Thermoplastic Composite Cylinders for Underwater Applications

A study of thermoplastic matrix composites has been performed to investigate their use in underwater applications such as oceanography, submarine, and sub-sea offshore structures. This article first presents six candidate materials. Results from simple mechanical and seawater aging screening tests on flat specimens are then described. Glass/epoxy and carbon/epoxy composites are used as reference materials. Two materials emerged from this process, glass/PEI and carbon/PEEK. Cylinders of both were manufactured and subjected to hydrostatic pressure tests, and results are compared to those for glass/epoxy and carbon/epoxy cylinders of similar geometry. The carbon/PEEK material appeared most promising. It resisted pressures in excess of 90 MPa and was retained for damage tolerance assessment studies. Drop weight impact damage zones were smaller in carbon/PEEK than carbon/epoxy for the same impact energies but the loss in residual collapse strength was more rapid in the thermoplastic composite. This was attributed to a change in failure mode, impact damage initiated a local buckling failure.

[1]  W. Cantwell,et al.  Fracture of glass/polypropylene laminates: influence of cooling rate after moulding , 1994 .

[2]  Y Lemiere.  The evolution of composite materials in submarine structures. , 1992 .

[3]  F. Cogswell.  Thermoplastic aromatic polymer composites : a study of the structure, processing, and properties of carbon fibre reinforced polyetheretherketone and related materials , 1996 .

[4]  Mark A. Lamontia,et al.  Manufacturing flat and cylindrical laminates and built up structure using automated thermoplastic tape laying, fiber placement, and filament winding , 2003 .

[5]  J. Gillespie,et al.  The Effects and Non-Destructive Evaluation of Defects in Thermoplastic Compression-Loaded Composite Cylinders , 1995 .

[6]  P. Soden,et al.  Chapter 2.2 – Biaxial test results for strength and deformation of a range of E-glass and carbon fibre reinforced composite laminates: Failure exercise benchmark data , 2004 .

[7]  J. Gillespie,et al.  Buckling and Growth of Delamination in Thermoset and Thermoplastic Composites , 1991 .

[8]  Takashi Ishikawa,et al.  Some experimental findings in compression-after-impact (CAI) tests of CF/PEEK (APC-2) and conventional CF/epoxy flat plates , 1995 .

[9]  T. Juska.  Effect of Water Immersion on Fiber/Matrix Adhesion in Thermoplastic Composites , 1993 .

[10]  Ali Yousefpour,et al.  Effects of Geometric Optimization of Plug-Supported End-Caps on the Performance of Thick Thermoplastic Composite Pressure Vessels Under External Hydrostatic Pressure , 2002 .

[11]  J. Gillespie,et al.  Performance of a Filament Wound Graphite/Thermoplastic Composite Ring-Stiffened Pressure Hull Model , 1995 .

[12]  Peter Davies,et al.  Beam analysis of angle-ply laminate end-notched flexure specimens , 1998 .

[13]  B. Z. Jang,et al.  Advanced thermoplastic composites , 1992 .

[14]  L. Carlsson,et al.  Marine Environmental Effects on Polymer Matrix Composites , 1995 .

[15]  D. R. Moore,et al.  Toughness of aromatic polymer composites reinforced with carbon fibres , 1985 .

[16]  P. Stevenson,et al.  The Mechanical Design and Implementation of an Autonomous Submersible , 1998 .

[17]  R. J. Lee.  Compression strength of aligned carbon fibre-reinforced thermoplastic laminates , 1987 .

[18]  Richard Sharp,et al.  Material Selection/Fabrication Issues for Thermoplastic Fiber Placement , 1995 .

[19]  Y. Jack Weitsman,et al.  Effects of Fluids on Polymeric Composites—A Review , 2000 .

[20]  Adrian P. Mouritz,et al.  Review of advanced composite structures for naval ships and submarines , 2001 .

[21]  Leif A. Carlsson,et al.  Thermoplastic composite materials , 1991 .