On the Role of Lengthscale in the Prediction of Failure of Composite Structures: Assessment and Needs

The role of modeling in the design of structural composite components against failure is discussed. Composite materials fail due to damage processes operating at several lengthscales. The interactions between these processes offer the principal challenges to applying mechanism-based models at structural scales beyond the ply level. A methodology is proposed to increase the efficiency of the design process, analogous to the 'building block' approach, which provides a framework for integrating mechanism-based models with the current experimentally-based design process. Available models are reviewed and their key elements identified. General concepts are illustrated via a discussion of the particular issues pertaining to notched components. Key steps needed to allow the evolution of the design process to the envisioned process are identified.

[1]  Su-Su Wang,et al.  The Extension of Crack Tip Damage Zones in Fiber Reinforced Plastic Laminates , 1975 .

[2]  Z. Suo,et al.  Mixed mode cracking in layered materials , 1991 .

[3]  C. Chamis.  Mechanics of Composite Materials: Past, Present and Future , 1989 .

[4]  R. Whitehead,et al.  A building block approach to design verification testing of primary composite structure , 1983 .

[5]  Jonathan Awerbuch,et al.  Notched Strength of Composite Laminates: Predictions and Experiments—A Review , 1985 .

[6]  P. Lagacé,et al.  Response of Notched Graphite/Epoxy and Graphite/PEEK Systems , 1993 .

[7]  N. Bhat,et al.  Delamination growth in graphite/epoxy composite laminates under tensile loading , 1993 .

[8]  J. Whitney,et al.  Stress Fracture Criteria for Laminated Composites Containing Stress Concentrations , 1974 .

[9]  H. Mcmanus,et al.  On Microcracking in Composite Laminates under Thermal and Mechanical Loading , 1995, Engineering Plastics.

[10]  Russell D. Jamison,et al.  On the Interrelationship Between Fiber Fracture and Ply Cracking in Graphite/Epoxy Laminates , 1986 .

[11]  S. Spearing,et al.  The fatigue damage mechanics of notched carbon fibre/PEEK laminates , 1992 .

[12]  Fu-Kuo Chang,et al.  Damage Tolerance of Laminated Composites Containing an Open Hole and Subjected to Compressive Loadings: Part I—Analysis , 1991 .

[13]  J. Hutchinson,et al.  Transverse cracking in fiber-reinforced brittle matrix, cross-ply laminates , 1993 .

[14]  Kuen Y. Lin,et al.  Fracture of Boron/Aluminum Composites with Discontinuities , 1977 .

[15]  T. O'Brien.  Characterization of delamination onset and growth in a composite laminate , 1982 .

[16]  K. Jen,et al.  On the Effect of Matrix Cracks on Laminate Strength , 1987 .

[17]  P. Peters.  On the increasing fracture toughness at increasing notch length of 090 and 0/±45/0 graphite/epoxy laminates , 1983 .

[18]  Satish A. Salpekar,et al.  Combined effect of matrix cracking and stress-free edge on delamination , 1991 .

[19]  Frank W. Zok,et al.  The physics and mechanics of fibre-reinforced brittle matrix composites , 1994, Journal of Materials Science.

[20]  H. Budiman,et al.  Nondimensional Parameters for Geometric Nonlinear Effects in Pressurized Cylinders With Axial Cracks , 1997 .

[21]  J. Aveston,et al.  Single and Multiple Fracture , 1971 .

[22]  G. Dvorak,et al.  Analysis of first ply failure in composite laminates , 1986 .

[23]  Stephen W. Tsai,et al.  A Survey of Macroscopic Failure Criteria for Composite Materials , 1984 .

[24]  W. Weibull.  A Statistical Distribution Function of Wide Applicability , 1951 .

[25]  John C. Brewer,et al.  Quadratic Stress Criterion for Initiation of Delamination , 1988 .

[26]  D. C. Phillips,et al.  The effect of specimen size on the strength of cfrp , 1978 .

[27]  M. Kortschot,et al.  Damage-Based Notched Strength Modeling: A Summary , 1991 .

[28]  William A. Curtin,et al.  THEORY OF MECHANICAL-PROPERTIES OF CERAMIC-MATRIX COMPOSITES , 1991 .

[29]  Peter W. R. Beaumont,et al.  Matrix cracking and stiffness reduction during the fatigue of a (0/90)s GFRP laminate , 1985 .

[30]  S. L. Phoenix,et al.  The Chain-of-Bundles Probability Model For the Strength of Fibrous Materials I: Analysis and Conjectures , 1978 .