Abstract By combining calorimetric measurements with dilatometry, it has been possible to calculate the contributions of thermal expansion, pore pressure, and crystallization pressure of ice to the strain observed in a mortar during freezing/thawing cycles. Air-entrained mortars contract upon freezing, while non-air-entrained mortars expand. The expansion of the latter is attributed primarily to hydraulic pressure, owing to the rapid growth of ice, which nucleates at low temperatures in laboratory samples. Poromechanical calculations account quantitatively for the contraction of samples with air entrainment, assuming that ice crystals form in the air voids. As originally proposed by Powers and Helmuth, those crystals create suction in the pore liquid that offsets the crystallization pressure of ice in the mesopores of the paste, resulting in a net contraction. Ice in the matrix also contributes significantly to the increase in the thermal expansion coefficient of the mortar. The magnitude of the contraction in air-entrained mortar is shown to account for a reduction of salt scaling damage. According to the glue-spall theory, the damage results from cracking of the ice on the surface of concrete, when the thermal expansion mismatch stress exceeds the strength of the ice. The contraction of the mortar caused by air entrainment offsets the thermal expansion mismatch sufficiently to prevent cracking. Based on observations of the nucleation temperature of ice in laboratory samples of various sizes, it is estimated that there is one site capable of nucleating ice at − 1 °C in a cube of mortar roughly 34 cm on an edge (or, one per square meter in a slab 3 cm thick). This suggests that ice nucleates in the field at high temperatures, compared to what is typically seen in the laboratory, and propagates slowly through the pores as the temperature drops. This mode of growth may lead to fatigue damage over many cycles, owing to local stresses from crystallization pressure, where the contribution of hydraulic pressure is insignificant.

[1]  G. Scherer,et al.  Measuring Permeability of Rigid Materials by a Beam‐Bending Method: III, Cement Paste , 2002 .

[2]  R. Gagnon,et al.  Elastic Properties of Ice , 2001 .

[3]  V. F. Petrenko,et al.  Physics of Ice , 1999 .

[4]  David J. Corr,et al.  Microscopic Characterization of Ice Morphology in Entrained Air Voids , 2002 .

[5]  Columbia Co.,et al.  Pore structure and permeability of cementitious materials , 1989 .

[6]  Charles Eyraud,et al.  A new method for the simultaneous determination of the size and shape of pores: the thermoporometry , 1977 .

[7]  D. Anderson.  Preliminary Results and Review of Sea Ice Elasticity and Related Studies , 1958 .

[8]  G. Scherer,et al.  Deformation of aerogels during characterization , 1995 .

[9]  T C Powers,et al.  "A tribute to Theory of Volume Changes in Hardened Portland-Cement Paste during Freezing""""" , 2008, SP-249: Selected Landmark Paper Collection on Concrete Materials Research.

[10]  Don L. Anderson,et al.  An Experimental Study of Strength of Young Sea Ice , 1958 .

[11]  Jean Sulem,et al.  Poromechanical behaviour of hardened cement paste under isotropic loading , 2008 .

[12]  George Comfort,et al.  MECHANICAL PROPERTIES OF FIRsT-YEAR SEA ICE AT TARSIUT ISLAND , 1997 .

[13]  George W. Scherer,et al.  New Methods to Measure Liquid Permeability in Porous Materials , 2007 .

[14]  J. Christian,et al.  The theory of transformations in metals and alloys , 2003 .

[15]  Richard Schapery.  Thermal Expansion Coefficients of Composite Materials Based on Energy Principles , 1968 .

[16]  John J. Valenza,et al.  A review of salt scaling: I. Phenomenology , 2007 .

[17]  Stephen J. Jones,et al.  Flexural Behavior of Model Sea Ice in a Centrifuge , 1999 .

[18]  George W. Scherer,et al.  A review of salt scaling: II. Mechanisms , 2007 .

[19]  J. Selker,et al.  Geometry and position of light nonaqueous-phase liquid lenses in water-wetted porous media , 1995 .

[20]  George W. Scherer,et al.  Mechanism for Salt Scaling , 2006 .

[21]  C. Kinoshita,et al.  Prediction of droplet size from the breakup of cylindrical liquid jets , 1995 .

[22]  R. C. Weast.  CRC Handbook of Chemistry and Physics , 1973 .

[23]  Garry Timco,et al.  Flexural strength equation for sea ice , 1994 .

[24]  G. Scherer.  Stress from crystallization of salt , 2004 .

[25]  J. Sharp,et al.  The influence of water removal techniques on the composition and microstructure of hardened cement pastes , 2008 .

[26]  S. Shtrikman,et al.  A variational approach to the theory of the elastic behaviour of multiphase materials , 1963 .

[27]  H. Jennings,et al.  Damage to the Pore Structure of Hardened Portland Cement Paste by Mercury Intrusion , 2005 .

[28]  George W. Scherer,et al.  Mechanism for salt scaling of a cementitious surface , 2005 .

[29]  Erik Schlangen,et al.  Modeling of frost salt scaling , 2008 .

[30]  P. Monteiro,et al.  Errata to “Poroelastic model for concrete exposed to freezing temperatures” [Cement and Concrete Research 38 (2008) 40–48] , 2009 .

[31]  Y. Soong,et al.  Effects of surfactants on the liquid-liquid dispersions in agitated vessels , 1985 .

[32]  M. D. Thouless,et al.  The edge cracking and spalling of brittle plates , 1987 .

[33]  P. Bowen,et al.  Changes in portlandite morphology with solvent composition: Atomistic simulations and experiment , 2011 .

[34]  Garry Timco,et al.  ON MEASURING FLEXURAL PROPERTIES OF ICE USING CANTILEVER BEAMS , 2010 .

[35]  N. Fukuta.  Ice Nucleation by Metaldehyde , 1963, Nature.

[36]  Dipayan Jana,et al.  CONCRETE, CONSTRUCTION OR SALT: WHICH CAUSES SCALING? , 2004 .

[37]  P. Monteiro,et al.  Poroelastic model for concrete exposed to freezing temperatures , 2008 .

[38]  K. Vaudrey.  Ice Engineering - study of Related Properties of Floating Sea-Ice Sheets and Summary of Elastic and Viscoelastic Analyses , 1977 .

[39]  Orientation Dependence of Elastic Constants for Ice , 1987 .

[40]  Paul Klieger,et al.  STUDIES OF 'SALT' SCALING OF CONCRETE , 1957 .