Ultrasonic Detection of Delamination and Material Characterization of Thermal Barrier Coatings

This article describes ultrasonic nondestructive evaluation (NDE) to detect the changes of material properties and provide early warning of delamination in thermal barrier coating (TBC) systems. NDE tests were performed on single-crystal René N5 superalloy coupons that were coated with a commercially available MCrAlY bond coat and an air plasma sprayed 7% yttria-stabilized zirconia (YSZ) top coat deposited by Air Plasma Spray method, as well as Haynes 230 superalloy coupons coated with MCrA1Y bond coat, and an electron beam physical vapor deposit of 7% YSZ top coat. The TBC coupons were subjected to either cyclic or isothermal exposure for various lengths of time at temperatures ranging from 900 to 1100 °C. The ultrasonic measurements performed on the coupons had provided an early warning of delamination along the top coat/TGO interface before exposure time, when delamination occurred. The material's property (Young’s modulus) of the top coat was estimated using the measured wave speeds. Finite element analysis (FEA) of the ultrasonic wave propagation was conducted on a simplified TBC system to verify experimental observations. The technique developed was also demonstrated on an as-manufactured turbine blade to estimate normalized top coat thickness measurements.

[1]  Dongming Zhu,et al.  Thermal conductivity and elastic modulus evolution of thermal barrier coatings under high heat flux conditions , 2000 .

[2]  Characterisation of air plasma sprayed TBC coating during isothermal oxidation at 1100°C , 2007 .

[3]  F. Lakestani,et al.  Ultrasonic characterisation of thermal barrier coatings , 1996, 1996 IEEE Ultrasonics Symposium. Proceedings.

[4]  Miss A.O. Penney.  (b) , 1974, The New Yale Book of Quotations.

[5]  Anette M. Karlsson,et al.  Evolution of surface morphology in thermomechanically cycled NiCoCrAlY- bond coats , 2006 .

[6]  William A. Ellingson,et al.  Optical NDT techniques for ceramic thermal barrier coatings : NDT of ceramics: an introduction to the technical focus issue , 2006 .

[7]  C. Starr,et al.  The Electric Power Research Institute , 1983, Science.

[8]  T. Hashida,et al.  Determination of Interface Fracture Toughness in Thermal Barrier Coating System by Blister Tests , 2003 .

[9]  Characterisation of air plasma sprayed TBC coating during isothermal oxidation at 1100 degrees centigrade , 2007 .

[10]  M. A. Alvin,et al.  Materials and Component Development for Advanced Turbine Systems , 2008 .

[11]  Sintering of the Top Coat in Thermal Spray TBC Systems Under Service Conditions , 2000 .

[12]  Wei-Jer Wang,et al.  Wave propagation in an inhomogeneous transversely isotropic material obeying the generalized power law model , 2012 .

[13]  D. Thompson,et al.  Review of Progress in Quantitative Nondestructive Evaluation , 1982 .

[14]  Amol D. Jadhav,et al.  Low-thermal-conductivity plasma-sprayed thermal barrier coatings with engineered microstructures , 2006 .

[15]  A. Fahr,et al.  Detection of thermally grown oxides in thermal barrier coatings by nondestructive evaluation , 2006 .

[16]  Mfj Martijn Koolloos,et al.  Effect of local thermal shock load on plasma sprayed thermal barrier coatings , 1998 .

[17]  Nondestructive Determination of Thickness and Elastic Modulus of Plasma Spray Coatings Using Laser Ultrasonics , 1999 .

[18]  Vimal Desai,et al.  Evaluation of thickness, porosity and pore shape of plasma sprayed TBC by electrochemical impedance spectroscopy , 2005 .

[19]  A. Fahr,et al.  Nondestructive measurement of porosity in thermal barrier coatings , 2003 .

[20]  R. Vaßen,et al.  Residual stresses and elastic modulus of thermal barrier coatings graded in porosity , 2004 .

[21]  D. Stöver,et al.  Failure of physical vapor deposition/plasma-sprayed thermal barrier coatings during thermal cycling , 2000 .