Double-sided brush-shaped TiO2 nanostructure assemblies with highly ordered nanowires for dye-sensitized solar cells.

We describe a seeded hydrothermal process for the growth of unique double-sided brush-shaped (DSBS) TiO2 nanostructure assemblies consisting of highly ordered rutile nanowires vertically aligned around an annealed TiO2 nanoparticle layer. The annealed TiO2 nanoparticle layer seeds the nanowire growth and also supports the DSBS structure. The morphology of the DSBS TiO2 nanostructure depends on the hydrothermal reaction time. The diameter of the nanowires is about 6.6 nm, and with increasing reaction time from 1 to 8 h the nanowire length increases from 0.6 to 6.2 μm, whereas the thickness of the nanoparticle layer decreases from 4.3 to 2.8 μm. These free-standing nanowire arrays provide large internal surface area, which is essential for minimizing carrier recombination in high performance photovoltaic devices. Furthermore, the nanowire architecture can help increase the rate of charge transport as compared to particulate films because of lower concentration of grain boundaries. The power conversion efficiency of backside (DSBS TiO2/FTO photoanode) illuminated dye-sensitized solar cells fabricated using the DSBS TiO2 nanostructure assembly is found to be depended on the nanowire length. A cell fabricated using 15.2 μm thick nanostructures sensitized by N719 has a short-circuit current density of 12.18 mA cm(-2), 0.78 V open circuit potential, and a 0.59 filling factor, yielding a maximum power conversion efficiency of 5.61% under AM 1.5 illumination.

[1]  Henry J. Snaith,et al.  Efficient planar heterojunction perovskite solar cells by vapour deposition , 2013, Nature.

[2]  S. Dou,et al.  Morphology-controllable 1D-3D nanostructured TiO2 bilayer photoanodes for dye-sensitized solar cells. , 2013, Chemical communications.

[3]  J. Gutmann,et al.  Fabrication and characterization of nanostructured titania films with integrated function from inorganic-organic hybrid materials. , 2012, Chemical Society reviews.

[4]  X. Lou,et al.  Direct Synthesis of Anatase TiO2 Nanowires with Enhanced Photocatalytic Activity , 2012, Advanced materials.

[5]  Q. Qiao,et al.  One dimensional nanostructure/nanoparticle composites as photoanodes for dye-sensitized solar cells. , 2012, Nanoscale.

[6]  A. J. Frank,et al.  Rapid charge transport in dye-sensitized solar cells made from vertically aligned single-crystal rutile TiO(2) nanowires. , 2012, Angewandte Chemie.

[7]  Successful demonstration of an efficient I(-)/(SeCN)2 redox mediator for dye-sensitized solar cells. , 2012, Physical chemistry chemical physics : PCCP.

[8]  Michael Grätzel,et al.  Porphyrin-Sensitized Solar Cells with Cobalt (II/III)–Based Redox Electrolyte Exceed 12 Percent Efficiency , 2011, Science.

[9]  S. Ramakrishna,et al.  A first report on the fabrication of vertically aligned anatase TiO2 nanowires by electrospinning: Preferred architecture for nanostructured solar cells , 2011 .

[10]  Changjian Lin,et al.  High efficiency dye-sensitized solar cells based on hierarchically structured nanotubes. , 2011, Nano letters.

[11]  L. Fang,et al.  TiO2 nanorod arrays grown from a mixed acid medium for efficient dye-sensitized solar cells , 2011 .

[12]  Jiehua Liu,et al.  Fabrication of O (dye)-terminated anatase TiO2 nanosheets for dye sensitized solar cells , 2011 .

[13]  Chunzhong Li,et al.  Planar scattering from hierarchical anatase TiO2 nanoplates with variable shells to improve light harvesting in dye-sensitized solar cells. , 2011, Chemical communications.

[14]  Liejin Guo,et al.  Nanostructured WO₃/BiVO₄ heterojunction films for efficient photoelectrochemical water splitting. , 2011, Nano letters.

[15]  Ulrich Wiesner,et al.  Block copolymer based composition and morphology control in nanostructured hybrid materials for energy conversion and storage: solar cells, batteries, and fuel cells. , 2011, Chemical Society reviews.

[16]  R. Friend,et al.  Dye-sensitized solar cell based on a three-dimensional photonic crystal. , 2010, Nano letters.

