Elaboration of CO2 tolerance limits of BaCe0.9Y0.1O3–δ electrolytes for fuel cells and other applications

Abstract The carbonation and decarbonation behaviour of BaCe 0.9 Y 0.1 O 2.95 (BCY10) powder has been investigated as a function of gas composition and temperature by thermogravimetric analysis and X-ray powder diffraction. The results obtained have been used to establish stability limits, which seem to indicate long-term stability for BCY10 under certain conditions. BCY10 powder is stable in pure CO 2 above 1150 °C. In atmospheres containing up to 9% CO 2 in argon, BCY10 is stable above 750 °C. Carbonated powders loose CO 2 above 700 °C when heated in air, or oxygen and at 620 °C in 5% hydrogen. BCY10 partly decomposes on ageing in pure CO 2 at 500 °C. The onset of the reverse water–gas shift reaction changes to lower temperatures in the presence of BCY10 powder. These results were obtained for powder samples and should be viewed as an accelerated ageing test. Overall these results imply that under fuel cell conditions BCY10 should be resistant to carbonation even in a hydrocarbon fuelled fuel cell at temperatures above 750 °C. In the worst case scenario with 100% hydrocarbon oxidation, no added water and assuming no localised benefit from the gas shift reaction carbonation could occur up to 925 °C. Fully densified electrolytes, especially with an electrode coating, should be much more resistant to carbonation, at least when there is no exolved alkaline earth rich phases at the grain boundary, something that can occur with unoptimised sintering or inappropriate choice of stoichiometry.

[1]  B. Ellis,et al.  Construction and operation of fuel cells based on the solid electrolyte BaCeO3:Gd , 1991 .

[2]  A. Virkar,et al.  Stability of AB 1 / 2 ′ B ″ 1 / 2 O 3 ‐ Type Mixed Perovskite Proton Conductors , 1999 .

[3]  S. Haile,et al.  The influence of cation non-stoichiometry on the properties of undoped and gadolinia-doped barium cerate , 1997 .

[4]  Srikanth Gopalan,et al.  Thermodynamic Stabilities of SrCeO3 and BaCeO3 Using a Molten Salt Method and Galvanic Cells , 1993 .

[5]  N. Bonanos.  Oxide-based protonic conductors: point defects and transport properties , 2001 .

[6]  K. Knight,et al.  The crystal structures of some doped and undoped alkaline earth cerate perovskites , 1995 .

[7]  A. Kruth.  Water incorporation studies on doped barium cerate perovskites , 2003 .

[8]  R. C. Weast.  CRC Handbook of Chemistry and Physics , 1973 .

[9]  U. Balachandran,et al.  The crystal structures and phase transitions in Y-doped BaCeO3: their dependence on Y concentration and hydrogen doping , 2000 .

[10]  H. Iwahara,et al.  Protonic and oxide ionic conduction in BaCeO3-based ceramics — effect of partial substitution for Ba in BaCe0.9O3−α with Ca , 1991 .

[11]  Guilin Ma,et al.  Ionic conduction and nonstoichiometry in BaxCe0.90Y0.10O3−α , 1998 .

[12]  K. Sandhage,et al.  Fabrication of Dense, Shaped Barium Cerate by the Oxidation of Solid Metal‐Bearing Precursors , 1996 .

[13]  K. Knight.  Structural phase transitions in BaCeO3 , 1994 .

[14]  A. Virkar,et al.  Instability of BaCeO3 in H2O-containing atmospheres , 1996 .

[15]  Kevin S. Knight,et al.  Structural phase transitions, oxygen vacancy ordering and protonation in doped BaCeO3: results from time-of-flight neutron powder diffraction investigations , 2001 .

[16]  K. Knight.  Powder neutron diffraction studies of BaCe0.9Y0.1O2.95 and BaCeO3 at 4.2 K: a possible structural site for the proton , 2000 .

[17]  K. Knight,et al.  Perovskite solid electrolytes: Structure, transport properties and fuel cell applications , 1995 .

[18]  S. Haile,et al.  Non-stoichiometry, grain boundary transport and chemical stability of proton conducting perovskites , 2001 .