Strain rate sensitivity and the portevin-le chatelier effect in Au–Cu alloys

The effect of strain rate changes on the flow stress of Au–Cu alloys in the region of strain prior to the start of serrated yielding has been investigated. The measurements of Δσ/Δ Δσ/Δ were found to depend on strain, strain rate, temperature, and composition. Negative values of Δσ/Δ ln ϵ were observed prior to the onset of serrated yielding. The effect of base strain rate on the strain rate sensitivity of the flow stress was correlated with the effect of ϵ on the strain at the onset of serrated yielding. The results are interpreted in terms of a recent model for dynamic strain ageing based on the diffusion of solute atoms to temporarily arrested dislocations. The occurrence of pronounced flow stress transients accompanying strain rate changes was also investigated. Der Einflus der Anderung der Deformationsgeschwindigkeit auf die Fliesspanung von Au–Cu-Legierungen im Deformationsbereich vor dem Einsatz des stufenweisen Fliesens wird untersucht. Es wird gefunden, das Δσ/Δ Δσ/Δ von der Deformation, Deformationsgeschwindigkeit, Temperatur und Zusammensetzung abhangt. Vor dem Einsatz des stufenweisen Fliesens werden negative Werte von Δσ/Δ ln ϵ beobachtet. Der Einflus der Deformationsgeschwindigkeit auf die Deformationsgeschwindigkeitsempfindlichkeit der Fliesspannung wird mit dem Einflus von ϵ auf die Deformation beim Einsetzen des stufenweisen Fliesens korreliert. Die Ergebnisse werden mit einem kurzlich veroffentlichten Modell fur dynamische Deformationsalterung, das auf der Diffusion von gelosten Atomen zu zeitweise festgesetzten Versetzungen beruht, interpretiert. Auch das Auftreten von ausgepragtem Einschwingverhalten der Fliesspannung, das mit den Anderungen der Deformationsgeschwindigkeit verbunden ist, wird untersucht.