Ultra-low reflection porous silicon nanowires for solar cell applications

High density vertically aligned Porous Silicon NanoWires (PSiNWs) were fabricated on silicon substrate using metal assisted chemical etching process. A linear dependency of nanowire length to the etching time was obtained and the change in the growth rate of PSiNWs by increasing etching durations was shown. A typical 2D bright-field TEM image used for volume reconstruction of the sample shows the pores size varying from 10 to 50 nm. Furthermore, reflectivity measurements show that the 35% reflectivity of the starting silicon wafer drops to 0.1%, recorded for more than 10 μm long PSiNWs. Models based on cone shape of nanowires located in a circular and rectangular bases were used to calculate the reflectance employing the Transfert Matrix Formalism (TMF) of the PSiNWs layer. Using TMF, the Bruggeman model was used to calculate the refractive index of PSiNWs layer. The calculated reflectance using circular cone shape fits better the measured reflectance for PSiNWs. The remarkable decrease in optical reflectivity indicates that PSiNWs is a good antireflective layer and have a great potential to be utilized in radial or coaxial p-n heterojunction solar cells that could provide orthogonal photon absorption and enhanced carrier collection.

[1]  Charles M. Lieber,et al.  Coaxial silicon nanowires as solar cells and nanoelectronic power sources , 2007, Nature.

[2]  Melissa Anne Fardy.  Semiconductor Nanowires and Nanotubes for Energy Conversion , 2010 .

[3]  Joël Charrier,et al.  Optical gain at 1.53 μm in Er3+–Yb3+ co-doped porous silicon waveguides , 2008 .

[4]  Shinji Yae,et al.  Antireflective porous layer formation on multicrystalline silicon by metal particle enhanced HF etching , 2006 .

[5]  Z. Pei,et al.  Ultra high-density silicon nanowires for extremely low reflection in visible regime , 2011 .

[6]  W. Theiß,et al.  Optical properties of porous silicon , 1997 .

[7]  M. Miu,et al.  The optical properties of porous silicon , 2008, 2008 International Nano-Optoelectronics Workshop.

[8]  M. Oueslati,et al.  Optical gain measurements in porous silicon planar waveguides codoped by erbium and ytterbium ions at 1.53μm , 2007 .

[9]  Gang Chen,et al.  Analysis of optical absorption in silicon nanowire arrays for photovoltaic applications. , 2007, Nano letters.

[10]  Otto L Muskens,et al.  Design of light scattering in nanowire materials for photovoltaic applications. , 2008, Nano letters.

[11]  J. Rand,et al.  Silicon Nanowire Solar Cells , 2007 .

[12]  N. Lewis.  Toward Cost-Effective Solar Energy Use , 2007, Science.

[13]  Charles M. Lieber,et al.  Epitaxial core–shell and core–multishell nanowire heterostructures , 2002, Nature.

[14]  L. Tsakalakos.  Nanostructures for photovoltaics , 2008 .

[15]  Peidong Yang,et al.  Silicon nanowire radial p-n junction solar cells. , 2008, Journal of the American Chemical Society.

[16]  Nathan S. Lewis,et al.  Comparison of the device physics principles of planar and radial p-n junction nanorod solar cells , 2005 .

[17]  D. Aspnes.  Optical properties of thin films , 1982 .

[18]  Yunjie Yan,et al.  Aligned single-crystalline Si nanowire arrays for photovoltaic applications. , 2005, Small.

[19]  F. Falk,et al.  Silicon nanowire-based solar cells , 2008, Nanotechnology.

[20]  A. Gawlik,et al.  Silicon nanowire-based solar cells on glass: synthesis, optical properties, and cell parameters. , 2009, Nano letters.

[21]  G. Michael Morris,et al.  Design, fabrication, and characterization of subwavelength periodic structures for semiconductor antireflection coating in the visible domain , 1996, Optical Systems Design.

[22]  L. Canham.  Silicon quantum wire array fabrication by electrochemical and chemical dissolution of wafers , 1990 .

[23]  Yun Jeong Hwang,et al.  Single crystalline mesoporous silicon nanowires. , 2009, Nano letters.

[24]  P. Vitanov,et al.  High-efficiency solar cell using a thin porous silicon layer , 1997 .

[25]  Y. Nakato,et al.  Efficient and stable solar to chemical conversion with n+−p junction crystalline silicon electrodes having textured surfaces , 1988 .