Er3+/Yb3+-activated silica–titania planar waveguides for EDPWAs fabricated by rf-sputtering

Abstract Two Er3+/Yb3+-codoped 92SiO2–8TiO2 planar waveguides, with 1.2 mol% Er and molar ratio Er/Yb of 2, were fabricated by rf-sputtering technique. The active films were deposited on silica-on-silicon and silica glass substrates. The thickness of the waveguides and the refractive index at 632.8 and 543.5 nm were measured by an m-line apparatus. The losses, for the TE0 mode, were evaluated at 632.8 and 1300 nm. The structural properties were investigated by energy dispersive spectroscopy and Raman spectroscopy. All waveguides were single-mode at 1550 nm. An attenuation coefficient of 0.5 dB/cm at 632.8 nm and 0.1 dB/cm at 1300 nm were measured. The emission at 1530 nm of the 4I13/2 → 4I15/2 transition of Er3+ ion was observed at room temperature upon continuous wave excitation at 981 and 514.5 nm. Back energy transfer from Er3+ to Yb3+ was demonstrated by measurement of Yb3+ emission upon Er3+ excitation at 514.5 nm. Effective excitation efficiency of Er3+ ions by co-doping with Yb3+ ions was shown by photoluminescence excitation spectroscopy.

[1]  Eric M. Yeatman,et al.  Sol-gel silica/titania-on-silicon Er/Yb-doped waveguides for optical amplification at 1.5 μm , 1999 .

[2]  Eric M. Yeatman,et al.  Optical gain in Er-doped SiO2–TiO2 waveguides fabricated by the sol–gel technique , 1999 .

[3]  Markus P. Hehlen,et al.  Spectroscopic properties of Er 3+ - and Yb 3+ -doped soda-lime silicate and aluminosilicate glasses , 1997 .

[4]  Homogeneous line width in a zinc borate glass activated by Eu3 , 1997 .

[5]  Niloy K. Dutta,et al.  Spectroscopic properties of Yb-doped silica glass , 2002 .

[6]  Carmen N. Afonso,et al.  Pulsed laser deposition for optical doping of active waveguide films , 1997 .

[7]  Mitsuho Yasu,et al.  Fabrication of SiO2-TiO2 glass planar optical waveguides by flame hydrolysis deposition , 1983 .

[8]  Fabio Pozzi,et al.  Erbium-activated silica–titania planar waveguides on silica-on-silicon substrates prepared by rf sputtering , 2001 .

[9]  Fabio Pozzi,et al.  Erbium-activated silica-titania planar waveguides prepared by rf-sputtering , 2001, SPIE OPTO.

[10]  X. Zou,et al.  Evaluation of spectroscopic properties of Yb3+-doped glasses. , 1995, Physical review. B, Condensed matter.

[11]  Michel J. F. Digonnet,et al.  Rare earth doped fiber lasers and amplifiers , 1993 .

[12]  A. Polman,et al.  Erbium implanted thin film photonic materials , 1997 .

[13]  G. Grand,et al.  Low-loss PECVD silica channel waveguides for optical communications , 1990 .

[14]  Younes Messaddeq,et al.  Low optical loss planar waveguides prepared in an organic-inorganic hybrid system , 2000 .

[15]  J. S. Hayden,et al.  Ion-exchanged waveguide lasers in Er3+/Yb3+ codoped silicate glass. , 1999, Applied optics.

[16]  M. Brenci,et al.  Active optical waveguides based on Er- and Er/Yb-doped silicate glasses , 2001 .

[17]  Rui M. Almeida,et al.  Optical loss mechanisms in nanocomposite sol-gel planar waveguides , 1997, Optics & Photonics.