An investigation of bioactive glass powders by sol-gel processing.

Bioactive glass powders, with a composition of SiO 2-CaO-P 2O 5, have been successfully synthesized via a sol-gel process at considerably lower temperatures than required for conventional melting methods. Bioactive glass powders made via conventional methods form an interfacial bond with bone when they are implanted. Bonding is correlated with the formation of a surface hydroxyapatite layer. This study examined the formation of a hydroxyapatite layer in Tris-buffered solution as a function of SiO 2 content of sol-gel derived powders. A FT-IRRS technique was used to monitor the formation of the hydroxyapatite on the surface of the powders. X-ray diffraction analysis and BET were also used to characterize the chemical and physical properties of the sol-gel derived bioactive powders. It was discovered that: (a) the rate of hydroxyapatite formation decreased with increasing SiO 2 content for powders whose SiO 2 content was less than 90 mol%; (b) a hydroxyapatite film does not form for the powders whose SiO 2 content is more than 90 mol%; (c) the SiO 2 limit, beyond which the powders lost their bioactivity, was much higher for bioactive glass powders made through sol-gel process (90%) than those made by conventional melting methods (60%). These results indicate that it is possible to significantly expand the bioactive composition range through microstructural control made possible by sol-gel processing techniques.

[1]  L. W. Rodgers,et al.  Facial bone augmentation using Bioglass in dogs. , 1986, Archives of otolaryngology--head & neck surgery.

[2]  J. Mackenzie,et al.  Sol-gel processing of silica. II: The role of the catalyst , 1986 .

[3]  Larry L. Hench,et al.  Bonding mechanisms at the interface of ceramic prosthetic materials , 1971 .

[4]  U. Gross,et al.  The anchoring of glass ceramics of different solubility in the femur of the rat. , 1980, Journal of biomedical materials research.

[5]  D. Williams,et al.  Fundamental aspects of biocompatibility , 1981 .

[6]  S. Sakka Glasses and glass-ceramics from gels , 1985 .

[7]  T Kitsugi,et al.  Ca,P-rich layer formed on high-strength bioactive glass-ceramic A-W. , 1990, Journal of biomedical materials research.

[8]  L L Hench,et al.  Toxicology and biocompatibility of bioglasses. , 1981, Journal of biomedical materials research.

[9]  B. O. Fowler Infrared studies of apatites. I. Vibrational assignments for calcium, strontium, and barium hydroxyapatites utilizing isotopic substitution , 1974 .

[10]  P. Gaskell Vibrational spectra of simple silicate glasses , 1970 .

[11]  R. J. Bell,et al.  Atomic vibrations in vitreous silica , 1970 .

[12]  C. Brinker,et al.  Sol → gel → glass: I. Gelation and gel structure , 1985 .

[13]  L. Hench,et al.  Chemical and mechanical behavior of bioglass-coated alumina. , 1976, Journal of biomedical materials research.

[14]  D. Williams,et al.  Biocompatibility of orthopedic implants , 1982 .

[15]  L L Hench,et al.  Compositional dependence of the formation of calcium phosphate films on bioglass. , 1980, Journal of biomedical materials research.

[16]  F. Orgaz-Orgaz Gel to glass conversion: densification kinetics and controlling mechanisms , 1988 .