Porous Silicon Nitride Ceramics Prepared by Reduction–Nitridation of Silica

A new method for preparing porous silicon nitride ceramics with high porosity had been developed by carbothermal reduction of die-pressed green bodies composed of silicon dioxide, carbon, sintering additives, and seeds. The resultant porous silicon nitride ceramics showed fine microstructure and uniform pore structure. The influence of SiO2 particle size and sintering process (sintering temperature and retaining time) on the microstructure of sintering bodies was analyzed. X-ray diffractometry demonstrated the formation of single-phase β-Si3N4 via the reaction between silicon dioxide and carbon at high temperature. SEM analysis showed that pores were formed by the banding up of rod-like β-Si3N4 grains. Porous Si3N4 ceramics with a porosity of 70–75%, and a strength of 5–8 MPa, were obtained.

[1]  G. Schneider,et al.  Synthesis of fibrous β-Si3N4 structured porous ceramics using carbothermal nitridation of silica , 2005 .

[2]  C. Kawai,et al.  Effect of Porosity and Microstructure on the Strength of Si3N4: Designed Microstructure for High Strength, High Thermal Shock Resistance, and Facile Machining , 2005 .

[3]  S. Kanzaki,et al.  Strain Tolerant Porous Silicon Nitride , 2005 .

[4]  J. Rödel,et al.  Evolution of Mechanical Properties of Porous Alumina during Free Sintering and Hot Pressing , 2004 .

[5]  K. Niihara,et al.  Influence of Yttria–Alumina Content on Sintering Behavior and Microstructure of Silicon Nitride Ceramics , 2004 .

[6]  T. Ohji,et al.  Fabrication and characterisation of porous silicon nitride ceramics using Yb2O3 as sintering additive , 2003 .

[7]  S. Kanzaki,et al.  Synthesis of Porous Silicon Nitride with Unidirectionally Aligned Channels Using Freeze‐Drying Process , 2002 .

[8]  Guo‐Jun Zhang,et al.  Porosity and microstructure control of porous ceramics by partial hot pressing , 2001 .

[9]  N. Shinohara,et al.  Fabrication of Porous Alumina Ceramics with Uni-Directionally-Arranged Continuous Pores Using a Magnetic Field , 1999 .

[10]  K. Chou,et al.  Studies on the Control of Porous Properties in the Fabrication of Porous Support , 1995 .

[11]  Y. Akimune,et al.  Effect of Grain Growth of β‐Silicon Nitride on Strength, Weibull Modulus, and Fracture Toughness , 1993 .

[12]  C. C. Wu,et al.  Fracture energy of Si3N4 , 1985 .

[13]  Robert L. Coble,et al.  Effect of Porosity on Physical Properties of Sintered Alumina , 1956 .

[14]  S. Hampshire,et al.  Characterisation of porous silicon nitride materials produced with starch , 2004 .

[15]  Bao-lin Zhang,et al.  Combustion synthesis of network silicon nitride porous ceramics , 2003 .

[16]  A. Boccaccini,et al.  Theoretical and experimental considerations on the thermal shock resistance of sintered glasses and ceramics using modelled microstructure-property correlations , 1996 .