Flat‐punch indentation of viscoelastic material

The indentation of standard viscoelastic solids, that is, the three-element viscoelastic material, by an axisymmetric, flat-ended indenter has been investigated theoretically. Under the boundary conditions of flat-punch indentation of a viscoelastic half-space, the solutions of the equations of viscoelastic deformation are derived for the standard viscoelastic material. Their generality resides in their inclusion of compressible as well as incompressible solids. They cover the two transient situations: flat-punch creep test and load-relaxation test. In experimental tests of their applicability, nanoindentation and microindentation probes under creep and relaxation conditions yielded a modulus from 0.1 to 1.1 GPa and viscosity from 1 to 37 Gpa · s for a crosslinked glassy polyurethane coatings. For bulk polystyrene, the values vary from 1 to 2 GPa and from 20 to 40 Gpa · s, respectively. The analysis here provides a fundamental basis for probing elastic and viscous properties of coatings with nanoindentation or microindentation tests. © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 38: 10–22, 2000

[1] En-Jui Lee,et al. The Contact Problem for Viscoelastic Bodies , 1960 .

[2] T. C. T. Ting,et al. The Contact Stresses Between a Rigid Indenter and a Viscoelastic Half-Space , 1966 .

[3] Wei Hsuin Yang,et al. The Contact Problem for Viscoelastic Bodies , 1966 .

[4] M. S. Paterson,et al. Effect of Pressure on Young's Modulus and the Glass Transition in Rubbers , 1964 .

[5] S. C. Hunter. The Hertz problem for a rigid spherical indenter and a viscoelastic half-space , 1960 .

[6] I. N. Sneddon,et al. The elastic stresses produced by the indentation of the plane surface of a semi-infinite elastic solid by a rigid punch , 1945, Mathematical Proceedings of the Cambridge Philosophical Society.

[7] T. W. Wu. Microscratch and load relaxation tests for ultra-thin films , 1991 .

[8] W. Gerberich,et al. Techniques and considerations for nanoindentation measurements of polymer thin film constitutive properties , 1998 .

[9] M. Shelef,et al. Prediction of the deformation properties of polymeric and composite materials , 1994 .

[10] P. Meares. Polymers: Structure and Bulk Properties , 1965 .

[11] L. Cheng,et al. HARD PROTECTIVE OVERLAYERS ON VISCOELASTIC-PLASTIC SUBSTRATES , 1999 .

[12] K. Johnson. Contact Mechanics: Frontmatter , 1985 .

[13] L. Sperling. Introduction to physical polymer science , 1986 .