EFFECT OF LOW‐TEMPERATURE ELECTRON IRRADIATION ON YOUNG'S MODULUS OF PURE Cu

A Cu sample was irradiated at 20 deg K with 1.0- to 0.35Mev electrons. The sample, 0.13 mm thick, gave a degradation of about 0.25 Mev. An increase in the modulus was observed from electrons as low as 0.40 Mev. (R.E.U.)

A. Sosin | D. Keefer

[1] A. Sosin. DISLOCATION PINNING IN COPPER AT 4.2 K AND IN STAGE I , 1962 .

[2] V. Paré,et al. Temperature dependence from 250°K to 370°K of dislocation pinning in copper single crystals by radiation defects , 1962 .

[3] J. Brinkman,et al. THERMALLY ACTIVATED POINT DEFECT MIGRATION IN COPPER , 1960 .

[4] A. Sosin,et al. Effect of Electron Irradiation and Subsequent Thermal Treatment on Young's Modulus of Copper , 1960 .

[5] J. Brinkman,et al. Electrical Resistivity Study of Lattice Defects Introduced in Copper by 1.25-Mev Electron Irradiation at 80°K , 1956 .

[6] J. Friedel. XLVI. Anomaly in the rigidity modulus of copper alloys for small concentrations , 1953 .

[7] N. Mott. CXVII. A theory of work-hardening of metal crystals , 1952 .