Transport properties in metakaolin blended concrete

One of the approaches in improving the durability of concrete is to use blended cement materials such as fly ash, silica fume, slag and more recently, metakaolin. By changing the chemistry and microstructure of concrete, pozzolans reduce the capillary porosity of the cementitious system and make them less permeable to exterior chemical sources as well as reducing the internal chemical incompatibilities such as alkali–silica reaction. This paper presents the results of a study on the transport properties and durability characteristics of concrete containing different levels of metakaolin. Water penetration, gas permeability, water absorption, electrical resistivity, chloride ingress, and alkali–silica reaction potential were studied and their inter-relationships discussed. Results show that substituting optimum levels of metakaolin improves different aspects of the transport properties and durability performance. At 15% replacement level, compressive strength increased by 20%, while the water penetration, gas permeability, water absorption, electrical resistivity and ionic diffusion had improvements of up to 50%, 37%, 28%, 450%, and 47%, respectively and the 28-day ASR expansion for this mix was reduced as much as 82%. The minimum replacement level required for mitigating ASR and the relationship between physical and chemical effects of metakaolin were discussed.

[1]  Luc Courard,et al.  Durability of mortars modified with metakaolin , 2003 .

[2]  Jamal M. Khatib,et al.  Pore size distribution of metakaolin paste , 1996 .

[3]  Michael D. A. Thomas,et al.  The effect of metakaolin on alkali-silica reaction in concrete , 2000 .

[4]  M. Mitchell,et al.  Correlations Between Depth of Water Penetration, Chloride Permeability, and Coefficient of Chloride Diffusion in Plain, Silica Fume, and Fly Ash Cement Concretes , 2008 .

[5]  H. Hilsdorf,et al.  Performance Criteria for concrete Durability , 1995 .

[6]  Mohammad Shekarchi,et al.  Effect of Curing Conditions on the Service Life Design of RC Structures in the Persian Gulf Region , 2008 .

[7]  Jamal M. Khatib,et al.  Portlandite consumption in metakaolin cement pastes and mortars , 1997 .

[8]  Jamal M. Khatib,et al.  Metakaolin concrete at a low water to binder ratio , 2008 .

[9]  John Bensted,et al.  Structure and Performance of Cements , 2001 .

[10]  R. Hooton,et al.  Influence of the C/S and C/A ratios of hydration products on the chloride ion binding capacity of lime-SF and lime-MK mixtures , 2008 .

[11]  E. Garboczi,et al.  Simulation Studies of the Effects of Mineral Admixtures on the Cement Paste-Aggregate Interfacial Zone (SP-105) , 1991 .

[12]  D. Sorrentino,et al.  Influence of key cement chemical parameters on the properties of metakaolin blended cements , 2001 .

[13]  Jamal M. Khatib,et al.  ABSORPTION CHARACTERISTICS OF METAKAOLIN CONCRETE , 2004 .

[14]  K. Kurtis,et al.  Influence of metakaolin surface area on properties of cement-based materials , 2007 .

[15]  J. Kropp,et al.  Performance criteria for concrete durability : state of the art report prepared by RILEM Technical Committee TC 116-PCD, Performance of Concrete as a Criterion of its Durability , 1995 .

[16]  J. Brooks,et al.  Effect of admixtures on the setting times of high-strength concrete , 2000 .

[17]  E. Badogiannis,et al.  Exploitation of poor Greek kaolins: Durability of metakaolin concrete , 2009 .

[18]  Min-Hong Zhang,et al.  Characteristics of a thermally activated alumino-silicate pozzolanic material and its use in concrete , 1995 .

[19]  G. Kakali,et al.  Metakaolin as a main cement constituent. Exploitation of poor Greek kaolins , 2005 .

[20]  S. Wild,et al.  Relative strength, pozzolanic activity and cement hydration in superplasticised metakaolin concrete , 1996 .

[21]  K. Kurtis,et al.  Influence of Portland Cement Composition on Early Age Reactions with Metakaolin , 2007 .

[22]  W. Aquino,et al.  The influence of metakaolin and silica fume on the chemistry of alkali-silica reaction products , 2001 .

[23]  Y. Tsuji,et al.  Determination of chloride diffusion coefficient and gas permeability of concrete and their relationship , 1996 .

[24]  A. Bonakdar,et al.  Properties of High-Performance Concrete Containing High Reactivity Metakaolin , 2005 .

[25]  P B Bamforth,et al.  The relationship between permeability coefficients for concrete obtained using liquid and gas , 1987 .

[26]  A. Dunster,et al.  The pozzolanic reaction of metakaolinite and its effects on Portland cement hydration , 1993 .

[27]  Min-hong Zhang,et al.  Permeability of High-Strength Lightweight Concrete , 1991 .

[28]  Andrea Boddy,et al.  Long-term testing of the chloride-penetration resistance of concrete containing high-reactivity metakaolin , 2001 .

[29]  C. Poon,et al.  Rate of pozzolanic reaction of metakaolin in high-performance cement pastes , 2001 .