Mechanical Behavior and Thermal Stability of EVA Encapsulant Material Used in Photovoltaic Modules

Abstract The mechanical behavior and the thermal stability of an encapsulant based on ethylene-vinyl acetate (EVA) were studied. The EVA properties were verified at temperatures ranging from −70 °C to 500 °C. Thermogravimetry, differential scanning calorimetry and dynamic mechanical analysis were used in this study. It has been shown that the encapsulant has a good weight stability; however, the encapsulant passes through both a glass transition and a melting phase in the range of operating temperatures. The kinetic parameters of crosslinking were also analyzed. It is possible to achieve 65% crosslinking at a temperature of 150 °C and a time of 5 minutes. The activation energy of crosslinking is 95.6 kJ/mol.

[1]  M. Boumaour,et al.  Thermal stability of slow and fast cure EVA encapsulant material for photovoltaic module manufacturing process , 2006 .

[2]  Cheryl E. Kennedy,et al.  Acetic acid production and glass transition concerns with ethylene-vinyl acetate used in photovoltaic devices , 2007 .

[3]  Erin Baker,et al.  Estimating the manufacturing cost of purely organic solar cells , 2009 .

[4]  Myer Ezrin,et al.  Investigation of the degradation and stabilization of EVA-based encapsulant in field-aged solar energy modules , 1997 .

[5]  F. Pern,et al.  Encapsulation of PV modules using ethylene vinyl acetate copolymer as a pottant: A critical review , 1996 .

[6]  S. Pelland,et al.  Estimating the uncertainty in long-term photovoltaic yield predictions , 2013 .

[7]  Gernot M. Wallner,et al.  Aging mechanisms of polymeric films for PV encapsulation , 2005 .

[8]  J. Foreman,et al.  Exploring the Sensitivity of Thermal Analysis Techniques to the Glass Transition , 1997 .

[9]  Guk-Rwang Won.  American Society for Testing and Materials , 1987 .

[10]  R. C. Mackenzie,et al.  Nomenclature in thermal analysis, Part IV , 1972 .

[11]  Gernot M. Wallner,et al.  Evaluation of the aging behavior of ethylene copolymer films for solar applications under accelerated weathering conditions , 2009 .

[12]  J. Ford.  Thermal Analysis - Fundamentals and Applications to Polymer Science, 2nd Edition, Edited by T. Hatakeyama and F.X. Quinn, Wiley, Chichester, 1999, viii+180 pages. ISBN 0-471-98362-4; @$55.00 , 2000 .

[13]  M. Jackson,et al.  Laser annealing of flash-evaporated CuInSe2 thin films , 2006 .

[14]  畠山 立子,et al.  Thermal Analysis: Fundamentals and Applications to Polymer Science , 1994 .

[15]  F. Chenlo,et al.  Early degradation of silicon PV modules and guaranty conditions , 2011 .

[16]  M. S. García-Cascales,et al.  Towards low-cost manufacturing of organic solar cells: multi-criteria assessment of fabrication technologies , 2010 .

[17]  K. Menard.  Dynamic Mechanical Analysis: A Practical Introduction , 1997 .

[18]  R. Polanský,et al.  Influence of thermal treatment on the glass transition temperature of thermosetting epoxy laminate , 2009 .

[19]  A. J. Zattera,et al.  Assessment of Avrami, Ozawa and Avrami–Ozawa equations for determination of EVA crosslinking kinetics from DSC measurements , 2008 .

[20]  Lin Zhao,et al.  Theoretical investigation on the absorption enhancement of the crystalline silicon solar cells by pyramid texture coated with SiNx:H layer , 2011 .