Dislocation-grain boundary interactions in martensitic steel observed through in situ nanoindentation in a transmission electron microscope

Dislocation-interface interactions in Fe-0.4 wt% C tempered martensitic steel were studied through in situ nanoindentation in a transmission electron microscope (TEM). Two types of boundaries were imaged in the dislocated martensitic structure: a low-angle (probable) lath boundary and a coherent, high-angle (probable) block boundary. In the case of a low-angle grain boundary, the dislocations induced by the indenter piled up against the boundary. As the indenter penetrated further, a critical stress appeared to have been reached, and a high density of dislocations was suddenly emitted on the far side of the grain boundary into the adjacent grain. In the case of the high-angle grain boundary, the numerous dislocations that were produced by the indentation were simply absorbed into the boundary, with no indication of pileup or the transmission of strain. This surprising observation is interpreted on the basis of the crystallography of the block boundary.

[1]  Z. Guo,et al.  On coherent transformations in steel , 2004 .

[2]  K. Tsuzaki,et al.  Evaluation of temper softening behavior of Fe–C binary martensitic steels by nanoindentation , 2003 .

[3]  K. Tsuzaki,et al.  Relationship between nanohardness and microstructures in high-purity Fe–C as-quenched and quench-tempered martensite , 2003 .

[4]  Tadashi Furuhara,et al.  The morphology and crystallography of lath martensite in Fe-C alloys , 2003 .

[5]  Z. Guo,et al.  The Nature and Consequences of Coherent Transformations in Steel , 2003 .

[6]  K. Tsuzaki,et al.  Evaluation of the matrix strength of Fe-0.4 wt% C tempered martensite using nanoindentation techniques , 2002 .

[7]  Zhenyou Guo.  The limit of strength and toughness of steel , 2001 .

[8]  K. Tsuzaki,et al.  Nanohardness measurement of high-purity Fe–C martensite , 2001 .

[9]  J. W. Morris,et al.  Quantitative in situ nanoindentation in an electron microscope , 2001 .

[10]  A. Minor,et al.  Development of a Nanoindenter for In Situ Transmission Electron Microscopy , 2001, Microscopy and Microanalysis.

[11]  Y. Kim,et al.  Thermal Mechanisms of Grain and Packet Refinement in a Lath Martensitic Steel , 1998 .

[12]  Ian M. Robertson,et al.  AnIn Situ transmission electron microscope deformation study of the slip transfer mechanisms in metals , 1990 .

[13]  R. H. Wagoner,et al.  Dislocation and grain boundary interactions in metals , 1988 .

[14]  R. H. Wagoner,et al.  Dislocation pile-up and grain boundary interactions in 304 stainless steel , 1986 .

[15]  K. Tsuzaki,et al.  The Morphology of Microstructure Composed of Lath Martensites in Steels , 1980 .

[16]  M. Ashby.  The deformation of plastically non-homogeneous materials , 1970 .

[17]  D. Mclean,et al.  Slip nuclei in silicon-iron , 1965 .

[18]  B. Chalmers,et al.  The plastic deformation of bicrystals of f.c.c. metals , 1961 .

[19]  E. Hall,et al.  The Deformation and Ageing of Mild Steel: III Discussion of Results , 1951 .

[20]  E. Hall,et al.  The Deformation and Ageing of Mild Steel , 1951 .

[21]  W. Zieliński,et al.  IN SITU INVESTIGATION OF THE EARLY STAGES OF PLASTIC DEFORMATION IN AN AUSTENITIC STAINLESS STEEL , 1984 .

[22]  N. Petch,et al.  The Cleavage Strength of Polycrystals , 1953 .