Real-time Quantitative Imaging of Failure Events in Materials under Load at Temperatures above 1,600

Ceramic matrix composites are the emerging material of choice for structures that will see temperatures above ~1,500 °C in hostile environments, as for example in next-generation gas turbines and hypersonic-flight applications. The safe operation of applications depends on how small cracks forming inside the material are restrained by its microstructure. As with natural tissue such as bone and seashells, the tailored microstructural complexity of ceramic matrix composites imparts them with mechanical toughness, which is essential to avoiding failure. Yet gathering three-dimensional observations of damage evolution in extreme environments has been a challenge. Using synchrotron X-ray computed microtomography, we have fully resolved sequences of microcrack damage as cracks grow under load at temperatures up to 1,750 °C. Our observations are key ingredients for the high-fidelity simulations used to compute failure risks under extreme operating conditions.

[1]  A. Evans,et al.  The mechanics of matrix cracking in brittle-matrix fiber composites , 1985 .

[2]  D. Marshall,et al.  Influence of statistical fiber strength distribution on matrix cracking in fiber composites , 1989 .

[3]  M. C. Nichols,et al.  X-Ray Tomographic Microscopy (XTM) Using Synchrotron Radiation , 1992 .

[4]  John W. Hutchinson,et al.  Fiber-matrix debonding effects oncracking in aligned fiber ceramic composites , 1995 .

[5]  G. Morscher,et al.  Determination of Interfacial Properties Using a Single‐Fiber Microcomposite Test , 1996 .

[6]  Adrian P. Mouritz,et al.  Review of applications for advanced three-dimensional fibre textile composites , 1999 .

[7]  M. S. Dadkhah,et al.  Effect of Weave Architecture on Tensile Properties and Local Strain Heterogeneity in Thin‐Sheet C–SiC Composites , 2002 .

[8]  J. H. Westbrook,et al.  Ultrahigh-Temperature Materials for Jet Engines , 2003 .

[9]  G. Morscher.  Tensile Stress Rupture of SiCf/SiCmMinicomposites with Carbon and Boron Nitride Interphases at Elevated Temperatures in Air , 2005 .

[10]  R. Raj,et al.  The role of carbon in unexpected visco(an)elastic behavior of amorphous silicon oxycarbide above 1273 K , 2005 .

[11]  A. Gessler,et al.  Ceramic Matrix Composites: A Challenge in Space‐Propulsion Technology Applications , 2005 .

[12]  M Stampanoni,et al.  Implementation of a fast method for high resolution phase contrast tomography. , 2006, Optics express.

[13]  Lorrie Molent,et al.  Flight-by-flight fatigue crack growth life assessment , 2007 .

[14]  P. Cloetens,et al.  Quantitative comparison of direct phase retrieval algorithms in in-line phase tomography. , 2008, Medical physics.

[15]  David B. Marshall,et al.  Integral Textile Ceramic Structures , 2008 .

[16]  T. Okabe,et al.  Estimation of statistical strength distribution of Carborundum polycrystalline SiC fiber using the single fiber composite with consideration of the matrix hardening , 2008 .

[17]  S. Stock.  Recent advances in X-ray microtomography applied to materials , 2008 .

[18]  G. Morscher,et al.  Design Guidelines for In‐Plane Mechanical Properties of SiC Fiber‐Reinforced Melt‐Infiltrated SiC Composites , 2009 .

[19]  Anne Sakdinawat,et al.  Nanoscale X-ray Imaging , 2009 .

[20]  M. Rappaz,et al.  In situ X-ray tomography observation of inhomogeneous deformation in semi-solid aluminium alloys , 2009 .

[21]  B. Münch,et al.  Stripe and ring artifact removal with combined wavelet--Fourier filtering. , 2009, Optics express.

[22]  W. Ludwig,et al.  In situ X-ray microtomography characterization of damage in SiCf/SiC minicomposites , 2011 .

[23]  F. Zok,et al.  High-temperature materials testing with full-field strain measurement: experimental design and practice. , 2011, The Review of scientific instruments.

[24]  Zheng Hui-qi.  Experimental Design and Practice of Green Inorganic Chemistry Based on “5R”Rules , 2013 .