Magnetic nanodot arrays produced by direct laser interference lithography

Periodic magnetic nanodot arrays have been produced on an area as large as 1 cm×1 cm by direct nanolithography using interferometric laser radiation. The dots are formed by the local annealing of sputtered amorphous Co–C films in regions where the laser intensity is highest. At room temperature the dots exhibit ferromagnetic order and are embedded in a paramagnetic matrix. The onset of room-temperature ferromagnetism is caused by nanoscale chemical and morphological changes during dot formation and reflects the phase separation of magnetic Co-rich clusters. The present single-step nanolithography is potentially an efficient method for fabrication of patterned magnetic arrays.

[1]  R. Sinclair,et al.  Crystallization of co-sputtered amorphous cobalt-carbon alloys , 1994 .

[2]  M. Ravet,et al.  Thermal evolution of X/C multilayers (with X=W, Ni, or SiWSi): A systematic study , 1990 .

[3]  Picosecond infrared holography on bismuth film , 1974 .

[4]  S. Chou,et al.  Study of nanoscale magnetic structures fabricated using electron‐beam lithography and quantum magnetic disk , 1994 .

[5]  D. Sellmyer,et al.  STRUCTURAL AND MAGNETIC PROPERTIES OF NANOCOMPOSITE CO:C FILMS , 1999 .

[6]  Takayoshi Hayashi,et al.  Formation and microstructural analysis of co-sputtered thin films consisting of cobalt nanograins embedded in carbon , 1997 .

[7]  F. Petroff,et al.  Structural and magnetic properties of Fex–C1−x nanocomposite thin films , 2000 .

[8]  Claude Chappert,et al.  Nanoscale Magnetic Domains in Mesoscopic Magnets , 1996, Science.

[9]  A. Hawryluk,et al.  Fabrication of sub‐0.5 μm diameter cobalt dots on silicon substrates and photoresist pedestals on 50 cm×50 cm glass substrates using laser interference lithograph , 1996 .

[10]  Zuimin Jiang,et al.  Thermal stability of multilayer films Pt/Si, W/Si, Mo/Si, and W/C , 1989 .

[11]  Caroline A. Ross,et al.  Properties of large-area nanomagnet arrays with 100 nm period made by interferometric lithography , 1999 .

[12]  Y. Yao,et al.  Development of high coercivity magnetic force microscopy tips , 1998 .

[13]  P. J. Bedrossian,et al.  Magnetic force microscopy of single-domain cobalt dots patterned using interference lithography , 1996 .

[14]  Peter Vettiger,et al.  Ion-beam patterning of magnetic films using stencil masks , 1999 .

[15]  Masato Tomita,et al.  Magnetic thin films of cobalt nanocrystals encapsulated in graphite-like carbon , 1996, Nature.

[16]  Ralph Skomski,et al.  Quasicoherent nucleation mode in two-phase nanomagnets , 1999 .