H2 production by methane decomposition: Catalytic and technological aspects

Abstract Ni and Co supported on SiO 2 and Al 2 O 3 silica cloth thin layer catalysts have been investigated in the catalytic decomposition of natural gas (CDNG) reaction. The influence of carrier nature and reaction temperature was evaluated with the aim to individuate the key factors affecting coke formation. Both Ni and Co silica supported catalysts, due to the low metal support interaction (MSI), promote s the formation of carbon filament with particles at tip. On the contrary, in case alumina was used as support, metals strongly interact with surface thus depressing both the metal sintering and the detachment of particles from catalyst surface. In such cases, carbon grows on metal particle with a “base mechanism” while particles remain well anchored on the catalyst surface. This allowed to realize a cyclic dual-step process based on methane decomposition and catalyst oxygen regeneration without deactivation of catalyst. Technological considerations have led to conclude that the implement of a process based on decomposition and regeneration of catalyst by oxidation requires the development of a robust catalytic system characterized by both a strong MSI and a well defined particle size distribution. In particular, the catalyst should be able to operate at high temperature, necessary to reach high methane conversion values (> 90%), avoiding at the same time the formation of both the carbon filaments with metal at tip or the encapsulating carbon which drastically deactivate the catalyst.

[1]  F. Frusteri,et al.  Doped Ni Thin Layer Catalysts for Catalytic Decomposition of Natural Gas to produce hydrogen , 2009 .

[2]  R. Chirone,et al.  Some issues in modelling methane catalytic decomposition in fluidized bed reactors , 2008 .

[3]  G. Froment,et al.  Filamentous carbon formation and gasification: Thermodynamics, driving force, nucleation, and steady-state growth , 1997 .

[4]  F. Frusteri,et al.  Methane decomposition over Co thin layer supported catalysts to produce hydrogen for fuel cell , 2010 .

[5]  F. Frusteri,et al.  Catalytic decomposition of natural gas for COx-free hydrogen production in a structured multilayer reactor , 2009 .

[6]  S. Banerjee,et al.  Continuous Production of H2 at Low Temperature from Methane Decomposition over Ni-Containing Catalyst Followed by Gasification by Steam of the Carbon on the Catalyst in Two Parallel Reactors Operated in Cyclic Manner , 2001 .

[7]  Andreas Züttel,et al.  Hydrogen as a future energy carrier , 2008 .

[8]  Gilbert F. Froment,et al.  Kinetic Study of the Carbon Filament Formation by Methane Cracking on a Nickel Catalyst , 1997 .

[9]  V. Likholobov,et al.  Iron-containing catalysts of methane decomposition: accumulation of filamentous carbon , 2002 .

[10]  S. Takenaka,et al.  Hydrogen–Deuterium Exchange Studies on the Decomposition of Methane over Ni/SiO2 , 2001 .

[11]  V. V. Chesnokov,et al.  Production of hydrogen by methane catalytic decomposition over Ni-Cu-Fe/Al2O3 catalyst , 2009 .

[12]  E. Tanabe,et al.  Formation of Carbon Nanofibers and Carbon Nanotubes through Methane Decomposition over Supported Cobalt Catalysts , 2004 .

[13]  A. Monzón,et al.  Kinetics of carbon nanotubes growth on a Ni–Mg–Al catalyst by CCVD of methane: Influence of catalyst deactivation , 2010 .

[14]  Yongdan Li,et al.  Methane decomposition to COx-free hydrogen and nano-carbon material on group 8–10 base metal catalysts: A review , 2011 .

[15]  E. Tanabe,et al.  Formation of highly concentrated hydrogen through methane decomposition over Pd-based alloy catalysts , 2006 .

[16]  J. Pinilla,et al.  Influence of nickel crystal domain size on the behaviour of Ni and NiCu catalysts for the methane decomposition reaction , 2009 .

[17]  A. Rashidi,et al.  Kinetics of methane decomposition to COx-free hydrogen and carbon nanofiber over Ni–Cu/MgO catalyst , 2010 .