Tensile fatigue behaviour of ultra-high performance fibre reinforced concrete (UHPFRC)

The tensile fatigue behaviour of ultra-high performance fibre reinforced concrete (UHPFRC) under constant amplitude fatigue cycles is presented. Three series of uniaxial tensile fatigue tests up to a maximum of 10 million cycles were conducted with the objective to determine the endurance limit of UHPFRC that was supposed to exist for this material. The fatigue tests reveal that an endurance limit exists in all three domains of UHPFRC tensile behaviour at S-ratios ranging from 0.70 to 0.45 with S being the ratio of the maximum fatigue stress to the elastic limit strength of UHPFRC. Rather large variation in local specimen deformations indicates significant stress and deformation redistribution capacity of the UHPFRC bulk material enhancing the fatigue behaviour. The fatigue fracture surface of UHPFRC shows features of the fatigue fracture surfaces of steel, i.e. fatigue crack propagation is identified by a smooth surface while final fracture leads to rather rough surface. Various fatigue damaging mechanisms due to fretting and grinding as well as tribocorrosion are identified.

[1]  E. Brühwiler,et al.  Structural Rehabilitations with Ultra-High Performance Fibre Reinforced Concretes (UHPFRC) / Strukturelle Instandsetzung von Betonbrücken mit Ultra-hochleistungsfähigem Faserfeinkornbeton (UHFB) , 2006 .

[2]  P. Pimienta,et al.  Fatigue Flexural Behavior of Pre-cracked Specimens of Special UHPFRC , 2005 .

[3]  Konrad Zilch,et al.  Fatigue Behaviour of Ultra-High Performance Concrete under Cyclic Stress Reversal Loading , 2008 .

[4]  A. M. Brandt.  On the optimal direction of short metal fibres in brittle matrix composites , 1985 .

[5]  A. K. Vasudevan,et al.  Analysis of endurance limits under very high cycle fatigue using a unified damage approach , 2007 .

[6]  P. Rossi.  Ultra-High Performance Fiber-Reinforced Concretes , 2001 .

[7]  Eugen Brühwiler,et al.  Rehabilitation of concrete structures using Ultra-High Performance Fibre Reinforced Concrete , 2008 .

[8]  D. Landolt,et al.  Corrosion and surface chemistry of metals , 2007 .

[9]  Jaap Schijve,et al.  Fatigue of structures and materials , 2001 .

[10]  Katrin Habel,et al.  Structural behaviour of elements combining ultra-high performance fibre reinforced concretes (UHPFRC) and reinforced concrete , 2004 .

[11]  Ulrika Johansson.  Fatigue tests and analysis of reinforced concrete bridge deck models , 2004 .

[12]  Victor C. Li,et al.  Effect of inclining angle, bundling and surface treatment on synthetic fibre pull-out from a cement matrix , 1990 .

[13]  John Wuest,et al.  Comportement structural des bétons de fibres ultra performants en traction dans des éléments composés , 2007 .

[14]  Bhushan Lal Karihaloo,et al.  High performance fibre-reinforced cementitious composite (CARDIFRC) - Performance and application to retrofitting , 2007 .

[15]  H.A.W. Cornelissen,et al.  Fatigue Failure of Concrete in Tension , 1984 .

[16]  Joost C. Walraven,et al.  FLEXURAL FATIGUE OF HIGH AND ULTRA HIGH STRENGTH FIBRE REINFORCED CONCRETE , 2006 .

[17]  Jun Zhang,et al.  Crack bridging model for fibre reinforced concrete under fatigue tension , 2001 .

[18]  Claude Boulay,et al.  Fatigue behavior of a multi-scale cement composite , 2007 .