Annealing effect on the structural and optical properties of Cr/α-Cr2O3 monodispersed particles based solar absorbers

Abstract A cost-effective and environmentally friendly green chemical method, the so-called aqueous chemical growth (ACG) method, was used to deposit chromium/alpha-chromium(III) oxide, Cr/α-Cr 2 O 3 , monodispersed particles, for solar absorbers applications. The deposited particles were annealed at various temperatures in a hydrogen atmosphere for 2 h to study the annealing temperature dependence of the structural, chemical and optical properties of the particles grown on tantalum substrates. The deposited Cr/α-Cr 2 O 3 was characterized by X-ray diffraction (XRD), attenuated total reflection (ATR), scanning electron microscopy (SEM), energy dispersive spectrometry (EDS), and diffuse reflectance UV–vis–NIR spectroscopy. The XRD and ATR analysis indicated that by increasing annealing temperature, the particles crystallinity was improved and Ta 2 O 5 was formed around 600 °C, due to the fast oxygen diffusion from the deposited α-Cr 2 O 3 toward the tantalum substrate. The optical measurements show that samples annealed at 400 and 500 °C exhibit the targeted high absorbing optical characteristics of “Black chrome”, while those annealed below 400 °C and above 500 °C show a significant low absorptivity and high emissivity.

[1]  M. Antonietti,et al.  Silica±carbon Nanocompositesða New Concept for the Design of Solar Absorbers** , 2022 .

[2]  P. Holloway,et al.  Oxidation and diffusion in black chrome selective solar absorber coatings , 1989 .

[3]  M. Maaza,et al.  Synthesis, characterization, and growth mechanism of α-Cr2O3 monodispersed particles , 2011 .

[4]  P. Holloway,et al.  Electrodeposition of black chrome selective solar absorber coatings with improved thermal stability , 1985 .

[5]  A. Manthiram,et al.  2-D mesoparticulate arrays of α-Cr2O3 , 2003 .

[6]  A. Schröder,et al.  Cr/SiO on Cu solar selective absorbers , 1985 .

[7]  W. Desisto,et al.  Study of chromium oxide film growth by chemical vapor deposition using infrared reflection absorption spectroscopy , 2001 .

[8]  Post-annealing effects on the structural properties and residual stress of Ta 2 O 5 thin films deposited by ion beam sputtering , 2007 .

[9]  K. Zahraman,et al.  Pulsed laser deposition of nanostructured dichromium trioxide thin films , 2006 .

[10]  Soteris A. Kalogirou,et al.  Solar thermal collectors and applications , 2004 .

[11]  F. Rheault,et al.  Spectrally selective surfaces of Co‐pigmented anodic Al2O3 , 1985 .

[12]  Optimization of an industrial DC magnetron sputtering process for graded composition solar thermal absorbing layer , 2006 .

[13]  P. Holloway,et al.  Oxidation of electrodeposited black chrome selective solar absorber films , 1980 .

[14]  N. Barradas,et al.  Graded selective coatings based on chromium and titanium oxynitride , 2003 .

[15]  P. Zavracky,et al.  Selective black absorbers using MgO/Au cermet films , 1976 .