论文信息 - High temperature corrosion and microstructure deterioration of KHR35H radiant tubes in continuous annealing furnace - 字舞流文

High temperature corrosion and microstructure deterioration of KHR35H radiant tubes in continuous annealing furnace

Zhichao Zhu | Cong-qian Cheng | Jie Zhao | Lu Wang

[1] Jie Zhao,et al. A New Approach of Reliability Design for Creep Rupture Property , 2010 .

[2] Antonio Rinaldi,et al. Damage characterization in two reformer heater tubes after nearly 10 years of service at different operative and maintenance conditions , 2010 .

[3] J. Furtado,et al. Microstructure evolution of HP40-Nb alloys during aging under air at 1000 °C , 2009 .

[4] H. M. Tawancy,et al. Failure analysis of furnace radiant tubes exposed to excessive temperature , 2006 .

[5] L. H. Almeida,et al. Microstructural characterization of modified 25Cr–35Ni centrifugally cast steel furnace tubes , 2002 .

[6] D. Young,et al. Microstructure of HK40 alloy after high temperature service in oxidizing/carburizing environment: I. Oxidation phenomena and propagation of a crack , 2002 .

[7] D. Young,et al. Alloy phase transformations driven by high temperature corrosion processes , 2002 .

[8] G. Arnau,et al. High-Temperature Oxidation Studies of Low-Nickel Austenitic Stainless Steel. Part I: Isothermal Oxidation , 2001 .