Defect-free asymmetric hollow fiber membranes from Torlon®, a polyamide–imide polymer, for high-pressure CO2 separations

Abstract Torlon ® , a polyamide–imide polymer, was used for high-pressure CO 2 separations, as it can form inter- and intra-chain hydrogen bonding that may provide stability against plasticization. Asymmetric hollow fiber membranes with a defect-free selective skin were successfully formed from Torlon ® using a dry–wet spinning process. Dope and spinning parameters were optimized to obtain these fibers, which had CO 2 /CH 4 selectivity of 44 and O 2 /N 2 selectivity of 7.7. These selectivities are about 85% of the intrinsic (dense film) value of 52 for CO 2 /CH 4 and 90% of the intrinsic value of 8.3 for O 2 /N 2 , respectively. Based on analyses presented, the reduced selectivities are attributed to substructure resistance rather than actual skin layer defects. Macrovoids, which compromise the strength of the fiber, were reduced by increasing the polymer concentration. The resulting fiber could withstand up to 2000 psi of N 2 , and a CO 2 permeation study indicates that this fiber can perform selective separations under supercritical conditions of 1100 psi of CO 2 at 35 °C.

[1]  William J. Koros,et al.  Phase separation, vitrification, and the manifestation of macrovoids in polymeric asymmetric membranes , 1996 .

[2]  Donald R Paul,et al.  Natural gas permeation in polyimide membranes , 2004 .

[3]  William J. Koros,et al.  TERMINOLOGY FOR MEMBRANES AND MEMBRANE PROCESSES , 1996 .

[4]  J. DeSimone,et al.  Heterogeneous polymerization of fluoroolefins in supercritical carbon dioxide , 2005 .

[5]  Klaus-Viktor Peinemann,et al.  Gas permeation through composite membranes , 1988 .

[6]  Marcel Mulder,et al.  Basic Principles of Membrane Technology , 1991 .

[7]  C. A. Smolders,et al.  Plasticization of gas separation membranes , 1991 .

[8]  W. Koros,et al.  Polymeric membranes based on bisphenol-A for gas separations , 1989 .

[9]  J. M. Henis,et al.  Composite Hollow Fiber Membranes for Gas Separation: The Resistance Model Approach , 1981 .

[10]  I. Pinnau,et al.  Relationship between substructure resistance and gas separation properties of defect-free integrally skinned asymmetric membranes , 1991 .

[11]  M. Donohue,et al.  Permeation behavior of carbon dioxide-methane mixtures in cellulose acetate membranes☆ , 1989 .

[12]  D. Peng,et al.  A New Two-Constant Equation of State , 1976 .

[13]  D. G. Pye,et al.  Measurement of gas permeability of polymers. I. Permeabilities in constant volume/variable pressure apparatus , 1976 .

[14]  William J. Koros,et al.  Formation of defect-free polyimide hollow fiber membranes for gas separations , 2000 .

[15]  William J. Koros,et al.  High Pressure CO2/CH4 Separation Using Carbon Molecular Sieve Hollow Fiber Membranes , 2002 .

[16]  S. Cooper,et al.  Hydrogen bonding in polyamides , 1976 .

[17]  Matthias Wessling,et al.  CO2-induced plasticization phenomena in glassy polymers , 1999 .

[18]  Paul C. Painter,et al.  Hydrogen bonding in polymers: infrared temperature studies of an amorphous polyamide , 1985 .

[19]  R. Baker.  Membrane Technology and Applications , 1999 .

[20]  Crosslinked hollow fiber membranes for natural gas purification and their manufacture from novel polymers , 2004 .

[21]  W. Koros,et al.  A model for permeation of mixed gases and vapors in glassy polymers , 1981 .

[22]  Edward L Cussler,et al.  Terminology for membranes and membrane processes (IUPAC Recommendations 1996) , 1996 .

[23]  C. P. Borges,et al.  Hollow fiber formation using Lewis acid : Base complex in the polymer solution , 2001 .

[24]  I. Pinnau,et al.  Structures and gas separation properties of asymmetric polysulfone membranes made by dry, wet, and dry/wet phase inversion , 1991 .

[25]  Donald R Paul,et al.  The Effects of Crosslinking Chemistry on CO2 Plasticization of Polyimide Gas Separation Membranes , 2002 .

[26]  Tejraj M. Aminabhavi,et al.  Matrimid polyimide membranes for the separation of carbon dioxide from methane , 2007 .

[27]  G. Robertson,et al.  Structural determination of Torlon® 4000T polyamide–imide by NMR spectroscopy , 2004 .

[28]  A. Cooper,et al.  Polymer synthesis and characterization in liquid / supercritical carbon dioxide , 1996 .

[29]  W. Koros,et al.  Aqueous quenched asymmetric polysulfone hollow fibers prepared by dry/wet phase separation , 1994 .

[30]  William J. Koros,et al.  Performance of natural gas membranes in the presence of heavy hydrocarbons , 2006 .

[31]  W. Koros,et al.  “Sorp-vection”: An unusual membrane-based separation , 2005 .

[32]  P. Painter,et al.  Hydrogen bonding in polymers. 2. Infrared temperature studies of nylon 11 , 1986 .

[33]  H Denny Kamaruddin,et al.  Some observations about the application of Fick's first law for membrane separation of multicomponent mixtures , 1997 .

[34]  W. Koros,et al.  A new technique for the measurement of multicomponent gas transport through polymeric films , 1986 .

[35]  William J. Koros,et al.  Characterization of low permeability gas separation membranes and barrier materials; design and operation considerations , 2004 .

[36]  C. A. Smolders,et al.  The resistance towards gas transport of the sublayer of asymmetric PPO hollow fiber membranes determined by plasma-etching , 1991 .

[37]  W. Koros,et al.  Morphology of integral-skin layers in hollow-fiber gas-separation membranes , 2003 .