论文信息 - ATOM PROBE ANALYSIS OF FE73.5SI13.5B9NB3CU1 NANOCRYSTALLINE SOFT MAGNETIC MATERIAL

ATOM PROBE ANALYSIS OF FE73.5SI13.5B9NB3CU1 NANOCRYSTALLINE SOFT MAGNETIC MATERIAL

The microstructure of Fe73.5Si13.5B9Nb3Cu1 soft magnetic material with a nanocrystalline structure has been investigated by atom probe field ion microscopy. In the as‐quenched amorphous sample, all the alloying elements were found to distribute homogeneously as an amorphous solid solution. In the annealed sample with the optimum soft magnetic properties, we found that two phases were present. One was Fe‐Si solid solution and the other was the B‐ and Nb‐enriched region with less Si content. Although some uncertainty remains regarding Cu, the present result is consistent with an early speculation based on the lattice parameter measurement.

A. Inoue | K. Hono | T. Sakurai

[1] M. B. Lee,et al. Relationship between crystallization process and magnetic properties of Fe‐(Cu‐Nb)‐Si‐B amorphous alloys , 1990 .

[2] G. Herzer,et al. Grain size dependence of coercivity and permeability in nanocrystalline ferromagnets , 1990, International Conference on Magnetics.

[3] Y. Yoshizawa,et al. Fe-Based Soft Magnetic Alloys Composed of Ultrafine Grain Structure , 1990 .

[4] Y. Yoshizawa,et al. Common mode choke cores using the new Fe-based alloys composed of ultrafine grain structure , 1988 .

[5] Y. Yoshizawa,et al. New Fe-based soft magnetic alloys composed of ultrafine grain structure , 1988 .

[6] P. Haasen,et al. Atom probe field ion microscopy of a FeNiB glass , 1982 .