Magnetocaloric effect in nanogranular glass coated microwires

Thermal dependences of the magnetic susceptibility of the glass-coated microwires with compositions Fe3P and SnMn prepared by the Taylor–Ulitovski method have been determined. Direct measurements of the adiabatic temperature change revealed ΔTad of 0.04 K in the SnMn and ΔTad of 0.02 K in the Fe3P microwires on the field change of 12 kOe. Temperatures of the peak values of MCE were found to be of ∼215 K and ∼320 K respectively. The variation of magnetic properties of the Fe3P wires with the change of their diameters was observed. (© 2008 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim)

[1] E. Brück,et al. Developments in magnetocaloric refrigeration , 2005 .

[2] G. F. Taylor. A Method of Drawing Metallic Filaments and a Discussion of their Properties and Uses , 1924 .

[3] D. Jiles. Recent advances and future directions in magnetic materials , 2003 .

[4] Vitalij K. Pecharsky,et al. Advanced magnetocaloric materials: What does the future hold? , 2006 .

[5] W. Szmaja. Separation of magnetic from non-magnetic information in the Bitter pattern method , 2001 .

[6] W. Giauque. A THERMODYNAMIC TREATMENT OF CERTAIN MAGNETIC EFFECTS. A PROPOSED METHOD OF PRODUCING TEMPERATURES CONSIDERABLY BELOW 1° ABSOLUTE , 1927 .

[7] M. Vázquez,et al. Magnetic properties of field annealed Ni-rich microwires , 2007 .

[8] J. M. Blanco,et al. Microwires coated by glass: A new family of soft and hard magnetic materials , 2000 .

[9] P. Debye. Einige Bemerkungen zur Magnetisierung bei tiefer Temperatur , 1926 .

[10] Karl A. Gschneidner,et al. Magnetocaloric effect and magnetic refrigeration , 1999 .