Rapid prototyping: porous titanium alloy scaffolds produced by selective laser melting for bone tissue engineering.

Selective laser melting (SLM), a method used in the nuclear, space, and racing industries, allows the creation of customized titanium alloy scaffolds with highly defined external shape and internal structure using rapid prototyping as supporting external structures within which bone tissue can grow. Human osteoblasts were cultured on SLM-produced Ti6Al4V mesh scaffolds to demonstrate biocompatibility using scanning electron microscopy (SEM), fluorescence microscopy after cell vitality staining, and common biocompatibility tests (lactate dihydrogenase (LDH), 3-(4,5-dimethylthiazol-2-yl)-2, 5-diphenyltetrazolium bromide (MTT), 5-bromo-2-deoxyuridine (BrdU), and water soluble tetrazolium (WST)). Cell occlusion of pores of different widths (0.45-1.2 mm) was evaluated. Scaffolds were tested for resistance to compressive force. SEM investigations showed osteoblasts with well-spread morphology and multiple contact points. Cell vitality staining and biocompatibility tests confirmed osteoblast vitality and proliferation on the scaffolds. Pore overgrowth increased during 6 weeks' culture at pore widths of 0.45 and 0.5 mm, and in the course of 3 weeks for pore widths of 0.55, 0.6, and 0.7 mm. No pore occlusion was observed on pores of width 0.9-1.2 mm. Porosity and maximum compressive load at failure increased and decreased with increasing pore width, respectively. In summary, the scaffolds are biocompatible, and pore width influences pore overgrowth, resistance to compressive force, and porosity.

[1]  D. Hutmacher,et al.  Scaffolds in tissue engineering bone and cartilage. , 2000, Biomaterials.

[2]  R. Adelung,et al.  Micro-tensile bond strength of three luting resins to human regional dentin. , 2006, Dental materials : official publication of the Academy of Dental Materials.

[3]  P H Krebsbach,et al.  Indirect solid free form fabrication of local and global porous, biomimetic and composite 3D polymer-ceramic scaffolds. , 2003, Biomaterials.

[4]  D J Mooney,et al.  Smooth muscle cell adhesion to tissue engineering scaffolds. , 2000, Biomaterials.

[5]  K. Osakada,et al.  Flexible manufacturing of metallic products by selective laser melting of powder , 2006 .

[6]  A. Ratcliffe,et al.  Human articular chondrocyte adhesion and proliferation on synthetic biodegradable polymer films. , 1999, Biomaterials.

[7]  M. Berzins,et al.  The Selective Laser Sintering of Polycarbonate , 1996 .

[8]  W. Bonfield,et al.  Characterization of porous hydroxyapatite , 1999, Journal of materials science. Materials in medicine.

[9]  M. Mabuchi,et al.  Processing and mechanical properties of autogenous titanium implant materials , 2002, Journal of materials science. Materials in medicine.

[10]  D. Kaplan,et al.  Porosity of 3D biomaterial scaffolds and osteogenesis. , 2005, Biomaterials.

[11]  B Vamsi Krishna,et al.  Processing and biocompatibility evaluation of laser processed porous titanium. , 2007, Acta biomaterialia.

[12]  C. Leroux,et al.  Bone growth in rapid prototyped porous titanium implants. , 2008, Journal of biomedical materials research. Part A.

[13]  Ph. Bertrand,et al.  Ceramic components manufacturing by selective laser sintering , 2007 .

[14]  B. Laget,et al.  Application of laser assisted technologies for fabrication of functionally graded coatings and objects for the International Thermonuclear Experimental Reactor components , 2007 .

[15]  Hyoun‐Ee Kim,et al.  Hydroxyapatite (HA) bone scaffolds with controlled macrochannel pores , 2006, Journal of materials science. Materials in medicine.

[16]  Jean-Pierre Kruth,et al.  New applications of rapid prototyping and rapid manufacturing (RP/RM) technologies for space instrumentation , 2006 .

[17]  L G Griffith,et al.  Effect of pore size and void fraction on cellular adhesion, proliferation, and matrix deposition. , 2001, Tissue engineering.

[18]  U. Ripamonti,et al.  Geometry of porous hydroxyapatite implants influences osteogenesis in baboons (Papio ursinus). , 1996, The Journal of craniofacial surgery.

[19]  H. Eufinger,et al.  Growth and transplantation of a custom vascularised bone graft in a man , 2004, The Lancet.

[20]  J. Le Huec,et al.  Influence of porosity on the mechanical resistance of hydroxyapatite ceramics under compressive stress. , 1995, Biomaterials.

[21]  Michael Wehmöller,et al.  Implant design and production—a new approach by selective laser melting , 2005 .

[22]  K. Hong,et al.  Osteoconduction at porous hydroxyapatite with various pore configurations. , 2000, Biomaterials.

[23]  Scott J Hollister,et al.  Mechanical and in vivo performance of hydroxyapatite implants with controlled architectures. , 2002, Biomaterials.

[24]  Wei Sun,et al.  Computer‐aided tissue engineering: overview, scope and challenges , 2004, Biotechnology and applied biochemistry.

[25]  Ke Yang,et al.  In vitro corrosion behaviour of Mg alloys in a phosphate buffered solution for bone implant application , 2008, Journal of materials science. Materials in medicine.

[26]  Colleen L Flanagan,et al.  Bone tissue engineering using polycaprolactone scaffolds fabricated via selective laser sintering. , 2005, Biomaterials.

[27]  Klaus Ludwig,et al.  The mechanical integrity of in vivo engineered heterotopic bone. , 2006, Biomaterials.

[28]  L. Galois,et al.  Bone ingrowth into two porous ceramics with different pore sizes: an experimental study. , 2004, Acta orthopaedica Belgica.

[29]  M. von Walter,et al.  Structural, mechanical and in vitro characterization of individually structured Ti-6Al-4V produced by direct laser forming. , 2006, Biomaterials.

[30]  Wei Sun,et al.  Computer‐aided tissue engineering: application to biomimetic modelling and design of tissue scaffolds , 2004, Biotechnology and applied biochemistry.

[31]  T. Lee,et al.  Bone tissue engineering evaluation based on rat calvaria stromal cells cultured on modified PLGA scaffolds. , 2006, Biomaterials.

[32]  Maryam Tabrizian,et al.  Three-dimensional growth of differentiating MC3T3-E1 pre-osteoblasts on porous titanium scaffolds. , 2005, Biomaterials.

[33]  L. Bačáková,et al.  The influence of pore size on colonization of poly(l-lactide-glycolide) scaffolds with human osteoblast-like MG 63 cells in vitro , 2008, Journal of materials science. Materials in medicine.

[34]  S. Hollister,et al.  Optimal design and fabrication of scaffolds to mimic tissue properties and satisfy biological constraints. , 2002, Biomaterials.

[35]  H. M. Kim,et al.  Bioactive macroporous titanium surface layer on titanium substrate. , 2000, Journal of biomedical materials research.

[36]  Abhay Pandit,et al.  Fabrication methods of porous metals for use in orthopaedic applications. , 2006, Biomaterials.

[37]  K. Hon,et al.  Selective Laser Sintering of SiC/Polyamide Composites , 2003 .