The influence of operational parameters on the performance of an undivided zinc–cerium flow battery

An undivided zinc–cerium redox flow battery was studied under a wide range of operational conditions, including: (i) electrolyte composition; the concentrations of ([Zn2+], [Ce3+] and [H+]), (ii) current density (0–80 mA cm−2), (iii) electrolyte flow linear velocity (0.64–7.0 cm s−1) and (iv) temperature (20–60 °C). The charge efficiency increased at higher current densities and at higher electrolyte flow velocities. Unlike the divided zinc–cerium system, the charge–discharge performance decreased at higher temperature, since oxygen evolution became increasingly favored at the positive electrode. The use of a low acid concentration led to a poor conversion of Ce(III) to Ce(IV) ions during the discharge cycle. Mixed electrolytes containing methanesulfonate and sulfate anions have been evaluated at a high Ce(III) ion concentration, e.g. 0.4 mol dm−3. After charging the battery for 4 h, the conversion of Ce(III) to Ce(IV) ions became less efficient over time due to a greater fraction of the current being used in oxygen evolution. Critical aspects for improvements in the battery performance are considered.

[1]  Frank C. Walsh,et al.  Zinc deposition and dissolution in methanesulfonic acid onto a carbon composite electrode as the negative electrode reactions in a hybrid redox flow battery , 2011 .

[2]  Yanzhi Sun,et al.  Study on a new single flow acid Cu–PbO2 battery , 2008 .

[3]  Gaoping Cao,et al.  Study on a single flow acid Cd–chloranil battery , 2009 .

[4]  Maria Skyllas-Kazacos,et al.  Novel vanadium chloride/polyhalide redox flow battery , 2003 .

[5]  D. Hall,et al.  Evaluation of carbon composite materials for the negative electrode in the zinc–cerium redox flow cell☆ , 2012 .

[6]  Yusheng Yang,et al.  Preliminary study on zinc–air battery using zinc regeneration electrolysis with propanol oxidation as a counter electrode reaction , 2009 .

[7]  Maria Skyllas-Kazacos,et al.  Characteristics and performance of 1 kW UNSW vanadium redox battery , 1991 .

[8]  Stephen E. Creager,et al.  Redox potentials and kinetics of the Ce3+/Ce4+ redox reaction and solubility of cerium sulfates in sulfuric acid solutions , 2002 .

[9]  Derek Pletcher,et al.  A novel flow battery: A lead acid battery based on an electrolyte with soluble lead(II). Part II. Flow cell studies , 2004 .

[10]  R. Spotnitz,et al.  Mediated electrochemical synthesis of aromatic aldehydes, ketones, and quinones using ceric methanesulfonate , 1989 .

[11]  Maria Skyllas-Kazacos,et al.  Electrochemical behaviour of vanadium(V)/vanadium(IV) redox couple at graphite electrodes , 1992 .

[12]  C. Ponce de León,et al.  Redox flow cells for energy conversion , 2006 .

[13]  R. C. Knechtli,et al.  Zinc‐Bromine Secondary Battery , 1977 .

[14]  Li Zhang,et al.  Preliminary study of single flow zinc-nickel battery , 2007 .

[15]  C. Low,et al.  Ce(III)/Ce(IV) in methanesulfonic acid as the positive half cell of a redox flow battery , 2011 .

[16]  Maria Skyllas-Kazacos,et al.  Efficient Vanadium Redox Flow Cell , 1987 .

[17]  Allen J. Bard,et al.  Electrochemical Methods: Fundamentals and Applications , 1980 .

[18]  Debi Zhou,et al.  Study of the Ce3+/Ce4+ Redox Couple in Mixed-Acid Media (CH3SO3H and H2SO4) for Redox Flow Battery Application , 2011 .

[19]  Frank C. Walsh,et al.  A dynamic performance model for redox-flow batteries involving soluble species , 2008 .

[20]  F. Walsh,et al.  Electrochemical technology for environmental treatment and clean energy conversion , 2001 .

[21]  Frank C. Walsh,et al.  Characterization of a zinc–cerium flow battery , 2011 .

[22]  C. Ponce de León,et al.  An undivided zinc–cerium redox flow battery operating at room temperature (295 K) , 2011 .

[23]  Susumu Okazaki,et al.  Performance testing of 10 kW-class advanced batteries for electric energy storage systems in Japan , 1988 .