Preparation of a nanosilica-modified negative-type acrylate photoresist

A new type of negative photoresist, which incorporated nanosized silica into a photosensitive acrylic resin, was developed. First, free-radical polymerization was employed to synthesize the acrylic resin, poly[methyl methacrylate/methacrylic acid/3-(trimethoxysilyl) propyl methacrylate], and then a silica precursor, prepared by hydrolysis and condensation of tetraethoxysilane in a sol–gel process, was introduced into the as-formed resin solution. After the addition of photosensitive monomers and photoinitiators, a negative-type organic–inorganic photoresist was produced. The morphology of the UV-cured photoresist, as observed by field emission scanning electron microscopy, indicated that the size of the silica domain in the material could be reduced from 300 to about 50 nm by appropriate dosage of 3-(trimethoxysilyl) propyl methacrylate. Thermogravimetric analysis, dynamic mechanical analysis, differential scanning calorimetry, and thermal mechanical analysis were used to evaluate the thermal and dimensional stabilities of the cured photoresists. It was found that the thermal decomposition temperature and glass-transition temperature increased, whereas the thermal expansion coefficients before and after the glass transition decreased, with increasing silica content. The incorporation of 3-(trimethoxysilyl) propyl methacrylate also enhanced the thermal and dimensional stabilities; however, the level of enhancement was moderate for the thermal decomposition temperature and thermal expansion coefficient and low for the glass-transition temperature. In addition, a photoresist coated on a copper substrate demonstrated high hardness (5H) and strong adhesion (100%) with a resolution of 30 μm. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2008

[1]  Xin Jin,et al.  Preparation and characterization of UV‐curable ZnO/polymer nanocomposite films , 2007 .

[2]  W. Tao,et al.  Photo‐differential scanning calorimetry study on photopolymerization of nanosized titanium dioxide/polyacrylate hybrid materials , 2006 .

[3]  Frank Bauer,et al.  Nano/Micro Particle Hybrid Composites for Scratch and Abrasion Resistant Polyacrylate Coatings , 2006 .

[4]  Liang Huang,et al.  Stabilized dispersions of titania nanoparticles via a sol–gel process and applications in UV-curable hybrid systems , 2006 .

[5]  Limin Wu,et al.  Structure and Mechanical Properties of Polyurethane/Silica Hybrid Coatings , 2005 .

[6]  M. Zaborski,et al.  Sol–gel process of alkoxysilanes in an elastomer medium , 2005 .

[7]  Youn-Sik Lee,et al.  Preparation and characterization of poly(MSMA-co-MMA)-TiO2/SiO2 nanocomposites using the colloidal TiO2/SiO2 particles via blending method , 2005 .

[8]  T. Wong,et al.  A study on Cu diffusion to sol-gel derived low-k films , 2005 .

[9]  A. Tinnemans,et al.  Transparent UV curable antistatic hybrid coatings on polycarbonate prepared by the sol–gel method , 2004 .

[10]  E. Longo,et al.  Sol–gel nonhydrolytic synthesis of a hybrid organic–inorganic electrolyte for application in lithium-ion devices , 2004 .

[11]  Wen‐Chang Chen,et al.  Transparent organic-inorganic hybrid thin films prepared from acrylic polymer and aqueous monodispersed colloidal silica , 2003 .

[12]  Wen‐Chang Chen,et al.  Synthesis and characterization of organic–inorganic hybrid thin films from poly(acrylic) and monodispersed colloidal silica , 2003 .

[13]  O. Soppera,et al.  Design of photoinduced relief optical devices with hybrid sol–gel materials , 2002 .

[14]  Jin-Who Hong,et al.  Determination of key variables affecting surface properties of UV curable coatings using experimental design , 2002 .

[15]  M. Mechtel,et al.  Organic-Inorganic Hybrid Coatings Based on Polyfunctional Silanols as New Monomers in Sol-Gel Processing , 2001 .

[16]  S. Nunes,et al.  Hybrid films of poly(ethylene oxide-b-amide-6) containing sol–gel silicon or titanium oxide as inorganic fillers: effect of morphology and mechanical properties on gas permeability , 2000 .

[17]  Ivan Javni,et al.  Structure and properties of polyurethane–silica nanocomposites , 2000 .

[18]  L. Matějka.  Reinforcement of crosslinked rubbery epoxies by in-situ formed silica , 2000 .

[19]  C. Mansur,et al.  Thermal analysis and NMR studies of methyl methacrylate (MMA)-methacrylic acid copolymers synthesized by an unusual polymerization of MMA , 2000 .

[20]  Wen‐Chang Chen,et al.  Synthesis and Characterization of Poly(methyl methacrylate)-Silica Hybrid Optical Thin Films , 2000 .

[21]  Jean Pierre Pascault,et al.  Synthesis, structure, and morphology of polymer-silica hybrid nanocomposites based on hydroxyethyl methacrylate , 1999 .

[22]  Yen Wei,et al.  Preparation and properties of poly(styrene-co-maleic anhydride)/silica hybrid materials by the in situ sol-gel process , 1998 .

[23]  F. Monte,et al.  Photopolymerization of hydroxyethylmethacrylate in the formation of organic–inorganic hybrid sol–gel matrices , 1996 .