The electrochemical reduction of VO2+ in acidic solution at high overpotentials

Abstract An investigation has been carried out to attempt to understand the unusually low apparent symmetry factor observed during the reduction of V(5) at higher overpotentials at carbon electrodes (typically 460 mV decade −1 ). This reaction is of interest because it occurs in vanadium redox-flow batteries (VRBs) during discharge. Polarisation curves were measured using a rotating disk electrode (RDE). The reaction was not solution mass transport controlled, was pH independent (ca from 0 to 1), and the observed Tafel slope was unaffected by V(5) concentration over a range from 0.031 to 280 mM. Electrode double layer capacitance measurements were also carried out in sulphuric acid with and without vanadium. These tests showed that the presence of V(5) caused a suppression of the normal carbon surface quinone pseudocapacitance, as well as the appearance of two new pseudocapacitance peaks, one around 0.175–0.2 V and the other around 0.675–0.725 V versus SCE. The observed results do not appear consistent with a precipitated film causing diffusion limitations or causing IR drop. A model is developed to try to explain the data, which involves electron transfer through an adsorbed layer of vanadium.

[1]  M. Pourbaix.  Atlas of Electrochemical Equilibria in Aqueous Solutions , 1974 .

[2]  J. Ulstrup,et al.  A theory of electrode reactions through bridge transition states; bridges with a discrete electronic spectrum , 1972 .

[3]  Yasushi Katayama,et al.  Investigation on V(IV)/V(V) species in a vanadium redox flow battery , 2004 .

[4]  P. Sherwood,et al.  X-ray photoelectron-spectroscopic studies of carbon-fibre surfaces. Part 5.—The effect of pH on surface oxidation , 1985 .

[5]  E. Gileadi,et al.  New techniques for double-layer capacitance measurements at solid metal electrodes , 1971 .

[6]  Maria Skyllas-Kazacos,et al.  Novel vanadium chloride/polyhalide redox flow battery , 2003 .

[7]  R. McCreery,et al.  Electron Transfer Kinetics at Modified Carbon Electrode Surfaces: The Role of Specific Surface Sites , 1995 .

[8]  W. M. Haynes.  CRC Handbook of Chemistry and Physics , 1990 .

[9]  R. Pardo,et al.  Electrochemical behaviour of vanadium compounds at a carbon paste electrode , 1997 .

[10]  F. Albert Cotton,et al.  Advanced Inorganic Chemistry , 1999 .

[11]  M. McDermott,et al.  Preparation of reproducible glassy carbon electrodes by removal of polishing impurities , 2003 .

[12]  L. H. Thaller,et al.  Electrically rechargeable REDOX flow cell , 1976 .

[13]  L. Meites,et al.  The reduction and oxidation of vanadium in acidic aqueous sulfate solutions at mercury electrodes , 1964 .

[14]  M. Skyllas-Kazacos,et al.  Raman spectroscopy studies of concentrated vanadium redox battery positive electrolytes , 2001 .

[15]  Maria Skyllas-Kazacos,et al.  Investigation of the V(V)/V(IV) system for use in the positive half-cell of a redox battery , 1985 .

[16]  Maria Skyllas-Kazacos,et al.  Chemical modification of graphite electrode materials for vanadium redox flow battery application—part II. Acid treatments , 1992 .

[17]  R. McCreery,et al.  Control of reactivity at carbon electrode surfaces , 1994 .

[18]  Maria Skyllas-Kazacos,et al.  Modification of graphite electrode materials for vanadium redox flow battery application—I. Thermal treatment , 1992 .

[19]  Xiaoqiao Lu.  Spectroscopic study of vanadium(V) precipitation in the vanadium redox cell electrolyte , 2001 .

[20]  C. Baes,et al.  The hydrolysis of cations , 1986 .

[21]  M. McDermott,et al.  Probing morphological and compositional variations of anodized carbon electrodes with tapping-mode scanning force microscopy. , 1999, Analytical chemistry.

[22]  David A. J. Rand,et al.  Energy storage — a key technology for global energy sustainability , 2001 .

[23]  R. McCreery,et al.  Electron Transfer Kinetics of Aquated Fe + 3 / + 2, Eu + 3 / + 2, and V + 3 / + 2 at Carbon Electrodes Inner Sphere Catalysis by Surface Oxides , 1993 .

[24]  J. Ulstrup,et al.  A theory of electrode reactions through bridge transition states bridge with a quasicontinuous energy spectrum , 1973 .

[25]  Maria Skyllas-Kazacos,et al.  Electrochemical behaviour of vanadium(V)/vanadium(IV) redox couple at graphite electrodes , 1992 .

[26]  M. Gattrell,et al.  Study of the Mechanism of the Vanadium 4+/5+ Redox Reaction in Acidic Solutions , 2004 .