The ambient aging of wood fiber and its effect on mechanical properties of MDF panels

Fourier-transform infrared (FTIR) spectroscopy and scanning electron microscopy (SEM) were used to study ambient-aged wood fibers and their effects on the mechanical properties of medium-density fiberboard (MDF). It was found that MDF made with ambient-aged fibers had poorer mechanical properties than MDF made with fresh fibers; this difference resulted from the alterations of surface characteristics of wood fibers after ambient aging, which led to poor wettability of the urea–formaldehyde (UF) resin applied to the aged wood fibers. After 6 months of ambient aging, the concentration of carbonyl groups in the fibers increased by 144%, while the pH value of wood fiber decreased from 5.2 to 4.7. SEM showed that much more UF resin agglomerated on the surface of ambient-aged fibers and the breakage of MDF made with aged fiber frequently occurred at the resin-fiber interfaces, indicated the poorer wettability of UF resin to fibers due to the decrease in surface energy after aging.

[1]  N. M. S. El‐Din,et al.  Effect of accelerated aging on the properties of some writing paper sheets , 1994 .

[2]  M. Dunky,et al.  Urea–formaldehyde (UF) adhesive resins for wood , 1998 .

[3]  B. Riedl,et al.  Chemical modification and wetting of medium density fibreboard panels produced from fibres treated with maleated polypropylene wax , 2006, Wood Science and Technology.

[4]  Zhenhua Gao,et al.  Curing Characteristics of Urea-Formaldehyde Resin in the Presence of Various Amounts of Wood Extracts and Catalysts , 2008 .

[5]  S. Y. Zhang,et al.  Differential scanning calorimetry characterization of urea–formaldehyde resin curing behavior as affected by less desirable wood material and catalyst content , 2005 .

[6]  A. W. Christiansen.  HOW OVERDRYING WOOD REDUCES ITS BONDING TO PHENOL-FORMALDEHYDE ADHESIVES : A CRITICAL REVIEW OF THE LITERATURE . PART I . PHYSICAL RESPONSES , 2006 .

[7]  C. Costa,et al.  A global model for the hot-pressing of MDF , 2003, Wood Science and Technology.

[8]  A. Christiansen.  How overdrying wood reduces its bonding to phenol-formaldehyde adhesives : a critical review of the literature. Part II, Chemical reactions , 1990 .

[9]  B. Riedl,et al.  Dimensional stability of MDF panels produced from fibres treated with maleated polypropylene wax , 2005, Wood Science and Technology.

[10]  R. Nussbaum.  Natural surface inactivation of Scots pine and Norway spruce evaluated by contact angle measurements , 1999, Holz als Roh- und Werkstoff.

[11]  C. Klason,et al.  The Efficiency of Cellulosic Fillers in Common Thermoplastics. Part II. Filling with Processing Aids and Coupling Agents , 1984 .