Improvement of microstructural and mechanical properties of plasma sprayed Mo coatings deposited on Al-Si substrates by pre-mixing of Mo with TiN powder

The present work embodies development of a new class of mechanically improved Mo-TiN coating material using plasma spray technique. The coatings are developed on Al-Si alloy at different torch input power levels ranging from 15 kW to 30 kW. Pre-mixing of TiN with molybdenum enhances adhesion strength and hardness of the coatings. Maximum adhesion strength of 22 MPa (±0.75) and hardness of 748 HV (±30) are found for the coating when molybdenum is pre-mixed with 10% TiN. FESEM micrographs of the as-sprayed coatings showed formation of plate-like structures of splats which indicates TiN sites as reinforcement in Mo matrix. X-ray diffraction study reveals the formation of both MoO2 and TiN as minor phases in the coating microstructure. The significant enhancement of mechanical properties like adhesion strength and hardness is attributed towards the presence of these phases.

[1]  B. Gill,et al.  Plasma spray coating processes , 1986 .

[2]  D. Toma,et al.  Wear and corrosion behaviour of thermally sprayed cermet coatings , 2001 .

[3]  R. C. Weast.  CRC Handbook of Chemistry and Physics , 1973 .

[4]  Huajian Gao,et al.  A quantitative study of the hardness of a superhard nanocrystalline titanium nitride/silicon nitride coating , 2005 .

[5]  A. Craft,et al.  Piston ring coatings for high horsepower diesel engines , 1993 .

[6]  P. Nylén,et al.  Effect of grit blasting and spraying angle on the adhesion strength of a plasma-sprayed coating , 2004 .

[7]  H. Jehn.  Multicomponent and multiphase hard coatings for tribological applications , 2000 .

[8]  D. Stone,et al.  Hardness and elastic modulus of TiN based on continuous indentation technique and new correlation , 1991 .

[9]  S. Hogmark,et al.  An evaluation of plasma sprayed ceramic coatings by erosion, abrasion and bend testing , 2000 .

[10]  S. Mitrovic,et al.  Evaluation of adhesion/cohesion bond strength of the thick plasma spray coatings by scratch testing on coatings cross-sections ☆ , 2011 .

[11]  Wei Wang,et al.  Microstructure and properties of TiN/Ni composite coating prepared by plasma transferred arc scanning process , 2009 .

[12]  Jeon G. Han,et al.  High temperature wear resistance of (TiAl)N films synthesized by cathodic arc plasma deposition , 1996 .

[13]  Sanjay Sampath,et al.  Effects of the spray angle on splat morphology during thermal spraying , 1997 .

[14]  R. McPherson,et al.  The relationship between the mechanism of formation, microstructure and properties of plasma-sprayed coatings , 1981 .

[15]  T. Rhys-Jones,et al.  The use of thermally sprayed coatings for compressor and turbine applications in aero engines , 1990 .

[16]  Robert B. Heimann.  Plasma-Spray Coating , 1996 .