In recent years, the microfabrication of Lithium Niobate (LiNbO3) based optical integrated devices by using femtosecond laser pulses has been attracting increasing attention. One key current challenge is to understand the mechanism of the interaction of femtosecond laser pulses on LiNbO3 crystal, which is still elusive. Here we demonstrate the etching of LiNbO3 crystal surface by using tightly focused femtosecond laser pulses with repetition rate 75 MHz, pulse duration 50 fs, and single pulse energy 3nJ. The morphology of the etched area is observed by a scanning electron microscope (SEM) which shows the laser illuminated area has obvious thermal damage. When the etching time is 30 seconds and the etched area is 42μm in diameter, thermal damage is observed within the area with 28μm diameter, redeposition is observed in between 28-34μm diameter, and modification is observed in between 34-42μm diameter. A theoretical thermal diffusion model is built to simulate the temperature distribution in the area etched by laser pulses with repetition rates 1 kHz, 1 MHz, and 75 MHz, respectively. The simulation result from 75 MHz repetition rate matches experimental observation very well. The results show that there is thermal damage when LiNbO3 crystal is illuminated with high repetition rate femtosecond laser pulses.
[1]
K Miura,et al.
Writing Waveguides and Gratings in Silica and Related Materials by Femto-Second Laser
,
1998,
Bragg Gratings, Photosensitivity, and Poling in Glass Fibers and Waveguides: Applications and Fundamentals.
[2]
Eric Mazur,et al.
Femtosecond Laser Micromachining
,
2013
.
[3]
Masaaki Sakakura,et al.
Three-dimensional temperature distribution and modification mechanism in glass during ultrafast laser irradiation at high repetition rates.
,
2012,
Optics express.
[4]
Zbigniew Sikorski,et al.
Single-pulse ultrafast-laser machining of high aspect nano-holes at the surface of SiO2.
,
2008,
Optics express.
[5]
Robert R. Thomson,et al.
Ultrafast Nonlinear Optics
,
2013
.
[6]
Christoph Vannahme,et al.
Integrated Optical Devices in Lithium Niobate
,
2008
.
[7]
K. Miura,et al.
Writing waveguides in glass with a femtosecond laser.
,
1996,
Optics letters.
[8]
Fumiyo Yoshino,et al.
Heat accumulation effects in femtosecond laser-written waveguides with variable repetition rate.
,
2005,
Optics express.
[9]
Roberto Osellame,et al.
Micromachining of photonic devices by femtosecond laser pulses
,
2008
.