Types, processing and properties of bioadhesives for wood and fibers

Abstract: The chapter describes the state of the art of biobased adhesives for wood, namely modern approaches to the already commercial tannin adhesives, as well as lignin-based adhesives, carbohydrate adhesives, protein adhesives, unsaturated oil adhesives and wood welding by mechanical friction without adhesives.

[1]  A. Pizzi,et al.  Synthetic-resin-free wood panel adhesives from mixed low molecular mass lignin and tannin , 2011, European Journal of Wood and Wood Products.

[2]  Antonio Pizzi,et al.  Application of Numerical Modelling to Dowel-Welded Wood Joints , 2010 .

[3]  R. Wool,et al.  Acrylated Epoxidized Soy Oil as an Alternative to Urea-Formaldehyde in Making Wheat Straw Particleboards , 2010 .

[4]  A. Pizzi,et al.  Gluten Protein Adhesives for Wood Panels , 2010 .

[5]  A. Pizzi,et al.  Wood Panel Adhesives from Low Molecular Mass Lignin and Tannin without Synthetic Resins , 2010 .

[6]  A. Pizzi,et al.  Influence of grain direction and pre-heating on linear wood welding , 2010, European Journal of Wood and Wood Products.

[7]  A. Pizzi,et al.  High resin content natural matrix–natural fibre biocomposites , 2009 .

[8]  A. Pizzi,et al.  Physico-chemical Causes of the Extent of Water Resistance of Linearly Welded Wood Joints , 2009 .

[9]  A. Pizzi,et al.  Improving the Water Resistance of Linear Vibration-Welded Wood Joints , 2009 .

[10]  A. Pizzi,et al.  Influence of Wood Grain Direction on Linear Welding , 2009 .

[11]  A. Pizzi,et al.  Influence of Wood Welding Frequency on Wood Constituents Chemical Modifications , 2009 .

[12]  A. Pizzi,et al.  Industrial hardboard and other panels binder from waste lignocellulosic liquors/phenol-formaldehyde resins , 1998, Holz als Roh- und Werkstoff.

[13]  A. Pizzi,et al.  Lower temperature tannin/hexamine-bonded particleboard of improved performance , 1996, Holz als Roh- und Werkstoff.

[14]  Antonio Pizzi,et al.  Environment-Friendly Soy Flour-Based Resins Without Formaldehyde , 2008 .

[15]  C. Ganne-Chédeville,et al.  CP-MAS 13C NMR and FT-IR investigation of the degradation reactions of polymer constituents in wood welding , 2008 .

[16]  G. Du,et al.  Environmentally friendly mixed tannin/lignin wood resins , 2008 .

[17]  A. Pizzi,et al.  Dependence of tannin/hexamine particleboard performance from pressing conditions , 1997, Holz als Roh- und Werkstoff.

[18]  A. Pizzi,et al.  Industrial tannin/hexamine low-emission exterior particleboards , 1997, Holz als Roh- und Werkstoff.

[19]  J. Salvadó,et al.  Lignin‐based polycondensation resins for wood adhesives , 2007 .

[20]  A. Pizzi,et al.  Wood joints and laminated wood beams assembled by mechanically-welded wood dowels , 2007 .

[21]  A. Pizzi,et al.  Low formaldehyde emission, fast pressing, pine and pecan tannin adhesives for exterior particleboard , 1994, Holz als Roh- und Werkstoff.

[22]  A. Pizzi.  Hardening mechanism of tannin adhesives with hexamine , 1994, Holz als Roh- und Werkstoff.

[23]  Yuan Liu,et al.  Development and characterization of adhesives from soy protein for bonding wood , 2007 .

[24]  A. Pizzi,et al.  Autocondensation-based, zero-emission, tannin adhesives for particleboard , 2007, Holz als Roh- und Werkstoff.

[25]  Antonio Pizzi,et al.  Lignin-based wood panel adhesives without formaldehyde , 2007, Holz als Roh- und Werkstoff.

[26]  G. Wegener,et al.  Chemical investigations on the thermal behaviour of wood during friction welding , 2006, Wood Science and Technology.

[27]  L. Resch,et al.  Full-scale (industrial) wood floor using welded-through dowels , 2006 .

[28]  Antonio Pizzi,et al.  Wood joints by through-dowel rotation welding: microstructure, 13C-NMR and water resistance , 2006 .

[29]  A. Pizzi,et al.  Structural beams from thick wood panels bonded industrially with formaldehyde-free tannin adhesives , 2006 .

[30]  L. Resch,et al.  Welding-through doweling of wood panels , 2006, Holz als Roh- und Werkstoff.

[31]  J. Natterer,et al.  Joining wood by friction welding , 2005, Holz als Roh- und Werkstoff.

[32]  Antonio Pizzi,et al.  Parameters influencing wood-dowel welding by high-speed rotation , 2005 .

[33]  C. Ganne-Chédeville,et al.  Parameter interactions in two-block welding and the wood nail concept in wood dowel welding , 2005 .

[34]  C. Frihart,et al.  Analysis of soy flour/phenol-formaldehyde adhesives for bonding wood , 2005 .

[35]  Antonio Pizzi,et al.  Influence of grain direction in vibrational wood welding , 2005 .

[36]  Antonio Pizzi,et al.  Wood dowel bonding by high-speed rotation welding , 2004 .

[37]  A. Pizzi,et al.  X-ray microdensitometry analysis of vibration-welded wood , 2004 .

