Effect of the clearance and interference-fit on failure of the pin-loaded composites

The aim of this study is to examine the effect of the clearance and interference-fit on the failure mode, failure load and bearing strength of the pin-loaded joints subjected to traction forces. The failure load and failure mode are determined both experimentally and numerically. Three-dimensional finite element models are created using ANSYS software. Non-linear contact analyses are performed to examine the effects of the clearance and interference for different ratios of the edge distance-to-hole diameter (E/D) and plate width-to-hole diameter (W/D). Damage is also examined using scanning electron microscope (SEM). It is observed that interference for all pin-loaded joint configurations is beneficial. A good agreement between experimental and numerical results is obtained.

[1]  O. Sayman,et al.  Failure analysis of pin-loaded aluminum–glass–epoxy sandwich composite plates , 2003 .

[2]  Huseyin Imrek,et al.  Experimental and numerical failure analysis of pinned-joints in composite materials , 2009 .

[3]  Onur Sayman,et al.  Experimental failure analysis of mechanically fastened joints with clearance in composite laminates under preload , 2008 .

[4]  Stefan Hallström,et al.  Bearing strength of carbon fibre/epoxy laminates: effects of bolt-hole clearance , 2004 .

[5]  Bulent Murat Icten,et al.  Progressive failure analysis of pin-loaded carbon–epoxy woven composite plates , 2002 .

[6]  P. Ramesh Babu,et al.  Assessment of Beneficial Effects of Interference-fit in Pin-loaded FRP Composites , 2007 .

[7]  C. Cooper,et al.  Effects of joint geometry and bolt torque on the structural performance of single bolt tension joints in pultruded GRP sheet material , 1995 .

[8]  Jin-Hwe Kweon,et al.  Failure Load Prediction of a Mechanically Fastened Composite Joint Subjected to a Clamping Force , 2008 .

[9]  Pauli Pedersen,et al.  On the influence of clearance in orthotropic disc-pin contacts , 2007 .

[10]  Srinivasa D. Thoppul,et al.  Mechanics of mechanically fastened joints in polymer–matrix composite structures – A review , 2009 .

[11]  Ramazan Karakuzu,et al.  The Failure Strength for Pin-Loaded Multi-Directional Fiber-Glass Reinforced Epoxy Laminate , 2002 .

[12]  Buket Okutan,et al.  Failure Strength of Woven Glass Fiber-Epoxy Composites Pinned Joints , 2003 .

[13]  F. Cappello,et al.  A Study on the Effects of Clearance and Interference Fits in a Pin-Loaded Cross-Ply FGRP Laminate , 1998 .

[14]  Heung-Joon Park,et al.  Effects of stacking sequence and clamping force on the bearing strengths of mechanically fastened joints in composite laminates , 2001 .

[15]  Ramazan Karakuzu,et al.  Effects of geometric parameters on failure behavior in laminated composite plates with two parallel pin-loaded holes , 2008 .

[16]  M. Husnu Dirikolu,et al.  The effect of stacking sequence of carbon epoxy composite laminates on pinned-joint strength , 2003 .

[17]  Ramazan Karakuzu,et al.  Failure Analysis of Two-Dimensional Carbon-Epoxy Composite Plate Pinned Joint , 1999 .

[18]  Fabrice Pierron,et al.  A Numerical and Experimental Study of Woven Composite Pin-Joints , 2000 .