Subcritical crack growth of edge and center cracks in façade rock panels subject to periodic surface temperature variations

This paper examines subcritical cracking in a rock panel or slab containing either a pre-existing edge or a center crack perpendicular to the panel surface. The panel is subject to periodic surface temperature variation on one side of the panel while the other is kept at a constant temperature. The thermally induced stress intensity factors are determined using superposition technique by employing the fundamental point load solution for an edge crack or a center crack in a slab of finite thickness. Rock panel is modeled as a long elastic strip with either a free or a fully constrained lateral end condition. The temperature variations versus time at various depths of the rock panel appear roughly as a sinusoidal function. The lateral thermal stress for the free end case is larger than the constrained end case; whereas stress intensity factors for both edge and center cracks in the constrained end slab are 1000 times larger than that of free end case. Subcritical crack propagation in rock panels on facade is then estimated as a function of time. This subcritical crack propagation continues until a critical crack size is attained and the rock panel will fail under wind load. This new theoretical framework provides a new paradigm to examine the mechanisms of time-dependent cracking in rock panels on facade of buildings.

[1]  R. J. Charles,et al.  Static Fatigue of Glass. II , 1958 .

[2]  Philip G. Meredith,et al.  4 – THE THEORY OF SUBCRITICAL CRACK GROWTH WITH APPLICATIONS TO MINERALS AND ROCKS , 1987 .

[3]  K. Chau,et al.  Microcracking in coarse and fine grain marbles , 1995 .

[4]  F. Hauser,et al.  Deformation and Fracture Mechanics of Engineering Materials , 1976 .

[5]  J. C. Jaeger,et al.  Fundamentals of rock mechanics , 1969 .

[6]  Siegfried Siegesmund,et al.  Physical weathering of marbles caused by anisotropic thermal expansion , 2000 .

[7]  A. Rizk,et al.  Fracture of a plate under transient thermal stresses , 1993 .

[8]  Bernd Leiss,et al.  Fabric anisotropy and its influence on physical weathering of different types of Carrara marbles , 2000 .

[9]  Erhard M. Winkler,et al.  Stone in Architecture , 1994 .

[10]  Gianni Royer-Carfagni.  Some considerations on the warping of marble façades: the example of Alvar Aalto’s Finland Hall in Helsinki , 1999 .

[11]  Y. Mahmutoğlu.  Mechanical Behaviour of Cyclically Heated Fine Grained Rock , 1998 .

[12]  B. Atkinson.  Subcritical crack growth in geological materials , 1984 .

[13]  K. Chau,et al.  Stress Concentration Reduction at a Reinforced Hole Loaded by a Bonded Circular Inclusion , 2001 .

[14]  Lord Rayleigh,et al.  The Bending of Marble , 1934 .

[15]  Gianni Royer-Carfagni,et al.  On the thermal degradation of marble , 1999 .

[16]  Mark A. Chacon.  Architectural Stone: Fabrication, Installation, and Selection , 1999 .

[17]  Gene Simmons,et al.  Cracks in building stone , 1993 .

[18]  J. M. Logan,et al.  A case study of the properties of marble as building veneer , 1993 .

[19]  J. C. Jaeger,et al.  Conduction of Heat in Solids , 1952 .

[20]  Walter Salvatore,et al.  The characterization of marble by cyclic compression loading: experimental results , 2000 .

[21]  Paola Marini,et al.  Experimental Studies on the Mechanical Behaviour of two Thermal Cracked Marbles , 2001 .

[22]  Elmar Karl Tschegg,et al.  Anisotropic Thermal Expansion Causes Deformation of Marble Claddings , 1996 .

[23]  J. C. Jaeger,et al.  FUNDAMENTALS OF ROCK MECHANICS, SECOND EDITION , 1976 .

[24]  Alberto Meda,et al.  Flexural strength and notch sensitivity in natural building stones: Carrara and Dionysos marble , 1999 .

[25]  K. Chau,et al.  A finite strip loaded by a bonded-rivet of a different material , 1999 .

[26]  Michael D. Lewis.  Modern stone cladding : design and installation of exterior dimension stone systems , 1995 .

[27]  Marco Franzini,et al.  Stones in monuments: natural and anthropogenic deterioration of marble artifacts , 1995 .

[28]  William H. Press,et al.  The Art of Scientific Computing Second Edition , 1998 .

[29]  William H. Press,et al.  Numerical recipes in C. The art of scientific computing , 1987 .

[30]  K. T. Chau,et al.  Microcracking and grain size effect in Yuen Long marbles , 1996 .

[31]  M Y L Chew,et al.  Building facades : A guide to common defects in tropical climates , 1998 .

[32]  K. T. Chau,et al.  An infinite plane loaded by a rivet of a different material , 1997 .

[33]  Michael Alber,et al.  Generation and visualization of microfractures in Carrara marble for estimating fracture toughness, fracture shear and fracture normal stiffness , 1999 .

[34]  V. Sglavo,et al.  Sandwiched-Beam Procedure for Precracking Brittle Materials , 2004 .

[35]  M. R. Smith.  Stone: Building Stone, Rock Fill and Armourstone in Construction , 1999 .

[36]  R O Ritchie,et al.  Cyclic fatigue-crack propagation in sapphire in air and simulated physiological environments. , 2000, Journal of biomedical materials research.

[37]  A. Rizk.  EDGE-CRACKED PLATE WITH ONE FREE AND ONE CONSTRAINED BOUNDARY SUBJECTED TO SUDDEN CONVECTIVE COOLING , 1994 .

[38]  Kinichiro Kusunose,et al.  Fracture Mechanics of Rocks , 1995 .

[39]  Julie Mark Cohen,et al.  Durability and Integrity of Marble Cladding: A State-of-the-Art Review , 1991 .

[40]  A. Rizk,et al.  Transient thermal stress problem for a cracked semi-infinite medium , 1992 .

[41]  D. Rooke,et al.  The compendium of stress intensity factors , 1978, International Journal of Fracture.

[42]  H. S. Carslow,et al.  Conduction of Heat in Solids, Second Edition , 1986 .

[43]  Y. Okui,et al.  Micromechanics-based prediction of creep failure of hard rock for long-term safety of high-level radioactive waste disposal system , 2003 .

[44]  Seymour A. Bortz,et al.  Laboratory Evaluation of Building Stone Weathering , 1997 .

[45]  Erhard M. Winkler.  Stone: properties, durability in man's environment , 1973 .