Matrix cracking and delamination in laminated composites. Part I: Ply constitutive law, first ply failure and onset of delamination

Abstract Matrix cracking and delamination are the main initial forms of damage in advanced laminated composites manufactured by stacking unidirectional plies of fiber reinforced polymers. In this paper, the onset of matrix cracking is determined for in-plane stress states; in addition, delamination promoted by matrix cracks is analyzed. Taking into account that under in-plane shear stresses composite laminates show a non-linear response prior to the formation of a macro-crack, a plastic-damage model is proposed and implemented. The models predictions correlate well with published experimental data.

[1]  H. Schürmann,et al.  FAILURE ANALYSIS OF FRP LAMINATES BY MEANS OF PHYSICALLY BASED PHENOMENOLOGICAL MODELS , 1998 .

[2]  George J. Dvorak,et al.  Analysis of Progressive Matrix Cracking in Composite Laminates I. Thermoelastic Properties of a Ply with Cracks , 1985 .

[3]  Fu-Kuo Chang,et al.  An Accumulative Damage Model for Tensile and Shear Failures of Laminated Composite Plates , 1995 .

[4]  Z. Bažant,et al.  Theory of Crack Spacing in Concrete Pavements , 1997 .

[5]  P. Camanho,et al.  A Micromechanics-Based Damage Model for [+/- Theta/90n]s Composite Laminates , 2006 .

[6]  Fu-Kuo Chang,et al.  The In Situ Ply Shear Strength Distributions in Graphite/Epoxy Laminated Composites , 1987 .

[7]  Pedro P. Camanho,et al.  Failure Criteria for FRP Laminates , 2005 .

[8]  P.P. Camanho,et al.  A Three-dimensional Damage Model for Transversely Isotropic Composite Laminates , 2008 .

[9]  J. Nairn.  APPLICATIONS OF FINITE FRACTURE MECHANICS FOR PREDICTING FRACTURE EVENTS IN COMPOSITES , 1999 .

[10]  P. D. Soden,et al.  Lamina properties, lay-up configurations and loading conditions for a range of fibre-reinforced composite laminates , 1998 .

[11]  Pedro P. Camanho,et al.  Mechanical Response of Composites , 2008 .

[12]  A. Evans,et al.  The thermomechanical integrity of thin films and multilayers , 1995 .

[13]  W. Paepegem,et al.  Modelling the nonlinear shear stress–strain response of glass fibre-reinforced composites. Part II: Model development and finite element simulations , 2006 .

[14]  John A. Nairn,et al.  Fracture mechanics analysis of coating/substrate systems Part I: Analysis of tensile and bending experiments , 2000 .

[15]  Mototsugu Tanaka,et al.  Experimental determination of the true epoxy resin strength using micro-scaled specimens , 2007 .

[16]  J. E. Bailey,et al.  Multiple transverse fracture in 90° cross-ply laminates of a glass fibre-reinforced polyester , 1977 .

[17]  P. Camanho,et al.  Mixed-Mode Decohesion Finite Elements for the Simulation of Delamination in Composite Materials , 2002 .

[18]  Pierre Ladevèze,et al.  An enhanced mesomodel for laminates based on micromechanics , 2002 .

[19]  P. D. Soden,et al.  Biaxial test results for strength and deformation of a range of E-glass and carbon fibre reinforced composite laminates: failure exercise benchmark data , 2002 .

[20]  Pedro P. Camanho,et al.  Failure Models and Criteria for Frp Under In-Plane or Three-Dimensional Stress States Including Shear Non-Linearity , 2013 .

[21]  Pierre Ladevèze,et al.  A mesomodel for localisation and damage computation in laminates , 2000 .

[22]  G. Dvorak,et al.  Analysis of first ply failure in composite laminates , 1986 .

[23]  L. McCartney.  Physically based damage models for laminated composites , 2003 .

[24]  Z. Hashin.  Failure Criteria for Unidirectional Fiber Composites , 1980 .

[25]  W. Paepegem,et al.  Modelling the nonlinear shear stress-strain response of glass fibre- reinforced composites. Part I: Experimental results , 2006 .

[26]  Zvi Hashin,et al.  Finite thermoelastic fracture criterion with application to laminate cracking analysis , 1996 .

[27]  Pedro P. Camanho,et al.  Analytical Modelling of Transverse Matrix Cracking of {±θ/90n} s Composite Laminates under Multiaxial Loading , 2010 .

[28]  Zvi Hashin,et al.  Fatigue Failure Criteria for Unidirectional Fiber Composites , 1981 .

[29]  M. Benzeggagh,et al.  Measurement of mixed-mode delamination fracture toughness of unidirectional glass/epoxy composites with mixed-mode bending apparatus , 1996 .

[30]  G. Maugin.  The Thermomechanics of Plasticity and Fracture , 1992 .

[31]  Stephen W. Tsai,et al.  Nonlinear Elastic Behavior of Unidirectional Composite Laminae , 1973 .

[32]  Pedro P. Camanho,et al.  Prediction of in situ strengths and matrix cracking in composites under transverse tension and in-plane shear , 2006 .

[33]  J. Hutchinson,et al.  Crack patterns in thin films , 2000 .

[34]  H. T. Hahn,et al.  A Mixed-Mode Fracture Criterion for Composite Materials , 1983 .

[35]  Norman Laws,et al.  Analysis of Progressive Matrix Cracking In Composite Laminates II. First Ply Failure , 1987 .

[36]  J. Nairn,et al.  Fracture mechanics analysis of coating/substrate systems: Part II: Experiments in bending , 2000 .

[37]  Ramesh Talreja,et al.  Damage in composite laminates with off-axis plies , 1999 .

[38]  M. G. Bader,et al.  Transverse Ply Cracking in Cross-Ply CFRP Laminates—Initiation or Propagation Controlled? , 1997 .

[39]  Roberts Joffe,et al.  Analytical modeling of stiffness reduction in symmetric and balanced laminates due to cracks in 90° layers , 1999 .

[40]  J. Nairn.  On the calculation of energy release rates for cracked laminates with residual stresses , 2006 .