Polycarboxylate superplasticiser admixtures: effect on hydration, microstructure and rheological behaviour in cement pastes

A study was conducted on the effect of a polycarboxylate (PC) admixture on the mechanical, mineralogical, microstructural and rheological behaviour of Portland cement pastes. It was observed that the presence of PC admixture retards the initial cement hydration reactions, although this effect may be offset by possible increased diffusion in later stages. Additionally, the PC admixtures produce a few alterations in the structure and composition of the formed C—S—H gel. The addition of 1% PC admixture in the pastes generates a higher percentage of silicate bridge (Si Q2 units) mainly at 2 days. The admixture used in this study induced microstructural modifications in the pastes which slightly reduced the porosity; however the admixture did not affect the mechanical strength of the pastes at either 2 or 28 days of hydration. Finally, from the results of the rheological studies it was concluded that a low dosage of PC led to a substantial reduction (over 70%) in the yield stress.

[1]  P. Aitcin,et al.  Ettringite formation: A crucial step in cement superplasticizer compatibility , 2003 .

[2]  R. Gettu,et al.  Study of the influence of superplasticizers on the hydration of cement paste using nuclear magnetic resonance and X-ray diffraction techniques , 2002 .

[3]  John Bensted,et al.  Hydration of Portland Cement , 1983 .

[4]  T. Vázquez,et al.  Hidratacion inicial del cemento. Efecto de aditivos superplastificantes , 2001 .

[5]  A. Chatterji,et al.  Hydration of Portland Cement , 1965, Nature.

[6]  Kazuo Yamada,et al.  Interaction between cement and chemical admixture from the point of cement hydration, absorption behaviour of admixture, and paste rheology , 1999 .

[7]  S. Hanehara,et al.  Effects of the chemical structure on the properties of polycarboxylate-type superplasticizer , 2000 .

[8]  H. Uchikawa,et al.  The role of steric repulsive force in the dispersion of cement particles in fresh paste prepared with organic admixture , 1997 .

[9]  Daisuke Sawaki,et al.  Influence of kind and added timing of organic admixture on the composition, structure and property of fresh cement paste , 1995 .

[10]  P. Hendra,et al.  The Raman spectroscopy of cement minerals under 1064 nm excitation , 1993 .

[11]  Robert Schennach,et al.  A review of cement–superplasticizer interactions and their models , 2000 .

[12]  H. J. Jakobsen,et al.  Characterization of calcium aluminate phases in cements by aluminum-27 MAS NMR spectroscopy , 1993 .

[13]  V M Malhotra,et al.  SUPLERPLASTICIZERS : PROPERTIES AND APPLICATIONS IN CONCRETE , 1998 .

[14]  Francisca Puertas,et al.  Pore solution in alkali-activated slag cement pastes. Relation to the composition and structure of calcium silicate hydrate , 2004 .

[15]  X. Cong,et al.  Raman spectroscopy of C-S-H, tobermorite, and jennite , 1997 .

[16]  J. Bensted,et al.  Some applications of infrared and raman spectroscopy in cement chemistry. Part 3 - hydration of portland cement and its constituents , 1974 .

[17]  Chiara F. Ferraris,et al.  The influence of mineral admixtures on the rheology of cement paste and concrete , 2001 .

[18]  Study of the strength of very young concrete as a function of the amount of hydrates formed—influence of superplasticizer , 1994 .

[19]  V. M. Malhotra,et al.  The rheology of fresh concrete , 1984 .

[20]  P. Hewlett,et al.  15 – Cement Admixtures , 1998 .

[21]  C. Jolicoeur,et al.  Chemical admixture-cement interactions: Phenomenology and physico-chemical concepts , 1998 .