Fatigue crack formation and growth from localized corrosion in Al–Zn–Mg–Cu

Abstract The effect of precorrosion on the fatigue life of aluminum alloy 7075-T6511 was measured, physical characteristics of corrosion topography plus fatigue damage were established by microscopy, and a corrosion modified equivalent initial flaw size (CM-EIFS) was established using fracture mechanics modeling. Fatigue life is reduced by clustered corrosion pits on the L–S surface from laboratory-EXCO exposure. Cracks initiate from pits clustered as a semi-elliptical surface micronotch rather than the deepest pits, consistent with shape-dependent stress intensity. Marker band analysis establishes that the number of cycles to form a crack about a pit cluster can be a significant fraction of total fatigue life. The CM-EIFS, back-calculated from fracture mechanics analysis of measured fatigue life, equals measured initiating-pit cluster size provided that important inputs are provided; such favorable comparison validates this approach to corrosion-fatigue interaction. Calculated CM-EIFS provides a metric to characterize alloy corrosion damage, and can be used to forward-model the effects of stress and loading environment on fatigue life distribution, critical for efficient alloy development. Use in prognosis of the fatigue performance of a service-corroded surface is hindered by uncertain non-destructive characterization of corrosion topography.

[1]  William A. Herman,et al.  A SIMPLIFIED LABORATORY APPROACH FOR THE PREDICTION OF SHORT CRACK BEHAVIOR IN ENGINEERING STRUCTURES , 1988 .

[2]  T. C. Lindley,et al.  The effect of porosity on the fatigue life of cast aluminium-silicon alloys , 2004 .

[3]  M. Liao,et al.  Fatigue modeling for aircraft structures containing natural exfoliation corrosion , 2007 .

[4]  S. Pantelakis,et al.  Evidence on the corrosion-induced hydrogen embrittlement of the 2024 aluminium alloy , 2005 .

[5]  R. J. H. Wanhill,et al.  An AGARD-coordinated corrosion fatigue cooperative testing programme , 1982 .

[6]  James C. Newman,et al.  The Merging of Fatigue and Fracture Mechanics Concepts: A Historical Perspective , 1998 .

[7]  Phil E. Irving,et al.  Corrosion pit size distributions and fatigue lives: a study of the EIFS technique for fatigue design in the presence of corrosion , 2004 .

[8]  Rj Bucci,et al.  Predicting fatigue life of pre-corroded 2024-T3 aluminum , 2004 .

[9]  Yiu-Wing Mai,et al.  Advances in Fracture Research , 1997 .

[10]  James C. Newman,et al.  On Generating Fatigue Crack Growth Thresholds , 2003 .

[11]  D. G. Harlow,et al.  Corrosion Enhanced Fatigue and MSD , 2002 .

[12]  S. D. Manning,et al.  Demonstration of probabilistic-based durability analysis method for metallic airframes , 1990 .

[13]  S. Spence,et al.  The EIFS distribution for anodized and pre-corroded 7010-T7651 under constant amplitude loading , 2005 .

[14]  A. J. Green,et al.  Characterisation of equivalent initial flaw sizes in 7050 aluminium alloy , 2006 .

[15]  Kumar V. Jata,et al.  Effects of pitting corrosion on the fatigue behavior of aluminum alloy 7075-T6: modeling and experimental studies , 2001 .

[16]  B. Hillberry,et al.  A model of initial flaw sizes in aluminum alloys , 2001 .

[17]  B. M. Hillberry,et al.  Initiation and shape development of corrosion-nucleated fatigue cracking , 2007 .

[18]  B. Craig,et al.  Multiple fatigue crack growth in pre-corroded 2024-T3 aluminum , 2005 .

[19]  C. Sarrazin-Baudoux,et al.  6.05 – Environmentally Assisted Fatigue in the Gaseous Atmosphere , 2003 .

[20]  Rudolph G. Buchheit,et al.  Correlation of residual fatigue life with quantified NDE measurements , 2005 .

[21]  Theodore E. Matikas,et al.  Multiscale characterization of pitting corrosion and application to an aluminum alloy , 2000 .

[22]  D. G. Harlow,et al.  Probabilities of occurrence and detection of damage in airframe materials , 1999 .

[23]  James A Harter,et al.  Comparison of contemporary FCG life prediction tools , 1999 .

[24]  D. G. Harlow,et al.  Probability modelling and statistical analysis of damage in the lower wing skins of two retired B‐707 aircraft , 2001 .

[25]  David W. Hoeppner,et al.  Pit-to-crack transition in pre-corroded 7075-T6 aluminum alloy under cyclic loading , 2005 .

[26]  Simon Barter,et al.  Initiation and early growth of fatigue cracks in an aerospace aluminium alloy , 2002 .

[27]  S. A. Fawaz.  Equivalent initial flaw size testing and analysis of transport aircraft skin splices , 2003 .

[28]  Robert P. Wei,et al.  Corrosion-Enhanced Fatigue and Multiple-Site Damage , 2003 .

[29]  Rj Bucci,et al.  Predicting fatigue life of pre-corroded 2024-T3 aluminum from breaking load tests , 2004 .

[30]  B. M. Hillberry,et al.  Characterization of pitting damage and prediction of remaining fatigue life , 2008 .