Homogenization of 7075 and 7049 Aluminium Alloys Intended for Extrusion Welding

During the extrusion of aluminum alloys profiles using porthole dies, the temperature of the material in the welding chamber is one of crucial parameters determining the quality of longitudinal welds. In order to extend the permissible temperature range, the billets intended for this process should be characterized by the maximum attainable solidus temperature. Within the present work, the homogenization of AlZnMgCu alloys DC-cast (Direct Chill-cast) billets was investigated, with the aim of solidus temperature maximization. Conditions of soaking and cooling stages were analyzed. The materials were homogenized in laboratory conditions, and the microstructural effects were evaluated on the basis of DSC (Differential Scanning Calorimetry) tests and SEM/EDS (Scanning Electron Microscopy/Energy-Dispersive Spectroscopy) investigations. For all examined alloys, the unequilibrium low-melting microstructure components were dissolved during soaking, which led to the significant solidus temperature increase, in comparison to the as-cast state. The values within the range of 525–548 °C were obtained. In the case of alloy with highest Cu concentration, the application of two-step soaking was necessary. In order to take advantage of the high solidus temperature obtained after soaking, the cooling rate from homogenization must be controlled, and the effective cooling manner is strongly dependent on alloy composition. For high-Cu alloy, the solidus decreased, despite the fast cooling and the careful billets preheating being necessary.

[1]  A. Ghosh,et al.  Microstructure and texture development of 7075 alloy during homogenisation , 2018 .

[2]  M. Krane,et al.  Modeling phase transformation kinetics during homogenization of aluminum alloy 7050 , 2017 .

[3]  A. V. Somov,et al.  Study of the Structure and Properties of Especially Strong Aluminum Alloys of the Al–Zn–Mg–Cu System , 2017, Metallurgist.

[4]  P. Pałka,et al.  The Effect of Cooling Rate after Homogenization on the Microstructure and Properties of 2017a Alloy Billets for Extrusion with Solution Heat Treatment on the Press , 2016 .

[5]  B. Leszczyńska-Madej,et al.  Analysis of Extrusion Welding Conditions for AlMg Alloys with High Mg Content , 2016 .

[6]  B. Leszczyńska-Madej,et al.  The Effect Of Homogenization Conditions On The Structure And Properties Of 6082 Alloy Billets , 2015 .

[7]  L. Zhuang,et al.  Solidification Paths and Phase Components at High Temperatures of High-Zn Al-Zn-Mg-Cu Alloys with Different Mg and Cu Contents , 2015, Metallurgical and Materials Transactions A.

[8]  Gang Zhao,et al.  Effect of homogenization treatment on microstructure and mechanical properties of DC cast 7X50 aluminum alloy , 2015 .

[9]  D. Shu,et al.  Microstructural Aspects of Second Phases in As-cast and Homogenized 7055 Aluminum Alloy with Different Impurity Contents , 2013, Metallurgical and Materials Transactions A.

[10]  Z. Yin,et al.  Intermetallic phase evolution of 7050 aluminum alloy during homogenization , 2012 .

[11]  M. Starink,et al.  DSC Study on Phase Transitions and Their Correlation with Properties of Overaged Al-Zn-Mg-Cu Alloys , 2012, Journal of Materials Engineering and Performance.

[12]  D. Leśniak.  Weldability Investigations of AlCuMg Alloys for Extrusion Welding , 2012 .

[13]  M. Couper,et al.  Effect of Homogenisation Parameters on Dissolution and Precipitation in Aluminium Alloy AA7150 , 2011 .

[14]  Henry Valberg,et al.  Joining of metal streams in extrusion welding , 2009 .

[15]  Q. Meng,et al.  The microstructural evolution of an Al–Zn–Mg–Cu alloy during homogenization , 2006 .

[16]  Tao Wang,et al.  Evolution of eutectic structures in Al-Zn-Mg-Cu alloys during heat treatment , 2006 .

[17]  D. Eskin,et al.  Multicomponent Phase Diagrams: Applications for Commercial Aluminum Alloys , 2005 .

[18]  C. Mondal,et al.  On the nature of T(Al2Mg3Zn3) and S(Al2CuMg) phases present in as-cast and annealed 7055 aluminum alloy , 2005 .

[19]  Hongwei Liu,et al.  The improvement of constituent dissolution and mechanical properties of 7055 aluminum alloy by stepped heat treatments , 2003 .

[20]  T. Sheppard.  Extrusion of Aluminium Alloys , 1999 .

[21]  Leśniak Dariusz,et al.  Estimation of Extrusion Welding Conditions for 6xxx Aluminum Alloys , 2020 .

[22]  Hua Chen,et al.  Dissolution and melting of constituent particles in a DC-cast Al-Zn-Mg-Cu alloy 7150 during homogenisation , 2010 .

[23]  S. Nam,et al.  Control of Equilibrium Phases (M,T,S) in the Modified Aluminum Alloy 7175 for Thick Forging Applications. , 2003 .

[24]  Extrusion of 2xxx and 7xxx Alloys , 2000 .