Tube , 1990, Plastic and reconstructive surgery.

[7]  S. Li,et al.  Attempts to map the structure and degradation characteristics of aliphatic polyesters derived from lactic and glycolic acids. , 1994, Journal of biomaterials science. Polymer edition.

[8]  J. Vacanti,et al.  Toward development of an implantable tissue engineered liver. , 1996, Biomaterials.

[9]  A. Mikos,et al.  Degradation of polydispersed poly(L-lactic acid) to modulate lactic acid release. , 1995, Biomaterials.

[10]  R. Reid,et al.  Biodegradable Cuff An Adjunct to Peripheral Nerve Repair: A Study in Dogs , 1978, The Hand.

[11]  M. Bracken,et al.  The Second National Acute Spinal Cord Injury Study. , 1990, Journal of neurotrauma.

[12]  A. Blight.  Delayed demyelination and macrophage invasion: a candidate for secondary cell damage in spinal cord injury. , 1985, Central nervous system trauma : journal of the American Paralysis Association.

[13]  N. Kleitman,et al.  Axonal regeneration into Schwann cell‐seeded guidance channels grafted into transected adult rat spinal cord , 1995, The Journal of comparative neurology.

[14]  M. Vert,et al.  Biocompatibility and resorbability of a polylactic acid membrane for periodontal guided tissue regeneration. , 1993, Biomaterials.

[15]  M. Oudega,et al.  A combination of insulin‐like growth factor‐I and platelet‐derived growth factor enhances myelination but diminishes axonal regeneration into Schwann cell grafts in the adult rat spinal cord , 1997, Glia.

[16]  M. Schwab,et al.  Secondary Cell Death and the Inflammatory Reaction After Dorsal Hemisection of the Rat Spinal Cord , 1994, The European journal of neuroscience.

[17]  A L Dellon,et al.  An Alternative to the Classical Nerve Graft for the Management of the Short Nerve Gap , 1988, Plastic and reconstructive surgery.

[18]  Michel Vert,et al.  In vivo degradation of massive poly(α-hydroxy acids): Validation of In vitro findings , 1992 .

[19]  C. M. Agrawal,et al.  Sterilization, toxicity, biocompatibility and clinical applications of polylactic acid/polyglycolic acid copolymers. , 1996, Biomaterials.

[20]  M. Vert,et al.  Hydrolytic degradation of films prepared from blends of high and low molecular weight poly(DL-lactic acid)s. , 1996, Journal of biomedical materials research.

[21]  J. M. Schakenraad,et al.  A new PLLA/PCL copolymer for nerve regeneration , 1993 .

[22]  R. Sidman,et al.  Peripheral nerve regeneration with entubulation repair: Comparison of biodegradeable nerve guides versus polyethylene tubes and the effects of a laminin-containing gel , 1987, Experimental Neurology.

[23]  R. Sidman,et al.  Nerve Regeneration through Synthetic Biodegradable Nerve Guides: Regulation by the Target Organ , 1984, Plastic and reconstructive surgery.

[24]  Antonios G. Mikos,et al.  Pore Morphology Effects on the Fibrovascular Tissue Growth in Porous Polymer Substrates , 1994, Cell transplantation.

[25]  M. Maltarello,et al.  Effectiveness of a bioabsorbable conduit in the repair of peripheral nerves. , 1996, Biomaterials.

[26]  E. Hall,et al.  Inhibition of lipid peroxidation in CNS trauma. , 1991, Journal of neurotrauma.

[27]  Robert Langer,et al.  Preparation and characterization of poly(l-lactic acid) foams , 1994 .

[28]  P H Robinson,et al.  Long‐term evaluation of nerve regeneration in a biodegradable nerve guide , 1993, Microsurgery.

[29]  J. Benoit,et al.  Biodegradation and brain tissue reaction to poly(D,L-lactide-co-glycolide) microspheres. , 1993, Biomaterials.

