Fatigue behaviour study of laser hybrid welded eccentric fillet joints – Part II : State-of-the-art of fracture mechanics and fatigue analysis of welded joints

Simplified fatigue and fracture mechanics based assessment methods are widely used by the industry to determine the structural integrity significance of postulated cracks, manufacturing flaws, serv ...

[1]  F. Hauser,et al.  Deformation and Fracture Mechanics of Engineering Materials , 1976 .

[2]  J.A.M. Ferreira,et al.  A fracture mechanics based fatigue life prediction for welded joints of square tubes , 1995 .

[3]  Mohamed El-Sayed,et al.  Fatigue analysis of spot-welded joints under variable amplitude load history , 1996 .

[4]  H. Schindler,et al.  A fracture mechanics approach to estimate the fatigue endurance of welded t‐joints including residual stress effects , 2007 .

[5]  F. Ellyin.  Fatigue Damage, Crack Growth and Life Prediction , 1996 .

[6]  Michel Raous,et al.  Creep crack initiation and creep crack growth assessments in welded structures , 2001 .

[7]  Zheng Xiulin,et al.  Fatigue tests and life prediction of 16 Mn steel butt welds without crack-like defect , 1994 .

[8]  P. C. Wang.  Fracture mechanics parameter for the fatigue resistance of laser welds , 1995 .

[9]  Sang‐Hee Cho,et al.  Fatigue strength in laser welding of the lap joint , 2004 .

[10]  Noel P. O’Dowd,et al.  A generic approach for a linear elastic fracture mechanics analysis of components containing residual stress , 2005 .

[11]  Tianwen Zhao,et al.  A study of fatigue crack growth with changing loading direction , 2007 .

[12]  E. S. Statnikov,et al.  Introductory fatigue tests on welded joints in high strength steel and aluminium improved by various methods including ultrasonic impact treatment ( UIT ) , 2000 .

[13]  Wolfgang Fricke,et al.  Fatigue analysis of welded joints: state of development , 2003 .

[14]  S. J. Maddox,et al.  An analysis of fatigue cracks in fillet welded joints , 1975 .

[15]  Chitoshi Miki,et al.  High strength and high performance steels and their use in bridge structures , 2002 .

[16]  F. M. Burdekin,et al.  Crack modeling in FE analysis of circular tubular joints , 1998 .

[17]  Y. Verreman,et al.  SHORT CRACK GROWTH AND COALESCENCE ALONG THE TOE OF A MANUAL FILLET WELD , 1991 .

[18]  Feargal Brennan,et al.  A new method for predicting stress intensity factors in cracked welded tubular joints , 2000 .

[19]  T. Björk,et al.  Finite element analysis of the effect of weld geometry and load condition on fatigue strength of lap joint , 2001 .

[20]  G. A. Webster,et al.  Fracture mechanics analysis of a crack in a residual stress field , 2000 .

[21]  V. Balasubramanian,et al.  Effect of weld size on fatigue crack growth behaviour of cruciform joints by strain energy density factor approach , 1999 .

[22]  Seçil Erim,et al.  Determination of mechanical and fracture properties of laser beam welded steel joints , 1999 .

[23]  Dieter Radaj,et al.  Design and Analysis of Fatigue Resistant Welded Structures , 1990 .

[24]  Kyong-Ho Chang,et al.  Residual stresses and fracture mechanics analysis of a crack in welds of high strength steels , 2007 .

[26]  Wing Kam Liu,et al.  Multi-scale constitutive model and computational framework for the design of ultra-high strength, high toughness steels , 2004 .

[27]  Y.-C. Hou,et al.  A fracture parameter for welded structures with residual stresses , 1998 .

[28]  Colin Gagg,et al.  Failure of components and products by ‘engineered-in’ defects: Case studies , 2005 .

[29]  Baohua Chang,et al.  Studies on the stress distribution and fatigue behavior of weld-bonded lap shear joints , 2001 .

[30]  T. Nykänen,et al.  A parametric fracture mechanics study of welded joints with toe cracks and lack of penetration , 2005 .

[31]  J. L. Otegui,et al.  Importance of toe irregularity for fatigue resistance of automatic welds , 1995 .

[32]  Pingsha Dong,et al.  A structural stress definition and numerical implementation for fatigue analysis of welded joints , 2001 .

[33]  H.-F. Henrysson.  Fatigue life predictions of spot welds using coarse FE meshes , 2000 .

[34]  T Dahle,et al.  Design fatigue strength of TIG-dressed welded joints in high-strength steels subjected to spectrum loading , 1998 .

[35]  P. J. Budden,et al.  Assessment of creep crack growth in dissimilar metal welds , 2000 .

[36]  Feargal Brennan,et al.  Predicting weld toe stress concentration factors for T and skewed T-joint plate connections , 2000 .

[37]  M. Sutton,et al.  Limited weld residual stress measurements in fatigue crack propagation: Part II. FEM-based fatigue crack propagation with complete residual stress fields , 2006 .

[38]  M. A. Wahab,et al.  Modeling the fatigue crack growth and propagation life of a joint of two elastic materials using interface elements , 2005 .

[39]  Michael A. Sutton,et al.  STRESS INTENSITY FACTORS FOR SURFACE CRACKS AT A HOLE BY A THREE‐DIMENSIONAL WEIGHT FUNCTION METHOD WITH STRESSES FROM THE FINITE ELEMENT METHOD , 1998 .

[40]  A. F. Hobbacher,et al.  Fatigue design of welded joints and components , 1996 .

[41]  C. Hou,et al.  Fatigue analysis of welded joints with the aid of real three-dimensional weld toe geometry , 2007 .

[42]  Paolo Lazzarin,et al.  From a local stress approach to fracture mechanics: a comprehensive evaluation of the fatigue strength of welded joints , 1999 .

[43]  C. Q. Lee,et al.  Effect of weld geometry on the fatigue life of non-load-carrying fillet welded cruciform joints , 2009 .

[44]  Peder Andersson,et al.  Numerical investigation of creep crack growth in cross‐weld CT specimens. Part II: influence of specimen size , 2000 .

[45]  Winfried Dahl,et al.  Determination of fracture mechanics properties of welded joints and comparison with the failure behaviour of wide plates , 1987 .

[46]  T. Teng,et al.  Effect of residual stresses on fatigue crack initiation life for butt-welded joints , 2004 .

[47]  William T. Becker,et al.  Failure analysis and prevention , 2002 .

[48]  Reidar Bjorhovde,et al.  Development and use of high performance steel , 2004 .

[49]  K. J. Kirkhope,et al.  Weld detail fatigue life improvement techniques. Part 2: application to ship structures ☆ , 1999 .

[50]  Matteo Chiesa,et al.  Fracture analysis of strength-mismatched welded wide plates by line spring elements , 2001 .

[51]  H. W. Kerr,et al.  Fatigue crack initiation from defects at weld toes in steel , 1989 .

[52]  K. J. Kirkhope,et al.  Weld detail fatigue life improvement techniques. Part 1: review , 1999 .

[53]  H. Hänninen,et al.  Nominal stress range fatigue of stainless steel fillet welds — the effect of weld size , 2000 .

[54]  Gert Pettersson.  Fatigue assessment of welded structures with non-linear boundary conditions , 2004 .

[55]  D Bowness,et al.  A finite element study of stress fields and stress intensity factors in tubular joints , 1995 .