[17]  Anuj R. Madaria,et al.  Growth of Aligned Single-Crystalline Rutile TiO2 Nanowires on Arbitrary Substrates and Their Application in Dye-Sensitized Solar Cells , 2010 .

[18]  Guozhong Cao,et al.  ZnO Nanostructures for Dye‐Sensitized Solar Cells , 2009 .

[19]  Michael Grätzel,et al.  Recent advances in sensitized mesoscopic solar cells. , 2009, Accounts of chemical research.

[20]  Bin Liu,et al.  Growth of oriented single-crystalline rutile TiO(2) nanorods on transparent conducting substrates for dye-sensitized solar cells. , 2009, Journal of the American Chemical Society.

[21]  Seeram Ramakrishna,et al.  Metal Oxides for Dye-Sensitized Solar Cells , 2009 .

[22]  M. Grätzel,et al.  The influence of charge transport and recombination on the performance of dye-sensitized solar cells. , 2009, Chemphyschem : a European journal of chemical physics and physical chemistry.

[23]  P. Sipos,et al.  Low temperature synthesis, characterization and substrate-dependent photocatalytic activity of nanocrystalline TiO2 with tailor-made rutile to anatase ratio , 2008 .

[24]  Liming Shen,et al.  Hydrothermal Splitting of Titanate Fibers to Single-Crystalline TiO2 Nanostructures with Controllable Crystalline Phase, Morphology, Microstructure, and Photocatalytic Activity , 2008 .

[25]  Henry J. Snaith,et al.  Advances in Liquid‐Electrolyte and Solid‐State Dye‐Sensitized Solar Cells , 2007 .

[26]  Lianxi Zheng,et al.  Carbon‐Nanotube Cotton for Large‐Scale Fibers , 2007 .

[27]  C. B. Carter,et al.  Photosensitization of ZnO nanowires with CdSe quantum dots for photovoltaic devices. , 2007, Nano letters.

[28]  Kouji Yasuda,et al.  TiO2 nanotubes: Self-organized electrochemical formation, properties and applications , 2007 .

[29]  D. Bavykin,et al.  Protonated Titanates and TiO2 Nanostructured Materials: Synthesis, Properties, and Applications , 2006 .

[30]  Craig A. Grimes,et al.  A review on highly ordered, vertically oriented TiO2 nanotube arrays: Fabrication, material properties, and solar energy applications , 2006 .

[31]  H. Imai,et al.  {1 1 1}-faceting of low-temperature processed rutile TiO2 rods , 2006 .

[32]  H. Smit,et al.  Influence of scattering layers on efficiency of dye-sensitized solar cells , 2006 .

[33]  Hidetoshi Miura,et al.  High‐Efficiency Organic‐Dye‐ Sensitized Solar Cells Controlled by Nanocrystalline‐TiO2 Electrode Thickness , 2006 .

[34]  Craig A Grimes,et al.  Use of highly-ordered TiO(2) nanotube arrays in dye-sensitized solar cells. , 2006, Nano letters.

[35]  Peidong Yang,et al.  Nanowire dye-sensitized solar cells , 2005, Nature materials.

[36]  A. J. Frank,et al.  Electrons in nanostructured TiO2 solar cells: Transport, recombination and photovoltaic properties , 2004 .

[37]  H. Imai,et al.  Growth of submicrometer-scale rectangular parallelepiped rutile TiO2 films in aqueous TiCl3 solutions under hydrothermal conditions. , 2004, Journal of the American Chemical Society.

[38]  Shi Erwei,et al.  Influence of solution concentration on the hydrothermal preparation of titania crystallites , 2001 .

[39]  T. Kitamura,et al.  Hydrothermal synthesis of nanosized anatase and rutile TiO2 using amorphous phase TiO2 , 2001 .

[40]  Jean-Pierre Jolivet,et al.  Synthesis of brookite TiO2 nanoparticlesby thermolysis of TiCl4 in strongly acidic aqueous media , 2001 .

[41]  M. Grätzel,et al.  A low-cost, high-efficiency solar cell based on dye-sensitized colloidal TiO2 films , 1991, Nature.

[42]  Fujio Izumi,et al.  Raman spectrum of anatase, TiO2 , 1978 .

[43]  G. Aubrecht,et al.  Neutrino charge radius in a model of weak and electromagnetic interactions , 1974 .

[44]  R. Katiyar,et al.  Coupled modes with A1 symmetry in tetragonal BaTiO3 , 1974 .