[30]  E. Hall,et al.  The neuroprotective pharmacology of methylprednisolone. , 1992, Journal of neurosurgery.

[31]  V. Maquet,et al.  Polylactide macroporous biodegradable implants for cell transplantation. II. Preparation of polylactide foams by liquid-liquid phase separation. , 1996, Journal of biomedical materials research.

[32]  R. Kenley,et al.  Poly(lactide-co-glycolide) decomposition kinetics in vivo and in vitro , 1987 .

[33]  G. Cain,et al.  Bioerosion and biocompatibility of poly(d,l-lactic-co-glycolic acid) implants in brain , 1997 .

[34]  P H Robinson,et al.  Nerve regeneration through a two‐ply biodegradable nerve guide in the rat and the influence of ACTH4‐9 nerve growth factor , 1991, Microsurgery.

[35]  R Langer,et al.  Design and Fabrication of Biodegradable Polymer Devices to Engineer Tubular Tissues , 1994, Cell transplantation.

[36]  P. Aebischer,et al.  A Combination of BDNF and NT-3 Promotes Supraspinal Axonal Regeneration into Schwann Cell Grafts in Adult Rat Thoracic Spinal Cord , 1995, Experimental Neurology.

[37]  J. Vacanti,et al.  Implantation in vivo and retrieval of artificial structures consisting of rabbit and human urothelium and human bladder muscle. , 1993, The Journal of urology.

[38]  Seung Jin Lee,et al.  Porous poly(l-lactide) membranes for guided tissue regeneration and controlled drug delivery: membrane fabrication and characterization , 1997 .

[39]  C. V. van Blitterswijk,et al.  Biocompatibility of a biodegradable matrix used as a skin substitute: an in vivo evaluation. , 1994, Journal of biomedical materials research.

[40]  E. Flamm,et al.  The free radical pathology and the microcirculation in the major central nervous system disorders. , 1980, Acta physiologica Scandinavica. Supplementum.

[41]  Aqing Chen,et al.  Bridging Schwann cell transplants promote axonal regeneration from both the rostral and caudal stumps of transected adult rat spinal cord , 1997, Journal of neurocytology.

[42]  Christian Grandfils,et al.  Biodegradable and macroporous polylactide implants for cell transplantation: 1. Preparation of macroporous polylactide supports by solid-liquid phase separation , 1996 .

[43]  M. Bunge,et al.  The use of schwann cell transplantation to foster central nervous system repair , 1993 .

[44]  Yoshito Ikada,et al.  Thermal characterization of polylactides , 1988 .

[45]  P. Flandroy,et al.  Control of the biodegradation rate of poly (dl-lactide) microparticles intended as chemoembolization materials , 1996 .

[46]  W. D. den Dunnen,et al.  Biological performance of a degradable poly(lactic acid-epsilon-caprolactone) nerve guide: influence of tube dimensions. , 1995, Journal of biomedical materials research.

[47]  M. Oudega,et al.  Nerve Growth Factor Promotes Regeneration of Sensory Axons into Adult Rat Spinal Cord , 1996, Experimental Neurology.

[48]  C H Tator,et al.  Review of the secondary injury theory of acute spinal cord trauma with emphasis on vascular mechanisms. , 1991, Journal of neurosurgery.

[49]  P H Robinson,et al.  Two-ply biodegradable nerve guide: basic aspects of design, construction and biological performance. , 1990, Biomaterials.

[50]  R Langer,et al.  Tissue engineering by cell transplantation using degradable polymer substrates. , 1991, Journal of biomechanical engineering.

[51]  R. Bodmeier,et al.  The effect of the addition of low molecular weight poly(dl-lactide) on drug release from biodegradable poly(dl-lactide) drug delivery systems , 1989 .

[52]  R. Sidman,et al.  Nerve regeneration through biodegradable polyester tubes , 1985, Experimental Neurology.

[53]  S. Bowald,et al.  Regeneration of peripheral nerve through a polyglactin tube , 1982, Muscle & nerve.