Paraffin/diatomite/multi-wall carbon nanotubes composite phase change material tailor-made for thermal energy storage cement-based composites

In this study, a paraffin/diatomite/MWCNTs (multi-wall carbon nanotubes) composite PCM (phase change material) was tailor-made for further applications in producing thermal energy storage cement-based composites. For the purpose of selecting an optimum diatomite as the supporting matrix for the new composite PCM, the pozzolanic reactivity and paraffin absorption capacity of various diatomite materials were evaluated. It was shown that the diatomite material calcined at 600°C for 2h has the best pozzolanic reactivity and comparable paraffin absorption capacity compared to other diatomite candidates. It, therefore, was used as the supporting matrix of the new paraffin/diatomite/MWCNTs composite PCM. The thermal properties of this fabricated composite PCM were determined by the DSC (differential scanning calorimetry) method. It was revealed that the composite PCM has a melting temperature of 27.12°C and latent heat of 89.40J/g. In addition, experimental results from FTIR (Fourier transform infrared) and TGA (thermogravimetric analysis) on this composite PCM showed that it has good chemical compatibility and thermal stability. Moreover, compared to paraffin/diatomite composite PCM, the use of MWCNTs was found to have clear beneficial effects for improving the thermal conductivity and heat storage/release rates, without affecting the thermal properties, chemical compatibility and thermal stability.

[1]  S. M. Sadrameli,et al.  A review of microencapsulation methods of phase change materials (PCMs) as a thermal energy storage (TES) medium , 2014 .

[2]  Dan Zhou,et al.  Review on thermal energy storage with phase change materials (PCMs) in building applications , 2012 .

[3]  Fredrik Setterwall,et al.  Phase transition temperature ranges and storage density of paraffin wax phase change materials , 2004 .

[4]  H. Brouwers,et al.  The behavior of self-compacting concrete containing micro-encapsulated Phase Change Materials , 2009 .

[5]  Yu Li,et al.  Improvement on pozzolanic reactivity of coal gangue by integrated thermal and chemical activation , 2013 .

[6]  S. C. Solanki,et al.  Heat transfer characteristics of thermal energy storage system using PCM capsules: A review , 2008 .

[7]  Bülent Yılmaz,et al.  The use of raw and calcined diatomite in cement production , 2008 .

[8]  Chang Liu,et al.  Advanced Materials for Energy Storage , 2010, Advanced materials.

[9]  A. Sari,et al.  Polyethylene glycol (PEG)/diatomite composite as a novel form-stable phase change material for thermal energy storage , 2011 .

[10]  Zhishen Wu,et al.  Study on preparation and thermal properties of binary fatty acid/diatomite shape-stabilized phase change materials , 2011 .

[11]  Zongjin Li,et al.  Paraffin/diatomite composite phase change material incorporated cement-based composite for thermal energy storage , 2013 .

[12]  Zhong Xin,et al.  Thermal properties of paraffin based composites containing multi-walled carbon nanotubes , 2009 .

[13]  Shazim Ali Memon,et al.  Phase change materials integrated in building walls: A state of the art review , 2014 .

[14]  G. Kakali,et al.  Properties and hydration of blended cements with calcareous diatomite , 2006 .

[15]  Jisoo Jeon,et al.  Optimal preparation of PCM/diatomite composites for enhancing thermal properties , 2013 .

[16]  Liwu Fan,et al.  Thermal conductivity enhancement of phase change materials for thermal energy storage: A review , 2011 .

[17]  R. Frost,et al.  Preparation and thermal energy storage properties of paraffin/calcined diatomite composites as form-stable phase change materials , 2013 .

[18]  T. Teng,et al.  Performance assessment of heat storage by phase change materials containing MWCNTs and graphite , 2013 .

[19]  Alejandra Tironi,et al.  Assessment of pozzolanic activity of different calcined clays , 2013 .

[20]  C. Poon,et al.  Use of phase change materials for thermal energy storage in concrete: An overview , 2013 .

[21]  Haifeng Shi,et al.  Composite macrocapsule of phase change materials/expanded graphite for thermal energy storage , 2013 .

[22]  M. Barsoum,et al.  Pozzolanic Activity of Diatomaceous Earth , 2010 .

[23]  Jay M. Khodadadi,et al.  Thermal conductivity enhancement of paraffins by increasing the alignment of molecules through adding CNT/graphene , 2013 .

[24]  Zhishen Wu,et al.  Properties of form-stable paraffin/silicon dioxide/expanded graphite phase change composites prepared by sol–gel method , 2012 .

[25]  Xiaohua Zhao,et al.  Mechanical behavior and microstructure of cement composites incorporating surface-treated multi-walled carbon nanotubes , 2005 .

[26]  C. Doetsch,et al.  Evaluation of paraffin/water emulsion as a phase change slurry for cooling applications , 2009 .

[27]  Shan Hu,et al.  The experimental exploration of carbon nanofiber and carbon nanotube additives on thermal behavior of phase change materials , 2011 .

[28]  Jisoo Jeon,et al.  Evaluation of PCM/diatomite composites using exfoliated graphite nanoplatelets (xGnP) to improve thermal properties , 2013, Journal of Thermal Analysis and Calorimetry.

[29]  Qijun Yu,et al.  The reaction between rice husk ash and Ca(OH)2 solution and the nature of its product , 1999 .

[30]  Zhishen Wu,et al.  Study on preparation and thermal property of binary fatty acid and the binary fatty acids/diatomite composite phase change materials , 2011 .

[31]  Zhengguo Zhang,et al.  Thermal energy storage cement mortar containing n-octadecane/expanded graphite composite phase change material , 2013 .

[32]  Ahmet Sarı,et al.  Thermal energy storage properties and thermal reliability of some fatty acid esters/building material composites as novel form-stable PCMs , 2012 .