Fabrication of 2-nm-wide silicon quantum wires through a combination of a partially-shifted resist pattern and orientation-dependent etching

This article proposes a nanofabrication technique for fabricating quantum wires with dimensions in the sub-10 nm regime. This technique consists of partially shifted resist-pattern formation and orientation-dependent Si etching that takes advantage of the difference in the crystallographic properties of the {111} planes and the other planes. When {110} Si substrates are etched using a partially shifted pattern as a mask, the etching generates a smooth {111} side plane and eventually forms a straight Si line pattern whose width is equal to the difference between the size of the shift and the originally exposed linewidth. Therefore, line patterns smaller than the beam diameter of lithographic tools can be formed. We show the effectiveness of this technique by fabricating a 2-nm-wide Si line. The electrical conductance characteristics of the Si nanoline formed by this technique are also shown.

[1]  Nano-scale fluctuations in electron beam resist pattern evaluated by atomic force microscopy , 1996 .

[2]  Kenji Kurihara,et al.  Fabrication of sub‐10‐nm silicon lines with minimum fluctuation , 1995 .

[3]  Photoluminescence from oxidized silicon nano-lines , 1996 .

[4]  Roger Fabian W. Pease,et al.  Oxidation of sub-50 nm Si columns for light emission study , 1992 .

[5]  E. Kratschmer,et al.  Nanostructure technology , 1988 .

[6]  Yasuo Takahashi,et al.  Fabrication of thickness‐controlled silicon nanowires and their characteristics , 1995 .

[7]  M. Nagase,et al.  Si nanostructures fabricated by electron beam lithography combined with image reversal process using electron cyclotron resonance plasma oxidation , 1995 .

[8]  Energy Eigenvalues and Quantized Conductance Values of Electrons in Si Quantum Wires on \mb{100\mb} Plane , 1995 .

[9]  Yasuo Takahashi,et al.  Quantized conductance of a silicon wire fabricated by separation-by-implanted-oxygen technology , 1995 .

[10]  M. Nagase,et al.  An Electron Beam Nanolithography System and its Application to Si Nanofabrication , 1995 .

[11]  A. N. Broers,et al.  Resolution limits for electron-beam lithography , 1988 .

[12]  Wei Chen,et al.  Fabrication of 5–7 nm wide etched lines in silicon using 100 keV electron‐beam lithography and polymethylmethacrylate resist , 1993 .

[13]  D. L. Kendall,et al.  A new theory for the anisotropic etching of silicon and some underdeveloped chemical micromachining concepts , 1990 .

[14]  S. Chou,et al.  10 nm Si pillars fabricated using electron‐beam lithography, reactive ion etching, and HF etching , 1993 .