[38]  M. Alma,et al.  Preparation of sulfuric acid-catalyzed phenolated wood resin , 1998, Wood Science and Technology.

[39]  A. Pizzi,et al.  Upgrading melamine–urea–formaldehyde polycondensation resins with buffering additives. I. The effect of hexamine sulfate and its limits , 2003 .

[40]  Z. Zhong,et al.  Wet Strength and Water Resistance of Modified Soy Protein Adhesives and Effects of Drying Treatment , 2003 .

[41]  A. Gandini,et al.  Furan-Based Adhesives , 2003 .

[42]  Antonio Pizzi,et al.  Wood bonding by vibrational welding , 2003 .

[43]  B. Riedl,et al.  Effects of Pinus pinaster bark extracts content on the cure properties of tannin-modified adhesives and on bonding of exterior grade MDF , 2003 .

[44]  Sumin Kim,et al.  Curing behavior and viscoelastic properties of pine and wattle tannin-based adhesives studied by dynamic mechanical thermal analysis and FT-IR-ATR spectroscopy , 2003 .

[45]  Yuan Liu,et al.  Chemical Modification of Soy Protein for Wood Adhesives , 2002 .

[46]  A. Pizzi,et al.  A no-aldehyde emission hardener for tannin-based wood adhesives for exterior panels , 2001, Holz als Roh- und Werkstoff.

[47]  P. Triboulot,et al.  Exterior OSB preparation technology at high moisture content – Part 1: Transfer mechanisms and pressing parameters , 2001, Holz als Roh- und Werkstoff.

[48]  P. Blanchet,et al.  Particleboard made from hammer milled black spruce bark residues , 2000, Wood Science and Technology.

[49]  A. Pizzi,et al.  Hexamine hardener behaviour: effects on wood glueing, tannin and other wood adhesives , 1999, Holz als Roh- und Werkstoff.

[50]  X. Sun,et al.  Shear strength and water resistance of modified soy protein adhesives , 1999 .

[51]  A. Pizzi,et al.  Crosslinked and entanglement networks in thermomechanical analysis of polycondensation resins , 1998 .

[52]  A. Pizzi,et al.  Polycondensation and autocondensation networks in polyflavonoid tannins. I. Final networks , 1998 .

[53]  A. Pizzi,et al.  Polycondensation and autocondensation networks in polyflavonoid tannins. II. Polycondensation versus autocondensation , 1998 .

[54]  A. Hüttermann,et al.  Polyphenoles for compounded materials , 1998 .

[55]  A. Hüttermann,et al.  Biotechnological production of wood composites. , 1998 .

[56]  A. Pizzi,et al.  Comparative kinetics of the induced radical autocondensation of polyflavonoid tannins. II. Flavonoid units effects , 1997 .

[57]  C. Felby,et al.  Enhanced Auto Adhesion of Wood Fibers Using Phenol Oxidases , 1997 .

[58]  A. Pizzi,et al.  Comparative kinetics of the induced radical autocondensation of polyflavonoid tannins. III. Micellar reactions vs. cellulose surface catalysis , 1996 .

[59]  A. Pizzi,et al.  Comparative kinetics of induced radical autocondensation of polyflavonoid tannins. I. Modified and nonmodified tannins , 1996 .

[60]  M. Alma,et al.  The Preparation and Flow Properties of HC1 Catalyzed Phenolated Wood and its Blends with Commercial Novolak Resin , 1996 .

[61]  D. Myers,et al.  Alkali-modified soy protein with improved adhesive and hydrophobic properties , 1995 .

[62]  A. Pizzi,et al.  Induced accelerated autocondensation of polyflavonoid tannins for phenolic polycondensates. III. CP‐MAS 13C‐NMR of different tannins and models , 1995 .

[63]  A. Pizzi,et al.  Induced accelerated autocondensation of polyflavonoid tannins for phenolic polycondensates. II. Cellulose effect and application , 1995 .

[64]  A. Pizzi,et al.  Induced accelerated autocondensation of polyflavonoid tannins for phenolic polycondensates. I. 13C‐NMR, 29Si‐NMR, X‐ray, and polarimetry studies and mechanism , 1994 .

[65]  Y. Sano,et al.  Preparation of Moderate-Temperature Setting Adhesives from Softwood Kraft Lignin. Part 2. Effect of Some Factors on Strength Properties and Chracteristics of Lignin-Based Adhesives , 1994 .

[66]  A. Pizzi,et al.  A comparative C13 NMR study of polyflavonoid tannin extracts for phenolic polycondensates , 1993 .

[67]  A. Pizzi,et al.  Rapid-Curing Lignin-Based Exterior Wood Adhesives. Part II: Esters Acceleration Mechanism and Application to Panel Products , 1993 .

[68]  A. Pizzi,et al.  Rapid Curing Lignin-Based Exterior Wood Adhesives. Part I. Diisocyanates Reaction Mechanisms and Application to Panel Products , 1993 .

[69]  Bryan H. River,et al.  Carbohydrate Modfied Phenol-Formaldehyde Resins , 1986 .

[70]  A. Jarrett.  University of the Orange Free State , 1985 .

[71]  W. Glasser,et al.  Engineering Plastics from Lignin - XII. Synthesis and Performance of Lignin Adhesives with Isocyanate and Melamine , 1985 .

[72]  A. Pizzi.  Tannin-Based Adhesives , 1980 .

[73]  V. Dallons.  Pollution from several wood species in hardboard production , 1978 .